A kind of car paint protective film

A technology for protective films and automotive paints, applied to biocide-containing paints, film/flaky adhesives, coatings, etc., can solve the problems of unresolved self-healing layer durability and achieve fast and long-lasting curing Excellent, long-lasting antifouling effect

Active Publication Date: 2021-10-08
昆山乐凯锦富光电科技有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this technology also does not solve the problem of self-healing layer persistence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of car paint protective film
  • A kind of car paint protective film
  • A kind of car paint protective film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Preparation of semi-finished paint protection film:

[0039] On a translucent polyester release film with a thickness of 30 μm, use known technology to obtain an assembly glue with a thickness of 10 μm, and then laminate it with a polyvinyl chloride film with a thickness of 100 μm, and roll it to obtain a semi-finished paint protection film for use. .

[0040] (2) Preparation of self-healing coating solution:

[0041]

[0042]Add 30 kg of modified polyol resin [LCR-100, NATOCO], 0.5 kg of reactive leveling agent [BYK-370, Bi Ke], 0.2 kg of metal drier [organotin drier] into the container DY-12, Deyin Chemical] and 60 kg of toluene, stirred at high speed for 30 minutes. Add 6.7 kg of curing agent 1 [hexamethylene diisocyanate, Asahi Kasei] and 3.3 kg of curing agent 2 [isophorone diisocyanate, Evonik] 30 minutes before coating, stir at high speed for 10 minutes, and set aside.

[0043] (3) Preparation of paint protective film

[0044] Apply the self-repairing ...

Embodiment 2

[0046] (1) Preparation of semi-finished paint protection film:

[0047] On a translucent polyester release film with a thickness of 38 μm, an assembly glue with a thickness of 20 μm was obtained by known technology, and then laminated with a thermoplastic polyurethane film with a thickness of 150 μm, and rolled to obtain a semi-finished paint protection film for use.

[0048] (2) Preparation of self-healing coating solution:

[0049]

[0050] Add 35 kg of modified polyol resin [HFC-PNS1, HARIMA], 1.0 kg of reactive leveling agent [Silok-359, Slok], 0.27 kg of metal drier [organic bismuth drier] into the container Agent B1610, Casol additives] and 51 kg of ethyl acetate, stirred at high speed for 30min. Add 10.2 kg of curing agent 1 [trimethylhexamethylene diisocyanate, BASF] and 3.8 kg of curing agent 2 [dicyclohexylmethane-4,4'-diisocyanate, Wanhua] 30 minutes before coating, and stir at high speed for 10 minutes ,stand-by.

[0051] (3) Preparation of paint protective f...

Embodiment 3

[0054] (1) Preparation of semi-finished paint protection film:

[0055] On a translucent polyester release film with a thickness of 50 μm, use known technology to obtain an assembly glue with a thickness of 30 μm, and then laminate it with a thermoplastic polyurethane film with a thickness of 200 μm, and roll it to obtain a semi-finished paint protection film for use.

[0056] (2) Preparation of self-healing coating solution:

[0057]

[0058] Add 40 kg of modified polyol resin [TRE-2-S2, ASIA], 1.5 kg of reactive leveling agent [Teck-2110, Tiger], 0.35 kg of metal drier [rare earth drier] into the container Agent B-18, Ka Suo additives] and 42 kg of methyl ethyl ketone, high-speed stirring for 30min. Add 13.6 kg of curing agent 1 [xylylene diisocyanate, mol] and 3.9 kg of curing agent 2 [cyclohexane dimethylene diisocyanate, Mitsui Takeda] 30 minutes before coating, stir at high speed for 10 minutes, and wait use.

[0059] (3) Preparation of paint protective film

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A kind of car paint protective film, described car paint protective film comprises transparent support body, on an optical surface of described transparent support body, arrange self-healing layer and transparent release film successively; On the other side of described transparent support body An assembly glue and a translucent release film are sequentially arranged on an optical surface, and the self-repairing layer is formed by heating and curing after being coated with a self-repairing coating solution; the components and parts by weight of the self-repairing coating solution are: Reactive polyol resin 30-50, curing agent 10-25, reactive leveling agent 0.5-2.5, metal drier 0.2-0.5, organic solvent 25-60. The automobile paint protection film provided by the invention has durable self-healing properties, yellowing resistance, anti-fouling properties and acid and alkali resistance, and can be applied to the field of paint protection on automobile surfaces.

Description

technical field [0001] The invention relates to the field of film technology, in particular to a paint protection film attached to the surface of an automobile. Background technique [0002] Car paint protection film, also known as "invisible car cover", is a layer of transparent protective film attached to the surface paint of the car to protect the original car paint of the car from damage. This product has strong toughness and self-healing function, which can effectively prevent scratches and sand hits, and also isolates the contact between the car paint and the air, and can prevent acid rain, asphalt, bird droppings, etc. from damaging the paint surface . At the same time, the paint protection film is high-definition and bright, which can improve and protect the color and luster of the car paint surface. [0003] In the prior art, Chinese patent CN 201720602261 discloses an invisible car cover with self-repairing function. By adding an automatic repairing resin layer o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/25C09J7/24C09D175/04C09D175/06C09D5/16C09D7/47C08G18/44C08G18/42
Inventor 刘玉磊李敏合王辉万金龙王巧
Owner 昆山乐凯锦富光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products