Sponge composite metallic organic framework material for adsorption separation

A metal-organic framework and organic framework technology, applied in the field of materials, can solve the problems that hinder industrial application, easy loss of MOFs powder, easy agglomeration, etc., and achieve the effect of mild conditions, enhanced interaction force, and high loading rate

Active Publication Date: 2019-07-23
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF7 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems that MOFs powders are easy to lose and easy to agglomerate and hinder practical industrial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A sponge composite metal organic framework material for adsorption and separation, the specific preparation method of which is:

[0020] In the first step, 0.33g metal salt CuSiF 6 ·H 2 O was dissolved in 10.00g methanol to obtain solution 1; 0.30g pyrazine was dissolved in 10.0g methanol to obtain solution 2;

[0021] In the second step, 1 g of polyvinyl alcohol (PVA) aqueous solution with a mass fraction of 5% is added to 9.00 g of absolute ethanol; 0.17 g of melamine foam is immersed in this mixed solution for pretreatment for 2 hours, and dried at 323 K to obtain a melamine foam carrier ;

[0022] In the third step, the melamine foam carrier obtained in the second step is poured into solution 1 to soak, and dried at a temperature of 328K with a rotary evaporator for 2 hours, and then the soaked and dried melamine foam carrier is poured into solution 2 for soaking, and then soaked at a temperature of 328K. The in-situ growth reaction was carried out for 12 hours, ...

Embodiment 2

[0038] A sponge composite metal organic framework material for adsorption and separation, the specific preparation method of which is:

[0039] In the first step, 0.45g metal salt CuSiF 6 ·H 2 O was dissolved in 10.50g methanol to obtain solution 1; 0.40g pyrazine was dissolved in 10.50g methanol to obtain solution 2;

[0040] In the second step, 1.20 g of polyvinyl alcohol (PVA) aqueous solution with a mass fraction of 5% was added to 9.50 g of absolute ethanol. Immerse 0.17g of melamine foam in this mixed solution for pretreatment for 2 hours, and dry at 333K to obtain a melamine foam carrier;

[0041] In the third step, the melamine foam carrier obtained in the second step is poured into solution 1 for soaking, and dried at a temperature of 333K with a rotary evaporator for 2 hours, and then the soaked and dried melamine foam carrier is poured into solution 2 for soaking, and then soaked at a temperature of 333K. Under the in-situ growth reaction for 20 hours, and then d...

Embodiment 3

[0056] A sponge composite metal organic framework material for adsorption and separation, the specific preparation method of which is:

[0057] In the first step, 0.65g metal salt CuSiF 6 ·H 2 O was dissolved in 11.00 g of methanol to obtain solution 1; 0.60 g of pyrazine was dissolved in 11.00 g of methanol to obtain solution 2;

[0058] In the second step, 2.00 g of polyvinyl alcohol (PVA) aqueous solution with a mass fraction of 5% was added to 9.00 g of absolute ethanol. Immerse 0.17g of melamine foam in this mixed solution for pretreatment for 3 hours, and dry at a temperature of 338K to obtain a melamine foam carrier;

[0059] In the third step, the melamine foam carrier obtained in the second step is poured into solution 1 to soak, and dried at a temperature of 343K with a rotary evaporator for 3 hours, and then the soaked and dried melamine foam carrier is poured into solution 2 for soaking, and then soaked at a temperature of 343K. Under the in-situ growth reaction...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
load ratioaaaaaaaaaa
load ratioaaaaaaaaaa
Login to view more

Abstract

The invention relates to a sponge composite metallic organic framework material for adsorption separation and belongs to the technical field of materials. According to the invention, a two-step in-situ growth method is adopted for loading MOFs (metallic organic framework material) into a duct in a sponge carrier. The MOFs is synthesized from following organic ligands and metal salts, wherein the organic ligands include pyrazine, trimesic acid, terephthalic acid, 2,5-dihydroxyterephthalic acid, and the metal salts include cupric fluosilicate, magnesium nitrate, zirconium chloride, cupric nitrate, chromic nitrate, ferric nitrate, aluminum nitrate and hydrates thereof. According to a preparation method provided by the invention, a large amount of MOFs loaded in the duct in the sponge carriercan be realized; MOFs load rate is high; load is stable; the defects of fragility and easiness in loss of MOFs powder can be overcome; a breakthrough experiment proves that the material provided by the invention has the characteristics of high CO2-absorbing capacity, high adsorption separation selectivity, stable adsorption separation property, and the like.

Description

technical field [0001] The invention relates to a sponge composite metal organic framework material used for adsorption and separation, and belongs to the technical field of materials. Background technique [0002] As a porous material with rich specific surface area, regular channels, adjustable window size, and a large number of active sites, metal-organic frameworks (MOFs) have very broad application prospects for adsorption and separation. But its crystal size is micron level, and it is in powder state. This kind of powder is easy to lose and cause pipeline blockage, and easy to agglomerate to affect the mass transfer in the adsorption process. This hinders the practical application of MOFs. In order to apply MOFs materials in the process of fixed bed adsorption separation, to realize the CO reduction in closed space and industrial production 2 Gas capture, invention of such composite materials and preparation methods. Contents of the invention [0003] The purpose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/26B01D53/02
CPCB01D53/02B01D2257/504B01J20/226B01J20/262Y02C20/40
Inventor 赵之平甄红刚蔡玮玮
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap