Method for preparing anode material of three-dimensional porous carbon skeleton/CoO composite structured lithium ion battery

A lithium-ion battery, composite structure technology, applied in battery electrodes, secondary batteries, structural parts, etc., can solve the problems of small specific surface area of ​​materials and less loaded oxides

Active Publication Date: 2016-08-10
SHAANXI UNIV OF SCI & TECH
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the porous biomass carbon loaded with oxides has a relatively large pore size, which makes the specific surface area of ​​the material itself relatively small, and the amount of loaded oxides will be relatively small.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing anode material of three-dimensional porous carbon skeleton/CoO composite structured lithium ion battery
  • Method for preparing anode material of three-dimensional porous carbon skeleton/CoO composite structured lithium ion battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1: A preparation method of a three-dimensional porous carbon skeleton / CoO composite structure lithium-ion battery negative electrode material,

[0020] 1) Wash the peanut skins and dry them;

[0021] 2) Put 3 g of peanut skins into 60 ml of concentrated sulfuric acid solution with a concentration of 5 mol / L, and react in an oven at 80°C for 5 hours to obtain suspension A;

[0022] 3) Suspension A was subjected to vacuum filtration, and rinsed with deionized water to pH = 7, then collected and dried to obtain precursor B;

[0023] 4) Mix precursor B and potassium hydroxide at a mass ratio of 1:1 and grind them evenly to obtain product C;

[0024] 5) Put the product C into a tube furnace with argon gas, set the reaction temperature to 800°C, keep it warm for 2h, and the heating rate is 3°C·min -1 , argon flow rate 0.2sccm·min -1 , to obtain the product D;

[0025] 6) Add 0.02mol of analytically pure cobalt acetate tetrahydrate and 0.06mol of urea into 100ml of...

Embodiment 2

[0029] Example 2: A preparation method of a three-dimensional porous carbon skeleton / CoO composite structure lithium ion battery negative electrode material,

[0030] 1) Wash the garlic skin and dry it;

[0031] 2) Put 4 g of garlic skin into 60 ml of concentrated sulfuric acid solution with a concentration of 7 mol / L, and react in an oven at 80°C for 7 hours to obtain suspension A;

[0032] 3) Suspension A was subjected to vacuum filtration, and rinsed with deionized water to pH = 7, then collected and dried to obtain precursor B;

[0033]4) Mix precursor B and potassium hydroxide at a mass ratio of 1:2 and grind them evenly to obtain product C;

[0034] 5) Put the product C into a tube furnace with argon gas, set the reaction temperature to 700°C, keep it warm for 3h, and the heating rate is 5°C·min -1 , argon flow rate 0.5sccm·min -1 , to obtain the product D;

[0035] 6) Take 0.02mol of analytically pure cobalt acetate tetrahydrate and 0.08mol of urea into 100ml of dei...

Embodiment 3

[0037] Example 3: A preparation method of a three-dimensional porous carbon skeleton / CoO composite structure lithium-ion battery negative electrode material,

[0038] 1) Wash the onion skin and dry it;

[0039] 2) Put 6g of green onion skin into 60ml of concentrated sulfuric acid solution with a concentration of 10mol / L, and react in an oven at 80°C for 6h to obtain suspension A;

[0040] 3) Suspension A was subjected to vacuum filtration, and rinsed with deionized water to pH = 7, then collected and dried to obtain precursor B;

[0041] 4) Mix precursor B and potassium hydroxide at a mass ratio of 1:3 and grind them evenly to obtain product C;

[0042] 5) Put the product C into a tube furnace with argon gas, set the reaction temperature to 900°C, keep it warm for 1h, and the heating rate is 8°C·min -1 , argon flow rate 0.4sccm·min -1 , to obtain the product D;

[0043] 6) Add 0.02mol of analytically pure cobalt acetate tetrahydrate and 0.07mol of urea into 100ml of deioni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing an anode material of a three-dimensional porous carbon skeleton / CoO composite structured lithium ion battery. Parenchymatous tissue of plants is used as the biomass carbon material; the biomass carbon material is immersed through acid, such that a pre-carbonized precursor is obtained; then, the precursor and alkali are mixed and sufficiently grinded, and then thermally treated in a tube furnace, such that a three-dimensional porous carbon skeleton is obtained; the three-dimensional porous carbon skeleton is immersed in solution including cobalt salt; then, suction filtration and drying are carried out; and finally, the mixture is thermally treated in the tube furnace, such that a CoO loaded three-dimensional porous carbon skeleton composite is obtained. The composite is applied to the lithium ion battery, such that the lithium ion battery has good cycle performance and rate performance; the porous carbon skeleton, prepared by using the parenchymatous tissue of plants as the biomass carbon material, has a steady structure for supporting load of CoO; the porous carbon skeleton having different pore diameters can be obtained by controlling the addition amount of urea; due to the porous carbon skeleton, the CoO structure can be stabilized; simultaneously, the electrical conductivity of CoO is also improved; therefore, the electron transmission rate is increased; the electrochemical reaction is accelerated; and the rate performance is improved easily.

Description

technical field [0001] The invention relates to a preparation method of a three-dimensional porous carbon skeleton-loaded oxide lithium ion battery negative electrode material, in particular to a preparation method of a three-dimensional porous carbon skeleton / CoO composite structure lithium ion battery negative electrode material. Background technique [0002] With the continuous development and updating of the new generation of electronic products and electric vehicles, people have put forward higher requirements for the performance of lithium-ion batteries, and the development of new and cheap negative electrode materials has become one of the hot topics in the research of lithium-ion batteries. The transition metal oxide CoO has become a research hotspot due to its high theoretical capacity (715mAh / g), but its poor electrical conductivity and volume expansion during charge and discharge limit its practical application. At present, the main method to solve these problems ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/52H01M4/583H01M4/62H01M10/0525
CPCH01M4/362H01M4/52H01M4/583H01M4/625H01M10/0525Y02E60/10
Inventor 李嘉胤康倩曹丽云程娅伊齐慧欧阳海波许占位黄剑锋
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka