A new material and high-quality technology, applied in the field of functional materials, can solve problems such as difficulties, weakened adhesion, and difficulty in meeting high adhesion, and achieve high adhesion, good friction resistance, and improved overall performance.

Inactive Publication Date: 2019-07-26
苏州妙文信息科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In general, it is very difficult to maintain these properties at the same time, because some properties are mutually restrictive, and the interaction between them is mutually beneficial. If the friction resistance is satisfied, it is difficult to meet the high adhesion capacity.
If the anti-friction ability in the component is adjusted to be very strong, the adhesion ability in the component will be weakened at this time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decoration new material
  • Decoration new material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: Preparation of a new decorative material

[0021] Wherein, the main chemical composition and content mass percentage of the new decorative material are: the mass percentage of polyvinyl chloride is 63.5%-73.5%; the mass percentage of plasticizer is 3.5%-5.5%; the mass percentage of lubricant is 5.5 %-7.5%; the mass percentage of calcium and zinc stabilizers is 0.5%-3.5%; the mass percentage of antioxidants is 2.5%-4.5%; the mass percentage of additives is 11.5%-15.5%; the mass percentage of graphene is 2.5%-4.5%.

[0022] The plasticizer is a mixture of epoxy acetyl linolenic acid methyl ester, epoxy soybean oleic acid octyl ester, and 9,10-epoxystearyl octyl ester; the lubricant is castor oil, stearic alcohol , Stearic acid amide, butyl stearate and stearic acid monoglyceride mixture; the antioxidant is a mixture of zinc dialkyl dithiophosphate and zinc dialkyl dithiocarbamate; The auxiliary agent is a mixture of leveling agent, defoamer, dispersant and paraffi...

Embodiment 2

[0025] Example 2: Preparation of a new decorative material

[0026] The rest is the same as in Example 1, except that: the mass percentage of the polyvinyl chloride is 68%, the mass percentage of the plasticizer is 4%; the mass percentage of the lubricant is 4%; the calcium zinc The mass percentage of the stabilizer is 5.5%; the mass percentage of the antioxidant is 3%; the mass percentage of the auxiliary agent is 15%; and the mass percentage of the graphene is 3%.

Embodiment 3

[0027] Example 3: Preparation of a new decorative material

[0028] The rest is the same as Example 1, except that: the mass percentage of the polyvinyl chloride is 67%, the mass percentage of the plasticizer is 4%; the mass percentage of the lubricant is 5.5%; the calcium zinc The mass percentage of the stabilizer is 2.5%; the mass percentage of the antioxidant is 3.5%; the mass percentage of the auxiliary agent is 1% to 3.5; and the mass percentage of the graphene is 4%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a decoration new material. The decoration new material comprises 63.5%-73.5% of polyvinyl chloride, 3.5%-5.5% of a plasticizer, 5.5%-7.5% of a lubricant, 0.5%-3.5% of a calcium-zinc stabilizer, 2.5%-4.5% of an anti-oxidant, 11.5%-15.5% of an assistant, and 2.5%-4.5% of graphene. The plasticizer is methyl epoxide acetyllinoleate, epoxy soybean oil acid octyl ester, and 9,10-epoxy octyl stearate. The lubricant is castor oil, stearyl alcohol, octadecanamide, butyl stearate and glycerol monostearate. The anti-oxidant is zinc dialkyl dithiophosphate and zinc dialkyl dithiocarbamate. The assistant is formed by mixing a flatting agent, a defoaming agent, a dispersing agent and paraffin according to a mass proportion of 2:1.5:1:3. A mass proportion of the polyvinyl chloride and the assistant is 4:1-6:1. A mass proportion of the polyvinyl chloride and the graphene is 16:1-28:1.

Description

Technical field [0001] The invention belongs to the field of functional materials, and relates to a PVC material, in particular to a new decorative material. Background technique [0002] PVC material is a kind of plastic decoration material. PVC is the abbreviation of polyvinyl chloride material. It is based on polyvinyl chloride resin as the main raw material, adding appropriate amount of anti-aging agents, modifiers, etc., after mixing, calendering, and vacuum suction Materials prepared by other processes. PVC material has the characteristics of light weight, heat insulation, heat preservation, moisture proof, flame retardant and convenient construction. The variety of specifications, colors and patterns are very decorative and can be applied to the decoration of indoor walls and ceilings. It is one of the most widely used decorative materials in plastic materials. [0003] At present, the existing PVC materials are used for decoration and have high requirements for many of it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L91/06C08L91/00C08K13/06C08K9/04C08K3/34C08K5/1515C08K3/04C08K5/101C08K5/103C08K5/20C08K5/39C08K5/5398C08K5/09
CPCC08K2201/014C08L27/06C08L2205/02C08L2205/03C08L91/06C08L91/00C08K13/06C08K9/08C08K3/346C08K5/1515C08K3/042C08K5/101C08K5/103C08K5/20C08K5/39C08K5/5398C08K5/09
Inventor 不公告发明人
Owner 苏州妙文信息科技有限公司