A technology of catalysts and compounds, applied in chemical instruments and methods, preparation of organic compounds, physical/chemical process catalysts, etc., can solve problems such as complex preparation process, reduced regeneration efficiency of degraded products, weak combination of carrier and active components, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0018] The first aspect of the present invention provides a kind of preparation method for the catalyst of the anthraquinone degradation product in regeneration hydrogen peroxide working solution, and this method comprises the following steps:
[0019] S1. Mix the quick-release powder, the alkaline earth metal compound and an optional extrusion aid to obtain the first dry material;
[0020] S2. Mixing the acid solution and the silicon source to obtain the first liquid;
[0021] S3. After mixing the first dry material with the first liquid, kneading, extruding, drying and roasting are performed sequentially.
[0022] According to the method of the present invention, S1 and S2 are in no particular order.
[0023] According to the method of the present invention, the quick-release powder can be activated alumina produced from gibbsite or bayerite, which can be a commercially available product. In a preferred situation, the specific surface area of the quick-release powder can...
Embodiment 1
[0048] S1. Mix 131.25g of quick-release powder, 4.5g of turnip powder, 15.0g of calcium oxide powder and 0.75g of manganese dioxide powder to obtain the first dry material;
[0049] S2, the content of 105.0g is the nitric acid solution of 5% by weight and the content of 10.0g is the silica sol of 30% by weight (as SiO 2 Meter) solution is mixed, stirs to obtain the first liquid;
[0050] S3. Mix the first dry material with the first liquid, then knead and extrude the obtained strips in the shade at room temperature for 24 hours, then dry them at 110°C for 6 hours, and then The temperature was raised to 600°C at a heating rate of 4°C / min, and calcined for 4 hours to obtain a catalyst, which was designated as C1.
[0051] Based on the total weight of the catalyst, the content of the activated alumina is 87.5% by weight, the content of the alkaline earth metal oxide is 10% by weight, the content of the manganese dioxide is 0.5% by weight, and the content of the silicon dioxide ...
Embodiment 2
[0054] S1. Mix 132.0 g of quick-release powder, 4.5 g of scallop powder and 15.0 g of calcium oxide powder to obtain the first dry material;
[0055] S2, the content of 105.0g is the nitric acid solution of 5% by weight and the content of 10.0g is the silica sol of 30% by weight (as SiO 2 Meter) solution is mixed, stirs to obtain the first liquid;
[0056] S3. Mix the first dry material with the first liquid, then knead and extrude the obtained strips in the shade at room temperature for 24 hours, then dry them at 110°C for 6 hours, and then The temperature was raised to 600°C at a heating rate of 4°C / min, and calcined for 4 hours to obtain a catalyst, which was designated as C2.
[0057] Based on the total weight of the catalyst, the content of the activated alumina is 88% by weight, the content of the alkaline earth metal oxide is 10% by weight, and the content of the silicon dioxide is 2% by weight.
[0058] The mechanical strength of the catalyst is shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com