A kind of adsorbent for oil refinery sewage treatment and its preparation and regeneration method

A technology for oil refinery sewage and adsorbent, which is applied in water/sewage treatment, adsorption water/sewage treatment, water/sludge/sewage treatment, etc. It can solve the problems of high bottom resin regeneration efficiency, low top resin regeneration efficiency, and acid solution seepage Slow and other problems, to achieve high anti-hydration ability and chemical stability, long operating cycle, large adsorption effect

Active Publication Date: 2022-02-18
广饶科力达石化科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the acid regeneration tower of the above-mentioned regeneration system is filled with resin, resulting in slow seepage of the acid solution and low regeneration efficiency, and because the acid regeneration tower is a downflow regeneration, the regeneration efficiency of the resin at the bottom is high, and the regeneration efficiency of the resin at the top is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of adsorbent for oil refinery sewage treatment and its preparation and regeneration method
  • A kind of adsorbent for oil refinery sewage treatment and its preparation and regeneration method
  • A kind of adsorbent for oil refinery sewage treatment and its preparation and regeneration method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Dissolve caustic mud in water and blow CO 2 , reacted for 6 hours, filtered to separate magnesium hydroxide, and dried at 120°C for 2 hours;

[0042] Add 3mol / L hydrochloric acid to the boiler fly ash, stir at 80°C for 6h and filter, add surfactants (SDBS and TEABr, the amount is 0.04 of the mass of the aluminum source) to the raffinate, and then add 2mol / L Sodium hydroxide solution, adjust the pH to 10.5, and co-precipitate; age at 100°C for 12h, filter, wash with deionized water until pH<8, and dry at 100°C for 4h to obtain aluminum-containing hydroxide. Mix according to the mass ratio of magnesium hydroxide and aluminum-containing hydroxide 6:8, add 4% binder citric acid, 3% forming aid scallop powder and appropriate amount of water, knead, shape, stand still, dry, and roast at 520°C After 2 hours, the finished adsorbent was obtained, which was denoted as A-1.

Embodiment 2

[0044] Dissolve caustic mud in water and blow CO 2 , reacted for 6 hours, filtered to separate magnesium hydroxide, and dried at 120°C for 2 hours;

[0045] Add 3mol / L hydrochloric acid to the boiler fly ash, stir at 80°C for 6h and then filter, add magnesium hydroxide (mass ratio of magnesium hydroxide to aluminum hydroxide 6:8) to the raffinate, add surface active agent (SDBS and TEABr, the dosage is 0.04 of the quality of the aluminum source); under stirring, add 2mol / L sodium hydroxide, adjust the pH to 10.5, and co-precipitate; age at 100°C for 12h, filter, and wash with deionized water until the pH< 8. Dry at 100°C for 4 hours to obtain magnesium-aluminum composite hydroxide; 4% binder citric acid, 3% forming aid scallop powder and appropriate amount of water, knead, shape, stand still, dry, and roast at 520°C for 2 hours , and the obtained adsorbent is denoted as A-2.

Embodiment 3

[0047] Dissolve caustic mud in water and blow CO 2 , reacted for 8 hours, filtered to separate magnesium hydroxide, and dried at 120°C for 2 hours;

[0048] Add 3mol / L hydrochloric acid to the gasification fine slag, stir at 60°C for 8h and filter, add magnesium hydroxide (mass ratio of magnesium hydroxide to aluminum-containing hydroxide is 7:8), add surface active agent (SDBS and TPABr, the dosage is 0.05 of the quality of the aluminum source); under stirring, add concentrated ammonia water, adjust the pH to 11.0, and coprecipitate; age at 80°C for 18h, filter, and wash with deionized water until pH<8, 80°C Dry for 12 hours to obtain magnesium-aluminum composite hydroxide; 3% binder citric acid, 3% forming aid safflower powder and appropriate amount of water, knead, shape, stand still, dry, and roast at 500°C for 3 hours, the obtained adsorption The agent is recorded as A-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an adsorbent for oil refinery sewage treatment and its preparation and regeneration method. The specific preparation process of the adsorbent includes: separating magnesium hydroxide through causticizing mud; extracting aluminum-containing solid waste with acid to obtain aluminum source, adding magnesium source and surfactant to the raffinate, and preparing a composite hydroxide containing compound hydroxide by co-precipitation method; after kneading, molding, drying, and roasting, it is used as an adsorbent for organic matter in oil refinery sewage; the adsorption regeneration system adopts the program The controller cooperates with the four-way valve at the inlet and outlet of the full radial reactor, and automatically controls the adsorption and regeneration process according to the set time and the COD value of the output. The adsorbent not only provides a way to utilize solid waste in the coal chemical industry, but also has the characteristics of large adsorption capacity for organic matter in refinery sewage, good regeneration performance in alkaline solution, and not easy to pulverize; the adsorption regeneration system based on this adsorbent The structure is simplified, the pressure is low, the processing capacity is large, the operation is stable, and the operation period is long.

Description

technical field [0001] The invention relates to the field of oil refinery sewage treatment, in particular to an adsorbent for oil refinery sewage treatment and a preparation and regeneration method thereof. Background technique [0002] At present, the chemical oxygen demand (COD) of many oil refining enterprises still exceeds the standard after treatment, which is low-quality sewage. If it is recycled to the system, it will cause certain harm to the operation of the system; if it is discharged directly, it will cause environmental pollution. Therefore, it is necessary to further treat low-quality sewage to effectively reduce the organic waste in it for reuse or direct discharge. [0003] Adsorption is one of the methods of sewage treatment, and choosing the right adsorbent is the key to adsorption technology. At present, the commonly used adsorbents include activated carbon, humic acid, resin, etc., whose synthesis and regeneration costs are relatively high, and their app...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/08B01J20/30B01J20/34C02F1/28C02F103/36
CPCB01J20/08B01J20/041B01J20/3475C02F1/281C02F2103/365
Inventor 王晓霞
Owner 广饶科力达石化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com