Corrosion-resistant floor paint and preparation method thereof

A floor paint and corrosion-resistant technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of poor wear resistance and corrosion resistance of floor paint, achieve low surface energy, increase cross-linking density, and improve the effect of bonding performance

Inactive Publication Date: 2019-08-30
陈卫国
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a corrosion-resistant floor paint and its preparation method in view of the poor wear resistance and corrosion resistance of the current floor paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of adhesive active agent is:

[0027] (1) Take 3,5-dimethoxy-4-hydroxycinnamic acid and add N,N-dimethylformamide according to the mass ratio of 1~4:40~50, protect it with argon, and store it at 20~25℃ Add imidazole 7-10 times the mass of 3,5-dimethoxy-4-hydroxycinnamic acid, stir and mix for 36-48 hours to obtain a stirred mixture, take the stirred mixture at a mass ratio of 20-30:4-9 and add deionized water , Stir and mix at -1~3°C for 20~30min to obtain the mixture, take the mixture according to the mass ratio of 2~5:10~15 and add ether for extraction, take the upper layer and dry it over anhydrous magnesium sulfate, distill and concentrate under reduced pressure to obtain a concentrated solution ;

[0028] (2) Take the concentrated solution and add the solvent according to the mass ratio of 2~5:10~15, stir and mix at 20~25°C for 20~30min, then add potassium carbonate with 3~5% of the concentrated solution, stir and mix for 8~10h to obtain St...

Embodiment 1

[0038] Epoxidized soybean oil: epoxy value 0.4.

[0039] The solvent is: take methanol and add tetrahydrofuran in a mass ratio of 5:10 to mix.

[0040] The preparation method of adhesive active agent is:

[0041] (1) Take 3,5-dimethoxy-4-hydroxycinnamic acid and add N,N-dimethylformamide at a mass ratio of 1:40, pass through argon protection, and add 3,5-dimethoxy Imidazole with 7 times the mass of methoxy-4-hydroxycinnamic acid was stirred and mixed for 36 hours to obtain a stirred mixture. Take the stirred mixture and add deionized water at a mass ratio of 20:4, and stir and mix at -1°C for 20 minutes to obtain a mixture. Take the mixture Add diethyl ether for extraction at a mass ratio of 2:10, take the upper layer, dry it over anhydrous magnesium sulfate, and distill and concentrate under reduced pressure to obtain a concentrated solution;

[0042] (2) Take the concentrated solution and add solvent according to the mass ratio of 2:10, stir and mix at 20°C for 20 minutes,...

Embodiment 2

[0052] Epoxidized soybean oil: epoxy value 0.4.

[0053] The solvent is: take methanol and add tetrahydrofuran in a mass ratio of 10:15 and mix to obtain.

[0054] The preparation method of adhesive active agent is:

[0055] (1) Take 3,5-dimethoxy-4-hydroxycinnamic acid and add N,N-dimethylformamide at a mass ratio of 4:50, pass through argon protection, and add 3,5-dimethoxy Imidazole with 10 times the mass of methoxy-4-hydroxycinnamic acid was stirred and mixed for 48 hours to obtain a stirred mixture. Take the stirred mixture and add deionized water at a mass ratio of 30:9, and stir and mix at 3°C ​​for 30 minutes to obtain a mixture. Take the mixture according to The mass ratio is 5:15, adding diethyl ether for extraction, taking the upper layer, drying it over anhydrous magnesium sulfate, and concentrating by distillation under reduced pressure to obtain a concentrated solution;

[0056] (2) Take the concentrated solution and add the solvent according to the mass ratio ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses corrosion-resistant floor paint and a preparation method thereof, and belongs to the technical field of coatings. An adhesive for preparation can improve cohesive performance and adhesion strength and improve the bonding property between the floor paint and a wood floor, and then covalent crosslinking can be formed between the adhesive active agent and the floor, so that mechanical performance of the floor is improved, the floor paint can still be kept on the surface of the floor and does not fall off in a friction and wear process, and a protective layer is formed. Curing auxiliary resin for preparation enables the surface of the formed paint film to be smooth, and enable active components to be uniformly dispersed, so that cross-linking density of the floor paintis improved; F420 polyaspartic ester resin is added in a preparation process of the floor paint, so that ultraviolet aging resistance and wear resistance of the paint film are improved, durability ofthe paint film is improved, damage of the external environment to the paint film is reduced, and overall performance is improved. According to the invention, the problems of poor wear resistance and poor corrosion resistance of existing floor paint are solved.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a corrosion-resistant floor paint and a preparation method thereof. Background technique [0002] Floor paint is a floor coating used for building interior floor coating finishes. The use of floor paint finishes is low in cost, light in weight, easy to maintain and update, and has good integrity. Its characteristics are impact resistance, high load, wear resistance; overall seamless, easy to clean; moisture-proof, dust-proof; general chemical corrosion resistance; non-slip or matte effect, etc. Solid wood flooring is the first choice for interior decoration. It is a floor material on the ground after the surface, side and other necessary processing of solid wood. It is a healthy and environmentally friendly product derived from nature. It preserves the original quality of wood. Natural texture, color and woody smell, the characteristics of natural solid wood make solid wood flooring hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/04C09D183/04C09D175/02C09D5/08C09D7/63
CPCC08L2205/035C09D5/08C09D7/63C09D129/04C09D183/04C08L83/04C08L75/02C08L71/02C08K5/3432
Inventor 陈卫国
Owner 陈卫国
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com