High-performance UV ink and preparation method and application thereof

A high-performance ink technology, applied in ink, applications, household appliances, etc., can solve the problems affecting the conductivity and poor adhesion of conductive materials such as conductive silver paste, and achieve good protection, prevent oxidation and discoloration, and good adhesion Effect

Inactive Publication Date: 2019-09-10
北京氦舶科技有限责任公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when UV ink is applied to flexible electronic components, its adhesion to flexible substrates such as PET, PP, and PE is poor, and it will also affect the conductivity of conductive materials such as conductive silver paste. In view of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The preparation method of above-mentioned UV printing ink, comprises the following steps:

[0040] (1) Stir and mix the saturated polyester resin and 1,6-hexanediol diacrylate evenly, the heating temperature is 50-60°C, the stirring rate is 500-1000r / min, and the stirring time is 3-8 hours;

[0041] (2) Add tetrahydrofuran acrylate to the mixture obtained in step (1), stir and mix evenly, the stirring temperature is 20-30°C, the stirring speed is 500-1000r / min, and the stirring time is 1-3 hours; then add ring Oxygen acrylate, methacrylate phosphate, photoinitiator, filler, toner, fumed silica, stir and mix evenly again, the stirring temperature is 20-30°C, the stirring speed is 500-1000r / min, and the stirring time is 3-5 hours;

[0042] (3) Grind the mixture obtained in step (2) on a three-roll machine until the fineness is ≤5 μm, add additives and stir and mix evenly, the stirring temperature is 20-30°C, and the stirring rate is 500-1000r / min, Stirring time is 3-5 h...

Embodiment 1

[0051] A kind of UV printing ink, its composition is as shown in table 1.

[0052] Epoxy acrylate resin adopts fatty acid modified bisphenol A type epoxy acrylate, viscosity is 10000cps. The saturated polyester resin is GK360. Methacrylate phosphate is PM1590. Fumed silica is H20. The photoinitiator is a mixture of TPO and BP with a mass ratio of 2:1. The toner is phthalo green. The filler is talcum powder. The additive is defoamer BYK-053.

[0053] The preparation method of above-mentioned UV printing ink:

[0054] (1) Stir and mix the saturated polyester resin and 1,6-hexanediol diacrylate evenly, the heating temperature is 60°C, the stirring rate is 500-1000r / min, and the stirring time is 3 hours;

[0055] (2) Add tetrahydrofuran acrylate to the mixture obtained in step (1) and stir to mix evenly, the stirring temperature is 25°C, the stirring speed is 1000r / min, and the stirring time is 1 hour; then add epoxy acrylate, methyl Acrylate phosphate, photoinitiator, fil...

Embodiment 2

[0059] A kind of UV printing ink, its composition is as shown in table 1.

[0060] The saturated polyester resin is BX7000A. Phosphate methacrylate is PQ611. Fumed silica is H18. The photoinitiator is a mixture of 184 and ITX, and the mass ratio of the two mixtures is 3:1. The color powder is phthalo blue. The filler is light calcium carbonate. The additive is defoamer BYK-2025S.

[0061] The preparation method of above-mentioned UV printing ink:

[0062] (1) Stir and mix the saturated polyester resin and 1,6-hexanediol diacrylate evenly, the heating temperature is 60°C, the stirring rate is 1000r / min, and the stirring time is 3 hours;

[0063] (2) Add tetrahydrofuran acrylate to the mixture obtained in step (1) and stir to mix evenly, the stirring temperature is 25°C, the stirring speed is 1000r / min, and the stirring time is 1 hour; then add epoxy acrylate, methyl Acrylate phosphate, photoinitiator, filler, toner, gas phase silica, stir and mix evenly again, the stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Pencil hardnessaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to view more

Abstract

The invention relates to high performance UV ink and a preparation method and application thereof. The ink comprises, by weight, 25-45 parts of epoxy acrylate resin, 8-12 parts of saturated polyesterresin, 2-5 parts of methacrylate phosphate, 15-25 parts of 1,6-hexanediol diacrylate, 5-7 parts of tetrahydrofuran acrylate, 0.5-1 part of fumed silica, 3-5 parts of a photoinitiator, 0.5-1 part of toner, 25-40 parts of a filler and 1-3 parts of an auxiliary agent. The ink has good adhesion on a flexible substrate, is applied to a flexible electronic component, has no influence on the electrical conductivity of a conductive material such as conductive silver paste, and can well protect a conductive line and prevent oxidative discoloration of the conductive line.

Description

technical field [0001] The invention relates to the field of UV ink, in particular to a high-performance UV ink and its preparation method and application. Background technique [0002] UV (ultraviolet, ultraviolet) curing technology is a material surface treatment technology that appeared in the 1960s. It has the characteristics of high efficiency, environmental protection, energy saving, high quality, and low investment. It is known as a new technology for green industry in the 21st century. . UV ink is the most common type of light-curing products, and has been widely used in the printing and packaging industry and the optoelectronics industry. UV ink is cured by UV irradiation at room temperature, and its energy consumption is only 10-20% of that of thermal curing. It is an energy-saving product. Its other advantage is that it does not contain volatile organic compounds, and the diluent used is acrylic acid with a high boiling point. Functional monomers participate in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/101
CPCC09D11/101
Inventor 饶龙来赵刚郎嘉良黄翟
Owner 北京氦舶科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka