A technology of bone china and underglaze color, which is applied in the field of preparation of underglaze color bone china, which can solve the problems of easy cracking, poor carcass hardness, and low service life, and achieve whiteness and brightness with less energy. Loss, the effect of increasing stability

Active Publication Date: 2019-09-17
FUJIAN QUANZHOU LONGPENG GROUP
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with traditional high-temperature porcelain, bone china also has its disadvantages. First, the hardness of the carcass is relatively poor, and it is easy to produce gaps in the porc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of underglaze color bone ash porcelain

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] A preparation method of underglaze color bone china includes the following steps:

[0023] (1) Weigh the ingredients according to the raw material formula of the body and the glaze, and the raw materials are separately mixed, crushed, mixed, and wet-milled to prepare the slurry and the glaze;

[0024] (2) The slurry and glaze prepared in step (1) are subjected to a magnetic separator to remove iron for many times until the iron content in the slurry and glaze is less than 0.05%;

[0025] (3) The green slurry obtained in step (2) is made into a green body, which is put into a kiln and sintered at 1220-1260°C for 4-5 hours to obtain a ceramic green body;

[0026] (4) Apply the glaze produced in step (2) to the surface of the ceramic green body obtained in step (3);

[0027] (5) After the glaze on the surface of the ceramic green body is dried, it is put into the kiln, and it is fired in a reducing atmosphere at 760-800℃ for 3-4h, then it is changed to an oxidizing atmosphere, and t...

Embodiment 1

[0034] An underglaze color bone ash porcelain, comprising a bone ash body and a glaze, the body comprising the following raw materials in parts by weight: 70 parts of bone charcoal, 35 parts of anorthite, 30 parts of quartz, 30 parts of kaolin, 10 parts of sepiolite, 20 parts of evening stone, 5 parts of vermiculite, 3 parts of diatomaceous earth, 8 parts of alumina, and 6 parts of magnesium oxide.

[0035] The glaze includes the following raw materials by weight: 20 parts of dolomite, 30 parts of cooked talc, 15 parts of anorthite, 10 parts of quartz, 12 parts of zirconium silicate, 6 parts of zinc oxide, 5 parts of magnesium silicate, and 1 part of barium oxide , 0.8 part of lanthanum oxide, 1 part of sodium polyacrylate.

[0036] A preparation method of underglaze color bone china includes the following steps:

[0037] (1) Weigh the ingredients according to the raw material formula of the body and the glaze, and the raw materials are separately mixed, crushed, mixed, and wet-mill...

Embodiment 2

[0048] An underglaze color bone ash china, comprising a bone ash body and a glaze. The body comprises the following raw materials in parts by weight: 80 parts of bone charcoal, 30 parts of anorthite, 40 parts of quartz, 20 parts of kaolin, 12 parts of sepiolite, 10 parts of evening stone, 10 parts of vermiculite, 5 parts of diatomaceous earth, 5 parts of alumina, 10 parts of magnesium oxide.

[0049] The glaze includes the following raw materials in parts by weight: 25 parts of dolomite, 20 parts of cooked talc, 18 parts of anorthite, 15 parts of quartz, 10 parts of zirconium silicate, 10 parts of zinc oxide, 3 parts of magnesium silicate, 3 parts of barium oxide , 0.5 parts of lanthanum oxide, 2 parts of sodium polyacrylate.

[0050] A preparation method of underglaze color bone china includes the following steps:

[0051] (1) Weigh the ingredients according to the raw material formula of the body and the glaze, and the raw materials are separately mixed, crushed, mixed, and wet-mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of underglaze color bone ash porcelain. The bone ash porcelain comprises a bone ash porcelain green body and glaze; the green body is prepared from the following raw materials in parts by weight: bone black, anorthite, quartz, kaolin, sepiolite, sillimanite, vermiculite, diatomaceous earth, alumina and magnesia. The green body takes bone charcoal, anorthite, quartz and kaolin as main raw materials, supplemented by sepiolite, sillimanite, vermiculite and diatomaceous earth, so that the prepared bone ash porcelain has higher strength; sepiolite with higher thermal stability, sillimanite with higher compressive strength and diatomaceous earth with higher impact strength, tensile strength and tear strength cooperate with bone black, anorthite, quartz and kaolin, so that the finally prepared bone ash porcelain has high compressive strength and impact strength for use as a daily porcelain.

Description

Technical field [0001] The invention belongs to the field of porcelain preparation, and specifically relates to a preparation method of underglaze color bone ashes porcelain. Background technique [0002] Bone china is a high-end porcelain produced in the United Kingdom with a history of more than 260 years. Because of its "thin paper, transparent like a mirror, sound like a chime, and white like jade", the porcelain is delicate and transparent, the shape is beautiful and elegant, the color surface is moist and bright, and the flower surface is colorful. It has achieved its white texture and luxury Its shape has the dual values ​​of use and art. Historically, it was a treasure for the court and a noble collection. It was a symbol of power and status. It was favored by many buyers. It is known as the "king of porcelain". After generations of master craftsmen, it has gradually become a world ceramic treasure. [0003] With its high quality, high style and high taste, bone china has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/447C04B35/622C04B35/63C04B41/86
CPCC04B35/447C04B35/622C04B35/6303C04B41/009C04B41/5022C04B41/86C04B2235/3481C04B2235/3418C04B2235/349C04B2235/3445C04B2235/3217C04B2235/3206C04B2235/656C04B2235/6567C04B2235/6583C04B2235/96C04B2235/9607C04B41/4535
Inventor 苏康福
Owner FUJIAN QUANZHOU LONGPENG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap