Preparation method of Monel metal for pressed plates

An alloy and plate technology, applied in the field of preparation of monel alloy, can solve the problems of multiple harmful inclusions, poor plasticity and high gas content, and achieve the effects of improving batch stability, reducing composition segregation and accurate alloy composition.

Inactive Publication Date: 2019-09-20
陕西宝锐金属有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing Monel alloy for pressing plates, which solv

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of preparation method of the Monel alloy that is used for pressing plate of the present invention specifically implements according to the following steps:

[0043] Step 1, batching: batching is carried out according to the requirements of the composition range in the Monel grade, and the furnace capacity of the melting crucible is 500kg, then the batching weight is Ni: 325Kg; Cu: 152.5Kg; C: 1Kg; Si: 1.5Kg; Mn: 10Kg ; Fe: 10Kg;

[0044] Step 2, prepare refractory material crucible for smelting alloy

[0045] Mix the refractory material evenly, put it into the mold with graphite core inserted in the middle, and place the mold in the induction coil, knot it into a barrel-shaped semi-finished crucible, and send electricity to induction heat the graphite core to bake the semi-finished crucible to obtain the surface Dense crucible, after baking, remove the graphite core, clean the inside of the crucible with a dense surface, put the nickel-copper alloy used for furn...

Embodiment 2

[0058] A kind of preparation method of the Monel alloy that is used for pressing plate of the present invention specifically implements according to the following steps:

[0059] Step 1, batching: batching is carried out according to the requirements of the composition range in the Monel grade, and the furnace capacity of the melting crucible is 500kg, then the batching weight is Ni: 325Kg; Cu: 143.25Kg; C: 0.75Kg; Si: 1.5Kg; Mn: 6Kg; Fe: 6Kg; Al: 15Kg; Ti: 2.5Kg;

[0060] Step 2, prepare refractory material crucible for smelting alloy

[0061] Mix the refractory material evenly, put it into the mold with graphite core inserted in the middle, and place the mold in the induction coil, knot it into a barrel-shaped semi-finished crucible, and send electricity to induction heat the graphite core to bake the semi-finished crucible to obtain the surface Dense crucible, after baking, remove the graphite core, clean the inside of the crucible with a dense surface, put the nickel-copp...

Embodiment 3

[0074] A kind of preparation method of the Monel alloy that is used for pressing plate of the present invention specifically implements according to the following steps:

[0075] Step 1, batching: batching is carried out according to the requirements of the composition range in the Monel grade, and the furnace capacity of the melting crucible is 500kg, then the batching weight is Ni: 325Kg; Cu: 152.5Kg; C: 1Kg; Si: 1.5Kg; Mn: 10Kg ; Fe: 10Kg;

[0076] Step 2, prepare refractory material crucible for smelting alloy

[0077] Mix the refractory material evenly, put it into the mold with graphite core inserted in the middle, and place the mold in the induction coil, knot it into a barrel-shaped semi-finished crucible, and send electricity to induction heat the graphite core to bake the semi-finished crucible to obtain the surface Dense crucible, after baking, remove the graphite core, clean the inside of the crucible with a dense surface, put the nickel-copper alloy used for furn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of Monel metal for pressed plates. The preparation method is implemented according to the following process: (1) Monel metal raw materials are prepared; (2) refractory material crucibles for smelting alloys are prepared; (3) a vacuum induction smelting furnace is used for vacuum induction smelting to obtain Monel metal ingots; (4) the ingots are machined; the head loose and empty parts are cut off; and the surfaces are polished without scales; (5) the vacuum arc remelting is performed; and (6) the surface layers of the Monel metal ingots are removed through lathe machining. The method guarantees precise metal components, and prevents the metal element oxidation problem; and through the subsequent vacuum arc remelting process, the component segregation is further reduced, and the metal structure uniformity is improved.

Description

technical field [0001] The invention belongs to the technical field of alloy preparation, and in particular relates to a preparation method of Monel alloy used for pressing plates. Background technique [0002] Monel alloy is a kind of nickel-based alloy. Its main components are Ni and Cu. In addition to the main elements Ni and Cu, it usually contains other alloying elements, such as iron, manganese, silicon, aluminum, sulfur, and carbon. etc., they play the role of solid solution strengthening, second phase strengthening, grain boundary strengthening, etc., and have good corrosion resistance to halogen elements and their compounds, non-oxidizing acids, alkalis, salts, etc., and can also withstand hydrogen fluorine Corrosion of acid, acetic acid, reducing inorganic acid, organic acid and other media; at the same time, Monel alloy also has excellent comprehensive properties such as good formability, easy cutting and welding. In 1906, Monel alloy was successfully developed b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/02C22C1/03C22C19/03F27B14/10C04B35/043
CPCC04B35/043C04B2235/3217C04B2235/3409C22C1/02C22C1/03C22C19/002C22C19/03F27B14/10F27B2014/102
Inventor 宋皓萌陈洁高晖
Owner 陕西宝锐金属有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap