Composite physical pigments and fillers with anti-rust and flame-retardant properties and preparation method thereof

A flame retardant performance and composite technology, which is applied in the field of composite pigments and fillers and their preparation, can solve problems such as performance to be improved, insufficient adhesion, high price, etc., to expand high value-added applications, improve anti-rust performance, enhance The effect of market competitiveness and application scope

Active Publication Date: 2019-09-27
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the existing technology cannot use steel slag and montmorillonite on a large scale and with high added value, the filler pigments currently used contain a large amount of heavy metal oxides such as chromium, zinc, and lead, which will cause serious environmental pollution after entering the antirust coating, and the existing Body pigments and fillers have problems of single function, insufficient adhesion, high price and performance to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite physical pigments and fillers with anti-rust and flame-retardant properties and preparation method thereof
  • Composite physical pigments and fillers with anti-rust and flame-retardant properties and preparation method thereof
  • Composite physical pigments and fillers with anti-rust and flame-retardant properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0029]

[0030] The mass fraction of the phosphoric acid solution is 86%; the steel slag fine powder is an electric furnace drum slag fine powder, and its particle size is 25 μm to 45 μm; the graphene is analytically pure; the cetyltrimethylammonium bromide is Analytical pure; the mass fraction of the dilute hydrochloric acid solution is 3%; the montmorillonite is calcium-based montmorillonite.

[0031] Firstly, the phosphoric acid solution and the fine steel slag powder were mixed at room temperature by using a constant temperature magnetic stirrer, the stirring speed was 800r / min, and the stirring time was 7h to obtain the porous steel slag fine powder.

[0032] Secondly, use a constant temperature magnetic stirrer to mix dilute hydrochloric acid solution, cetyltrimethylammonium bromide and montmorillonite at a stirring temperature of...

Embodiment 2

[0036] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0037]

[0038] The mass fraction of the phosphoric acid solution is 82%; the steel slag fine powder is a mixture of hot stuffy slag fine powder and converter drum slag fine powder, and its particle size is 25 μm to 45 μm; the graphene is analytically pure; the hexadecyl Trimethylammonium bromide is analytically pure; the mass fraction of the dilute hydrochloric acid solution is 6%; the montmorillonite is magnesium-based montmorillonite.

[0039] Firstly, the phosphoric acid solution and the fine steel slag powder were mixed at room temperature by using a constant temperature magnetic stirrer, the stirring speed was 950r / min, and the stirring time was 6h to obtain the porous steel slag fine powder.

[0040] Secondly, use a constant temperature magnetic stirrer to mix dilute hydrochloric acid solution, cetyltrimethylammonium bromide and ...

Embodiment 3

[0044] Taking the preparation of product 100g of the present invention as an example, the components used and their mass proportions are:

[0045]

[0046] The mass fraction of the phosphoric acid solution is 80%; the steel slag fine powder is a mixture of wind-quenched slag fine powder and electric furnace hot slag fine powder, and its particle size is 25 μm to 45 μm; the graphene is analytically pure; the hexadecane Trimethylammonium bromide is analytically pure; the mass fraction of the dilute hydrochloric acid solution is 5%; the montmorillonite is sodium-calcium montmorillonite.

[0047] Firstly, the phosphoric acid solution and the fine steel slag powder were mixed at normal temperature by using a constant temperature magnetic stirrer, the stirring speed was 1000r / min, and the stirring time was 8h to obtain the porous steel slag fine powder.

[0048] Secondly, use a constant temperature magnetic stirrer to mix dilute hydrochloric acid solution, cetyltrimethylammonium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses composite physical pigments and fillers with anti-rust and flame-retardant properties and a preparation method thereof, and belongs to the field of utilization of solid waste resources. The pigments and fillers comprise a phosphoric acid solution, steel slag micro powder, graphene, cetyltrimethylammonium bromide, a dilute hydrochloric acid solution and montmorillonite, wherein the steel slag powder is one or more of hot braised slag micro powder, air quench slag micro powder, molten iron desulfurization slag micro powder, casting residual slag micro powder, converter hot splashing slag micro powder, converter drum slag micro powder, electric furnace hot splashing slag micro powder and electric furnace drum slag micro powder. According to the composite physical pigments and fillers with anti-rust and flame-retardant properties and the preparation method thereof, not only is the production cost of existing physical pigments and fillers reduced by 30%-50%, but the anti-rust property, flame-retardant property and adhesive force of the physical pigments and fillers are also improved; the integration of anti-rust property, flame-retardant property and high adhesive force on the physical pigments and fillers is realized; the market competitiveness and application range of the physical pigments and fillers are significantly enhanced; the high value-added application of steel slag and the montmorillonite is expanded; a new thought of using waste to enhancing the effect is realized.

Description

technical field [0001] The invention belongs to the field of utilization of solid waste resources, and in particular relates to a composite pigment and filler with antirust and flame retardant properties and a preparation method thereof. Background technique [0002] Steel slag is solid waste produced in the steelmaking process, accounting for about 15% to 20% of steelmaking output, and its main components are CaO, Fe 2 o 3 、Al 2 o 3 , SiO 2 , MgO, P 2 o 5 , MnO, SO 3 And a small amount of free calcium oxide, of which CaO (35.0% ~ 55.0%), Fe 2 o 3 (10.0%~35.0%), Al 2 o 3 (2.0% ~ 12.0%) content is relatively high, the stockpiling of a large number of steel slags not only takes up valuable land, but also pollutes the surrounding environment and groundwater. In my country, there are a large number of montmorillonites composed of silicate sheets with nanometer thickness, which mainly include calcium-based montmorillonite, sodium-based montmorillonite, sodium-calcium-b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D5/18
CPCC08K3/346C08K3/36C08K9/04C08K9/12C08K13/06C08K2003/2206C08K2003/222C08K2003/2227C08K2003/2272C08K2201/003C09D5/084C09D5/18C08K3/042
Inventor 张浩龙红明宗志芳高青叶雯静张梦莉
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap