Non-shrinkage cementing material made of phosphogypsum and preparation method of non-shrinkage cementing material and concrete

A technology of cementitious material and phosphogypsum, applied in cement production and other directions, can solve problems such as improper control of raw material mix ratio, poor quality of concrete products, poor performance of cementitious materials, etc., so as to improve the value of comprehensive utilization of resources and save cement. Dosage, the effect of improving the density

Active Publication Date: 2019-10-25
赵源 +2
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the inappropriate use of phosphogypsum in the prior art and the inappropriate control of the ratio of raw materials in the cementitious material, the resulting cementitious material has poor performance and unsatisfactory shrinkage performance, which leads to the application of the cementitious material to the preparation of concrete and other products. During the process, the quality of the concrete product is poor, especially the shrinkage deformation value is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-shrinkage cementing material made of phosphogypsum and preparation method of non-shrinkage cementing material and concrete
  • Non-shrinkage cementing material made of phosphogypsum and preparation method of non-shrinkage cementing material and concrete
  • Non-shrinkage cementing material made of phosphogypsum and preparation method of non-shrinkage cementing material and concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The cementitious material is mixed with ordinary portland cement, and the mixed material is composed of 5% phosphogypsum, 60% mixture of fly ash and phosphorus slag, 15% water-quenched slag, and 20% steel slag in weight percentage. It is mixed; the mass ratio of mixed material to 42.5 ordinary Portland cement is 1:7.

Embodiment 2

[0027] The cementitious material is mixed with ordinary portland cement, wherein the mixed material is composed of 20% phosphogypsum, 30% phosphorus slag, 30% water-quenched slag and 20% steel slag in weight percentage; the mixed material and 52.5 The mass ratio of ordinary Portland cement is 1:9.

Embodiment 3

[0029] The cementitious material is mixed with ordinary portland cement, and the mixed material is composed of 20% phosphogypsum, 40% fly ash, 30% water-quenched slag and 10% steel slag in weight percentage; the mixed material The mass ratio to 42.5 ordinary Portland cement is 3:7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of comprehensive utilization of phosphogypsum, in particular to a non-shrinkage cementing material made of the phosphogypsum and a preparation method of the non-shrinkage cementing material and concrete. The phosphogypsum, coal ash or phosphorous slag, water quenching slag and steel slag are compounded to form a mixed material, the non-shrinkage cementing material is prepared by adding ordinary Portland cement, high-value comprehensive utilization of the phosphogypsum is achieved, sulfate in the phosphogypsum is used as an activator to activate theactivity of the coal ash, the phosphorous slag, the water quenching slag, the steel slag and the like, and reacts with the coal ash, the phosphorous slag, the water quenching slag, the steel slag, Al2O3 in the cement and hydrated product of the cement Ca(OH)2 to form ettringite Aft, capillary pore in the concrete is filled and blocked, the quality percentage control of raw materials is combined, the performance of the cementing material is improved, thus when the cementing material is applied to the concrete, the compactness of the concrete is improved, volume expansion is generated, the non-shrinkage high-performance concrete is obtained, at the same time, the hydration heat of the cement is lowered, cement consumption is saved, and the production cost of the concrete is lowered.

Description

technical field [0001] The invention relates to the technical field of comprehensive utilization of phosphogypsum, in particular to a non-shrinkage cementitious material made of phosphogypsum, a preparation method thereof and concrete. Background technique [0002] Phosphogypsum is a solid waste produced by decomposing phosphate rock with sulfuric acid and filtering to produce phosphoric acid in the production process of wet-process phosphoric acid. For every ton of wet-process phosphoric acid produced, about 4-5 tons of phosphogypsum will be discharged. Phosphogypsum is in powder form, the main phase composition is calcium sulfate dihydrate, containing a small amount of quartz; the main chemical components are calcium oxide, sulfur trioxide, silicon dioxide, phosphorus pentoxide, fluorine ions, etc.; The content of gypsum is generally above 90%. According to relevant statistics, the global discharge of phosphogypsum has reached 150 million tons, while the discharge of phos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B7/26C04B7/21C04B7/19C04B7/36C04B28/14
CPCC04B7/19C04B7/21C04B7/26C04B7/36C04B28/143C04B7/02C04B18/141C04B18/142C04B18/145C04B18/08C04B14/02C04B14/06C04B2103/40Y02P40/10
Inventor 赵源王勇秦思波高遇事
Owner 赵源
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products