High heat-resistant anti-aging CPVC power cable protection tube and preparation method thereof

A power cable and anti-aging technology, which is applied in the field of high heat-resistant and anti-aging CPVC power cable protection tubes and its preparation, can solve the problems of heat resistance and anti-aging performance to be improved, and achieve a simple and controllable preparation method. The effect of obvious reduction of heat release and change of heat release history

Pending Publication Date: 2019-11-08
东莞市庆隆塑胶有限公司
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing CPVC power pipes still have the problems of heat resistance and anti-aging performance that need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A CPVC power cable protection tube with high heat resistance and aging resistance, which includes the following raw materials in parts by weight: 450 parts of CPVC, 300 parts of PVC, 150 parts of calcium powder, 50 parts of toughening agent, 3 parts of nitrile rubber, and stabilizer 30 parts, 10 parts of flame retardant, 5 parts of stearic acid, 12 parts of paraffin. The toughening agent is a terpolymer of methyl methacrylate, butadiene, and styrene; the stabilizer is a mixture of xylitol, cerium citrate, and zinc glycerol in a ratio of 2:1:1; the flame retardant is hydrotalcite , zinc borate, and carbon black are mixed at a ratio of 5:1:0.5.

[0021] A preparation method for a CPVC power cable protection tube with high heat resistance and aging resistance, comprising the following preparation steps:

[0022] (1) Weigh raw materials according to parts by weight;

[0023] (2) Mixing the raw materials weighed in parts by weight for 10 minutes;

[0024] (3) Put the raw ...

Embodiment 2

[0026] A high heat-resistant, anti-aging CPVC power cable protection tube, which includes the following raw materials in parts by weight: 550 parts of CPVC, 200 parts of PVC, 200 parts of calcium powder, 30 parts of toughening agent, 15 parts of nitrile rubber, stabilizer 20 parts, 20 parts of flame retardant, 1 part of stearic acid, 18 parts of paraffin. The toughening agent is a terpolymer of methyl methacrylate, butadiene, and styrene; the stabilizer is a mixture of xylitol, cerium citrate, and zinc glycerol in a ratio of 2:1:1; the flame retardant is hydrotalcite , zinc borate, and carbon black are mixed at a ratio of 5:1:0.5.

[0027] A preparation method for a CPVC power cable protection tube with high heat resistance and aging resistance, comprising the following preparation steps:

[0028] (1) Weigh raw materials according to parts by weight;

[0029] (2) Mixing the raw materials weighed in parts by weight for 20 minutes;

[0030] (3) Put the raw materials mixed in ...

Embodiment 3

[0032] A high heat-resistant, anti-aging CPVC power cable protection tube, which includes the following raw materials in parts by weight: 500 parts of CPVC, 250 parts of PVC, 180 parts of calcium powder, 35 parts of toughening agent, 5 parts of nitrile rubber, stabilizer 25 parts, 15 parts of flame retardant, 3 parts of stearic acid, 15 parts of paraffin. The toughening agent is a terpolymer of methyl methacrylate, butadiene, and styrene; the stabilizer is a mixture of xylitol, cerium citrate, and zinc glycerol in a ratio of 2:1:1; the flame retardant is hydrotalcite , zinc borate, and carbon black are mixed at a ratio of 5:1:0.5.

[0033] A preparation method for a CPVC power cable protection tube with high heat resistance and aging resistance, comprising the following preparation steps:

[0034] (1) Weigh raw materials according to parts by weight;

[0035] (2) Mixing the raw materials weighed in parts by weight for 15 minutes;

[0036] (3) Put the raw materials mixed in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high heat-resistant anti-aging CPVC power cable protection tube. The tube comprises the following raw materials, in parts by weight: 450-550 parts of CPVC, 200-300 parts of PVC, 150-200 parts of calcium powder, 30-50 parts of a toughening agent, 3-15 parts of nitrile rubber, 20-30 parts of a stabilizer, 10-20 parts of a flame retardant, 1-5 parts of stearic acid, and 12-18 parts of paraffin. The high heat-resistance anti-aging CPVC power cable protection tube provided by the invention has a temperature resistant to heat deformation of 98 DEG C or more, has excellent high-temperature resistance, and can adapt to high-temperature harsh environments; the flame retardant performance reaches a FV-0 level; the tube has the characteristics of good flexibility, uneasy breakage and aging, long service life, no radiation pollution and a light weight; and in addition, a preparation method provided by the invention is simple and controllable, and the production is easy tooperate.

Description

technical field [0001] The invention belongs to the technical field of power cable protection tubes, and in particular relates to a high heat-resistant and anti-aging CPVC power cable protection tube and a preparation method thereof. Background technique [0002] CPVC power pipes are usually used as cable protection pipes with excellent corrosion resistance. In recent years, they have been widely used in steel, metallurgy, petroleum, chemical, fertilizer, dye, pharmaceutical, electric power, environmental protection and sewage treatment industries. It has the characteristics of good performance, good insulation performance, no pollution, and convenient construction. It is an ideal substitute for traditional asbestos cable pipes and ordinary PVC pipes. CPVC power pipe is extruded with CPVC (chlorinated polyethylene resin) as the main raw material. CPVC resin is obtained by chlorination and modification of PVC (polyvinyl chloride) resin. After PVC resin is chlorinated, the irr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/24C08L27/06C08L9/02C08L91/06C08L51/04C08K13/02C08K3/26C08K3/38C08K3/04C08K5/098C08K5/09
CPCC08L27/24C08L2201/08C08L2203/202C08L2205/035C08K2003/387C08L2201/02C08L27/06C08L9/02C08L91/06C08L51/04C08K13/02C08K3/26C08K3/38C08K3/04C08K5/098C08K5/09
Inventor 庾文辉
Owner 东莞市庆隆塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com