Halogen-free flame-retardant synergistic functional masterbatch special for polyphenyl ether modification and preparation method thereof

A functional masterbatch, flame retardant and synergistic technology, applied in the field of plastic modification processing, can solve the problems of poor thermal stability, large loss of flame retardant performance, low fluidity, etc., to enhance compactness and structural stability, reduce physical Loss of mechanical properties, effect of reducing loss of mechanical properties

Active Publication Date: 2019-12-27
江苏万纳普新材料科技有限公司
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to address the problems of strong hygroscopicity, easy oxidation, poor thermal stability, poor compatibility with resin matrix, large loss of flame retardant performance and low fluidity of red phosphorus in the process of modifying halogen-free flame-retardant polyphenylene ether. , poor dispersion and other application defects, as well as problems such as thermal degradation caused by powder friction during twin-screw direct blending extrusion processing, resulting in flame retardant performance and physical and mechanical decline, while overcoming traditional polymer or inorganic wall material coating The defect that red phosphorus cannot provide sufficient protection, the present invention proposes a method of using a wall material with flame retardant synergy and dense material to implement multiple composite coatings on red phosphorus, and then combine it with the corresponding flame retardant synergist and auxiliary agent Low-temperature internal mixing to prepare a halogen-free flame-retardant synergistic functional masterbatch for polyphenylene ether halogen-free flame-retardant modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant synergistic functional masterbatch special for polyphenyl ether modification and preparation method thereof
  • Halogen-free flame-retardant synergistic functional masterbatch special for polyphenyl ether modification and preparation method thereof
  • Halogen-free flame-retardant synergistic functional masterbatch special for polyphenyl ether modification and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A special halogen-free flame retardant synergistic functional masterbatch for polyphenylene ether modification, the quality ratio of raw materials is as follows:

[0034]

[0035] The preparation method of the multi-composite coated red phosphorus used in the above-mentioned polyphenylene ether modified special-purpose halogen-free flame-retardant synergistic functional masterbatch is as follows:

[0036] Add 230L of absolute ethanol, 120kg of red phosphorus, 7kg of aluminum sol, and 1kg of zinc oxide sol into the enamel reaction kettle with a stirring and temperature control device, stir evenly and add to 40°C, then add dropwise at an even speed with a mass percentage of 10.0wt .% ammonia water, and control the pH value of the reaction solution at 7.5 to 8.5 to promote the sol-gel reaction between the aluminum sol and the zinc oxide sol. After the addition is completed, continue to stir for 3.5 hours to end the reaction; , and dried in an oven at 125° C. for 8 hours...

Embodiment 2

[0039] A special halogen-free flame retardant synergistic functional masterbatch for polyphenylene ether modification, the quality ratio of raw materials is as follows:

[0040]

[0041] The preparation method of the multi-composite coated red phosphorus used in the above-mentioned polyphenylene ether modified special-purpose halogen-free flame-retardant synergistic functional masterbatch is as follows:

[0042] Add 230L of absolute ethanol, 120kg of red phosphorus, 8kg of aluminum sol, and 1.5kg of zinc oxide sol into the enamel reaction kettle with a stirring and temperature control device, stir evenly and add to 35°C, then add dropwise at an even speed with a mass percentage of 11.5 wt.% ammonia water, and control the pH value of the reaction solution at 7.5-8.5 to promote the sol-gel reaction between the aluminum sol and the zinc oxide sol. After the dropwise addition, continue to stir for 4 hours to end the reaction; then wash with water and filter , and dried in an ov...

Embodiment 3

[0045] A special halogen-free flame retardant synergistic functional masterbatch for polyphenylene ether modification, the quality ratio of raw materials is as follows:

[0046]

[0047] The preparation method of the multi-composite coated red phosphorus used in the above-mentioned polyphenylene ether modified special-purpose halogen-free flame-retardant synergistic functional masterbatch is as follows:

[0048] Add 230L of absolute ethanol, 120kg of red phosphorus, 7.5kg of aluminum sol, 2kg of zinc oxide sol into the enamel reaction kettle with a stirring and temperature control device, stir evenly and add to 37°C, then add dropwise at an even speed with a mass percentage of 12.5 wt.% ammonia water, and control the pH value of the reaction solution at 7.5-8.5 to promote the sol-gel reaction between the aluminum sol and the zinc oxide sol. After the dropwise addition, continue to stir for 4 hours to end the reaction; then wash with water and filter , and dried in an oven a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of plastic modification processing, in particular to halogen-free flame-retardant synergistic functional masterbatch special for polyphenyl ether modification and a preparation method thereof. According to the functional masterbatch, multiply composited coated red phosphorus is used as a phosphorus flame retardant; and the functional masterbatch is prepared from the following components in percentage by mass: 70.0 wt.%-80.0 wt.% of the multiply composited coated red phosphorus, 3.0 wt.%-5.0 wt.% of organic phosphate, 17.0 wt.%-25.0 wt.% of an ethylene-methyl acrylate copolymer, 0.5 wt.%-1.0 wt.% of a dispersing agent and 0.3 wt.%-0.5 wt.% of a lubricating agent. Compared with the traditional flame-retardant functional masterbatch, the functionalmasterbatch prepared by the method has the advantages that thermal stability and water resistance of red phosphorus are remarkably enhanced, the activity of red phosphorus and the corrosion of red phosphorus to a base material are reduced, and the compatibility with a resin matrix is improved, so that the flame-retardant effect of red phosphorus to polyphenyl ether is more effectively improved.

Description

technical field [0001] The invention relates to the technical field of plastic modification processing, in particular to a special halogen-free flame retardant synergistic functional masterbatch for polyphenylene ether modification and a preparation method thereof. Background technique [0002] Polyphenylene ether is an engineering plastic with excellent dielectric and electrical insulation properties, which is widely used in the fields of industry and household electronic appliances. When polyphenylene ether is used to manufacture electronic and electrical components or related peripheral equipment, it is often necessary to implement flame retardant modification to improve its safety in use. The flame retardant modification of polyphenylene ether can be realized by adding a flame retardant and melt blending through a twin-screw extruder. Flame retardants can prevent polyphenylene ether from being ignited and inhibit flame propagation, which can effectively improve the comb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/08C08K9/10C08K3/02C08K5/523C08J3/22C08L71/12
CPCC08J3/226C08J2423/08C08J2371/12C08K9/10C08K2003/026C08K5/523
Inventor 李翰卿汪晓东
Owner 江苏万纳普新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products