A kind of anti-icing pavement sealing layer material and preparation method thereof

A technology of anti-icing and layer materials, applied in coatings, anti-corrosion coatings, asphalt coatings, etc., can solve problems affecting the durability of asphalt mixtures, high energy consumption, and environmental damage, and achieve improved photocatalysis and anti-fouling effect, improvement of water repellency, and effect of preventing water damage

Active Publication Date: 2021-06-29
CHANGAN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, passive snow removal technology usually consumes a lot of energy and has poor effect; while active snow melting technology uses mainly corrosive substances such as chloride salts, which cause great damage to the environment and seriously affect the durability of asphalt mixture during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-icing pavement sealing layer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The present embodiment provides a kind of anti-icing pavement sealing material, in parts by weight, is made of the following raw materials: emulsified asphalt is 57%, filler is 5.4%, mixed solution is 15.2%, organosilicon polyacrylic resin is 22.4%;

[0035] The filler is made of the following raw materials: 65.3% zinc oxide, 19.8% zirconium dioxide, 14.9% ferric chloride;

[0036] The mixed solution is made from the following raw materials: 33.3% of acetylacetone, 16.7% of butyl acetate, and 50% of cyclohexane.

[0037] The preparation method of the anti-icing pavement sealing material of the present embodiment, the method specifically comprises the following steps:

[0038] Step 1: After weighing zinc oxide, zirconium dioxide and ferric chloride, add them to a planetary ball mill in turn, mill for 2 hours, take them out and calcinate them in a muffle furnace at 600°C for 1 hour, then take them out and rinse them with distilled water, and take out the precipitate for ...

Embodiment 2

[0043] The present embodiment provides a kind of anti-icing pavement sealing material, in parts by weight, is made of the following raw materials: emulsified asphalt is 59.8%, filler is 5.4%, mixed solution is 12.4%, organosilicon polyacrylic resin is 22.4%;

[0044] The filler is made of the following raw materials: 73.7% zinc oxide, 21.1% zirconium dioxide, 5.2% ferric chloride;

[0045] The mixed solution is made from the following raw materials: 33.3% of acetylacetone, 16.7% of butyl acetate, and 50% of cyclohexane.

[0046] The preparation method of the anti-icing pavement sealing material of this embodiment is the same as that of Embodiment 1.

[0047] See Table 1 for the test results of the asphalt pavement performance of the anti-icing pavement sealing material of this embodiment.

Embodiment 3

[0049] The present embodiment provides a kind of anti-icing pavement sealing material, is made of the following raw materials in parts by weight: emulsified asphalt is 56.2%, filler is 6.2%, mixed solution is 11%, organosilicon polyacrylic resin is 26.6%;

[0050] The filler is made of the following raw materials: 69.1% zinc oxide, 21.8% zirconium dioxide, 9.1% ferric chloride;

[0051]The mixed solution is made from the following raw materials: 33.3% of acetylacetone, 16.7% of butyl acetate, and 50% of cyclohexane.

[0052] The preparation method of the anti-icing pavement sealing material of this embodiment is the same as that of Embodiment 1.

[0053] See Table 1 for the test results of the asphalt pavement performance of the anti-icing pavement sealing material of this embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention provides an anti-icing pavement sealing material and a preparation method thereof, which is made of the following raw materials: emulsified asphalt, filler, mixed solution and organic silicon polyacrylic resin; the filler is made of the following raw materials: zinc oxide, Zirconium and ferric chloride; the mixture is made from: acetylacetone, butyl acetate, cyclohexane. The present invention has undergone a large number of researches and tests, and the results show that applying the anti-icing emulsified asphalt seal material produced by the present invention to the laying of asphalt pavement can achieve the effect of melting snow and deicing, and can significantly improve the anti-icing performance and anti-icing performance of the road surface. slippery performance. In addition, this material can also form a dense waterproof layer on the asphalt pavement, which can effectively prevent water damage on the pavement, and can also play a role in sealing the cracks in the pavement, which has the effect of preventive maintenance.

Description

technical field [0001] The invention relates to the technical field of road materials, in particular to an anti-icing pavement, in particular to an anti-icing pavement sealing material and a preparation method thereof. Background technique [0002] Due to the advantages of convenient construction and maintenance and good driving stability, asphalt pavement has been widely popularized and applied in various grades of highways, and has gradually developed into the main structural form of highways in our country. However, under the influence of freezing rain and snowfall in winter, the asphalt pavement is prone to icing and other phenomena. The icing on the road surface not only has an adverse effect on driving, but also brings serious damage to the asphalt pavement, especially the "black ice" problem. Seriously endanger driving safety. Therefore, in view of the freezing problem of asphalt pavement in winter, the development of asphalt pavement sealing material with excellent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D133/04C09D5/08C09D7/62
CPCC08K2003/2244C08K2003/2296C08L2201/08C09D5/08C09D195/005C09D7/62C08L43/04C08K9/04C08K3/22C08K3/16
Inventor 何锐梁映平郑睢宁陈华鑫王振军薛成段德峰房建宏郭凤俊
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com