APAO-modified polyurethane waterborne resin and preparation method thereof
A water-based resin and polyurethane technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems such as insufficient water resistance, insufficient adhesion, and poor anti-sag performance, and achieve good anti-sag, improve adhesion, The effect of excellent adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] An APAO modified polyurethane water-based resin, which consists of the following formula in parts by weight: 42.0 parts of isophorone diisocyanate, 32.0 parts of polytetrahydrofuran diol, 7.0 parts of APAO grafted with hydroxyethyl acrylate, and 8.0 parts of butanediol 2.5 parts of trimethylolpropane, 3.5 parts of dimethylolpropionic acid, 0.8 parts of hydroxypropyl acrylate, 0.06 parts of dibutyltin dilaurate, 5.0 parts of ethanol, 4.5 parts of ethylenediamine, 6.8 parts of triethylamine, 150.0 parts of deionized water.
[0026] A kind of preparation method of APAO modified polyurethane aqueous resin in the present embodiment, comprises the following steps:
[0027] a) In the multifunctional reactor, add polytetrahydrofuran diol, butanediol, trimethylolpropane, and dimethylolpropionic acid in sequence according to the weight of the formula, raise the temperature to 110°C, and dehydrate under vacuum for 1.5h ;
[0028] b) Cool down to 65°C, add isophorone diisocyanate...
Embodiment 2
[0031] An APAO modified polyurethane water-based resin, in parts by weight, consists of the following formula: 35.0 parts of toluene diisocyanate, 35.0 parts of polycarbonate diol, 6.0 parts of APAO grafted with hydroxyethyl acrylate, and 7.0 parts of neopentyl glycol , 4.0 parts of dipropylene glycol, 4.0 parts of dimethylol propionic acid, 0.7 parts of hydroxypropyl acrylate, 0.06 parts of dibutyltin dilaurate, 6.8 parts of ethanol, 4.5 parts of ethylenediamine, 5.0 parts of ammonia water, 140.0 parts of deionized water share.
[0032] A kind of preparation method of APAO modified polyurethane aqueous resin in the present embodiment, comprises the following steps:
[0033] a) In the multifunctional reactor, add polycarbonate diol, neopentyl glycol, dipropylene glycol, and dimethylol propionic acid in sequence according to the weight of the formula, raise the temperature to 105°C, and dehydrate under vacuum for 2.0 h;
[0034] b) Cool down to 70°C, add toluene diisocyanate ...
Embodiment 3
[0037] An APAO modified polyurethane water-based resin, which consists of the following formula in parts by weight: 28.0 parts of hexamethylene diisocyanate, 35.0 parts of polyether diol, 4 parts of APAO grafted with hydroxyethyl acrylate, and 8.8 parts of butanediol 4.0 parts of dimethylolpropionic acid, 0.6 parts of hydroxypropyl acrylate, 0.05 parts of dibutyltin dilaurate, 6.0 parts of ethanol, 4.0 parts of ethylenediamine, 5.0 parts of triethylamine, and 130.0 parts of deionized water.
[0038] A kind of preparation method of APAO modified polyurethane aqueous resin in the present embodiment, comprises the following steps:
[0039]a) In the multifunctional reactor, add polyether diol, butanediol, and dimethylolpropionic acid in sequence according to the weight of the formula, raise the temperature to 110°C, and dehydrate under vacuum for 1.5h;
[0040] b) Cool down to 60°C, add hexamethylene diisocyanate and pass through N 2 , add the formula amount of dibutyltin dilaura...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap