Glass film and preparation method thereof

A glass film and modification technology, which is applied in the production of film/sheet adhesives, adhesives, bulk chemicals, etc., can solve problems affecting GPS satellite navigation system signal reception, signal interference, poor performance, etc. The effect of size controllable, prolonging the service life and improving the bonding fastness

Inactive Publication Date: 2020-02-11
宁波泰意德过滤技术有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the existing glass film contains a metal layer, which is prone to signal interference to the GPS satellite navigation system in the car or indoors, thereby affecting the signal reception of the GPS satellite navigation system, radio communication and mobile phones.
[0004] Therefore, how to develop a glass film with good heat insulation performance, strong anti-ultraviolet performance and strong anti-interference is a problem that those skilled in the art have paid close attention to for a long time. Although some glass films have appeared on the market, their performance is still unsatisfactory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of glass sticking film, described glass sticking film is made up of the raw material of following parts by weight: 100 parts of modified PET resins, 7 parts of modified masterbatches, 0.8 parts of coupling agents and 2.5 parts of additives; the modified masterbatches are Benzimidazole diketone compounds and modified PET resin coat inorganic oxide solid particles.

[0033] The modified PET resin is polyhydroxy cage silsesquioxane modified PET resin.

[0034] The cage-type silsesquioxane-modified PET resin is prepared by adding polyhydroxy cage-type silsesquioxane to the raw materials of terephthalic acid and ethylene glycol for polycondensation reaction, and the polyhydroxy cage-type silsesquioxane The amount of siloxane added accounted for 5.5% by mass of the raw material.

[0035] The benzimidazole diketone compound is 5-hydroxy-1,2,6-trimethyl-1H-benzimidazole-4,7-dione.

[0036] The inorganic oxide solid particles are titanium dioxide.

[0037] The particle...

Embodiment 2

[0045] A glass film, the glass film is made up of the following raw materials in parts by weight: 100 parts of modified PET resin, 4 parts of modified masterbatch, 0.5 part of coupling agent and 2 parts of additive; the modified masterbatch is Benzimidazole diketone compounds and modified PET resin coat inorganic oxide solid particles.

[0046] The modified PET resin is polyhydroxy cage silsesquioxane modified PET resin.

[0047] The cage-type silsesquioxane-modified PET resin is prepared by adding polyhydroxy cage-type silsesquioxane to the raw materials of terephthalic acid and ethylene glycol for polycondensation reaction, and the polyhydroxy cage-type silsesquioxane The amount of siloxane added accounted for 3% by mass of the raw material.

[0048] The benzimidazole diketone compound is 2-(hydroxymethyl)-1H-benzimidazole-4,7-dione.

[0049] The inorganic oxide solid particles are silicon dioxide.

[0050] The particle size of the modified masterbatch is 100nm.

[0051]...

Embodiment 3

[0058] A kind of glass sticking film, described glass sticking film is made up of the raw material of following parts by weight: 100 parts of modified PET resins, 12 parts of modified masterbatches, 1.0 parts of coupling agents and 3 parts of additives; the modified masterbatches are Benzimidazole diketone compounds and modified PET resin coat inorganic oxide solid particles.

[0059] The modified PET resin is polyhydroxy cage silsesquioxane modified PET resin.

[0060] The cage-type silsesquioxane-modified PET resin is prepared by adding polyhydroxy cage-type silsesquioxane to the raw materials of terephthalic acid and ethylene glycol for polycondensation reaction, and the polyhydroxy cage-type silsesquioxane The amount of siloxane added accounted for 8% by mass of the raw material.

[0061] The mass ratio of the benzimidazole diketone compound is 5-hydroxy-1,2,6-trimethyl-1H-benzimidazole-4,7-dione and 2-(hydroxymethyl) -1H-benzimidazole-4,7-dione composition.

[0062] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass film, which comprises the following raw materials by weight: 100 parts of a modified PET resin, 1-15 parts of modified master batch, 0.2-1.2 parts of a coupling agent and 1.5-3.5 parts of an additive, wherein the modified master batch is benzimidazoledione compound and modified PET resin coated inorganic oxide solid particles. According to the invention, the glass film has good comprehensive properties of heat insulation, ultraviolet resistance, interference resistance, oxidation resistance, easy maintenance and the like. The invention further discloses a preparation method of the glass film, wherein the comprehensive performance of the glass film is improved, the overall performance of the glass film is uniform, the service life of the glass film is prolonged, and the large-scale application and popularization is well facilitated.

Description

technical field [0001] The invention relates to the technical field of glass film, in particular to a glass film and a preparation method thereof. Background technique [0002] Glass film refers to the product used to paste a thin layer of glass film on the surface of automobile glass, architectural glass or other glass. Generally speaking, glass film is a single-layer or multi-layer functionalized polyester composite film material (PET), which makes it extremely Excellent clarity, excellent strength and durability, as well as high heat insulation efficiency, impact resistance or decoration performance, adhered to the surface of glass and other materials through back adhesive to improve the performance of glass. It is mainly used in the fields of automobile glass, building door and window glass, mobile phone display screen, TV display screen, etc., so that it has the functions of heat preservation, heat insulation, energy saving, explosion protection, beautification of appe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/25C08L67/04C08L71/02C08K13/06C08K3/34C08K7/24C08K5/41C08K9/10C08K3/22C08K3/36C08J5/18C08J3/22
CPCC08J3/223C08J5/18C08J2367/02C08J2471/02C08K3/34C08K3/36C08K5/41C08K7/24C08K9/10C08K13/06C08K2003/2241C08K2201/014C09J2467/006C09J7/255Y02P20/54
Inventor 赵金燕
Owner 宁波泰意德过滤技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com