Method of improving dyeing properties of hard wooden door

A dyeing performance and wooden door technology, applied in wood treatment, impregnated wood, wood impregnation, etc., can solve the problems that do not meet the aesthetic needs of consumers, dye molecules are difficult to dye, increase the amount of dye, etc., to promote rapid Uniform coloring, highlighting light and heat stability, and reducing repelling effect

Inactive Publication Date: 2020-02-18
含山县宏达门业家具有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the structural characteristics of hard wood and the hydrophobic effect, it is difficult for dye molecules to be dyed, and the color is very unstable. It will change and fade under the influence of light and climate.
The existing treatment method is to increase the amount of dye, and improve the coloring performance of wooden doors through vacuum pressure, microwave treatment, etc. However, after this treatment method, the color tone after dyeing is dull and single, and the color is deep, which does not meet the needs of consumers. Aesthetic needs for color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for improving the dyeing performance of hard wooden doors, comprising adding the prepared strengthening agent to the dye solution, and after homogenizing for 20 minutes, the hard wooden doors can be dyed; the preparation method of the strengthening agent comprises the following steps:

[0020] (1) Weigh 7.5 grams of calcium sulfate and 0.5 grams of sodium polyacrylate into a beaker, add 70 milliliters of distilled water, disperse with magnetic stirring for 30 minutes, use phosphate buffer to adjust the pH of the system between 8.8-9.0, add 0.30 grams of nano Silica, ultrasonically dispersed for 60 minutes, placed in a reaction kettle, pressurized for 13 hours, and the reaction temperature was 120°C. After the reaction, the supernatant liquid was removed by filtration, and the remaining products were washed with deionized water and absolute ethanol for 3 The second time, dry the product in a vacuum oven at 80°C and grind it into powder;

[0021] (2) Put a four-n...

Embodiment 2

[0030] A method for improving the dyeing performance of hardwood doors, comprising adding the prepared strengthening agent to the dye solution, and after homogenizing for 25 minutes, the hardwood doors can be dyed; the preparation method of the strengthening agent comprises the following steps:

[0031] (1) Weigh 7.8 grams of calcium sulfate and 0.55 grams of sodium polyacrylate into a beaker, add 75 milliliters of distilled water, disperse with magnetic stirring for 35 minutes, use phosphate buffer to adjust the pH of the system between 8.8-9.0, add 0.32 grams of nano Silica, ultrasonically dispersed for 65 minutes, placed in a reaction kettle, pressurized for 14 hours, and the reaction temperature was 125°C. After the reaction was completed, the supernatant liquid was removed by filtration, and the remaining products were washed with deionized water and absolute ethanol for 4 hours. The second time, dry the product in a vacuum oven at 85°C and grind it into powder;

[0032] ...

Embodiment 3

[0041] A method for improving the dyeing performance of hardwood doors, comprising adding the prepared strengthening agent into the dye solution, and after homogenizing for 30 minutes, the hardwood doors can be dyed; the preparation method of the strengthening agent comprises the following steps:

[0042] (1) Weigh 8.0 grams of calcium sulfate and 0.6 grams of sodium polyacrylate into a beaker, add 80 milliliters of distilled water, disperse with magnetic stirring for 40 minutes, use phosphate buffer to adjust the pH of the system between 8.8-9.0, add 0.35 grams of nano Silica, ultrasonically dispersed for 70 minutes, placed in a reaction kettle, pressurized for 15 hours, and the reaction temperature was 130°C. After the reaction, the supernatant liquid was removed by filtration, and the remaining products were washed with deionized water and absolute ethanol for 5 The second time, dry the product in a vacuum oven at 90°C and grind it into powder;

[0043] (2) Put a four-necke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of wood processing and treatment and discloses a method of improving dyeing properties of a hard wooden door. According to the method, a reinforcing agentobtained through preparation is added into a dye liquor, and after homogenization treatment for 20-30 minutes, dyeing treatment can be performed on the hard wooden door; the reinforcing agent emulsioncan lower surface tension of wood in contact with dyestuff, rapid absorption of the dyestuff by cellulose is promoted, the color of the dyestuff is maintained, and the wooden door obtained after dyeing has prominent optical stability and thermal stability and is suitable for all types of dyestuff (including acid dyestuff, basic dyestuff, reactive dyestuff and the like); nanoparticles are well dispersed, the wet rubbing fastness of the hard wooden door can be improved, and the hard wooden door has extremely good fastness to light, sublimation and sunlight; and besides, a hardening layer formedthrough calcium-based crystallization can protect the surface of a wooden structure, so that the waterproofness of a wood surface is improved, and the fastness to washing is high.

Description

technical field [0001] The invention belongs to the technical field of wood processing, and in particular relates to a method for improving the dyeing performance of hard wooden doors. Background technique [0002] Due to the advantages of strong plasticity, environmental protection and beauty of hard wood, it occupies a place in the furniture market, especially in the choice of wooden doors necessary for the family. Or fashionable and modern, doors with different decoration styles give consumers a wide choice space. [0003] The application of wood dyeing technology began in 1913. Since then, many scholars have done a lot of research on the basic theory and technology of wood dyeing, which has made the practical and industrialization of wood dyeing technology develop rapidly. Wood staining is an aspect of improving the visual properties of wood and is one of the avenues for decoration. Dyeing the wooden door can enrich the shape and decoration, so as to enhance the appear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/00B27K3/18B27K3/36B27K3/52B27K5/02
CPCB27K3/007B27K3/18B27K3/36B27K3/52B27K5/02
Inventor 赵卫
Owner 含山县宏达门业家具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap