Graphene natural rubber polymer automobile cushion composite foamed material and preparation method thereof

A technology of natural rubber and car seat cushions, applied in the field of rubber products, can solve the problems of poor mechanical properties such as tensile strength, insufficient light weight, high compression set rate, etc., to achieve improved quality stability, excellent mechanical properties, and good mechanical properties Effect

Inactive Publication Date: 2020-03-27
FUJIAN WUCHIHENG TECH DEV CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 1. High compression set rate, low rebound rate, easy to deform during use, and easy to damage when used as a car seat cushion material;
[0008] 2. Either the quality is not light enough, or the mechanical properties such as tensile strength after foaming are poor, easy to damage, and the practical life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene natural rubber polymer automobile cushion composite foamed material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of graphene natural rubber macromolecule automobile cushion composite foaming material, is made of the raw material that comprises following parts by weight:

[0041] Natural rubber 66-74 parts, isoprene rubber 13-17 parts, polyolefin elastomer 9-12 parts, nano-media 4-6 parts, graphene 1.5-1.8 parts, carbon nanotubes 1.8-2.2 parts, zinc oxide 1.5- 2 parts, heat stabilizer 3-4 parts, cross-linking agent 1.5-1.8 parts, expansion agent 2-2.4 parts, foaming agent 2-2.4 parts.

[0042] In the present embodiment, described graphene natural rubber macromolecule automobile cushion composite foaming material is made of the raw material that comprises following weight part:

[0043] 70 parts of natural rubber, 15 parts of isoprene rubber, 10 parts of polyolefin elastomer, 5 parts of nano media, 1.65 parts of graphene, 2 parts of carbon nanotubes, 1.75 parts of zinc oxide, 3.5 parts of heat stabilizer, 1.7 parts of crosslinking agent , 2.2 parts of expansion agent, 2.2 pa...

Embodiment 2

[0058] A kind of graphene natural rubber macromolecule automobile cushion composite foaming material, is made of the raw material that comprises following parts by weight:

[0059] 66 parts of natural rubber, 17 parts of isoprene rubber, 12 parts of polyolefin elastomer, 4 parts of nano media, 1.5 parts of graphene, 1.8 parts of carbon nanotubes, 1.5 parts of zinc oxide, 3 parts of heat stabilizer, 1.5 parts of crosslinking agent , 2 parts of expansion agent, 2 parts of foaming agent.

[0060] In this embodiment, the graphene is reduced graphene oxide.

[0061] In this embodiment, the carbon nanotubes have a diameter of 90-120 nm and a length of 1.5-3 μm.

[0062] In this embodiment, the nano-medium is nano-calcium carbonate.

[0063] In the present embodiment, the thermal stabilizer is a mixture of zinc stearate and stearic acid; the mass ratio of zinc stearate and stearic acid in the mixture of zinc stearate and stearic acid is 10 :5.

[0064] In this embodiment, the cro...

Embodiment 3

[0074] A kind of graphene natural rubber macromolecule automobile cushion composite foaming material, is made of the raw material that comprises following parts by weight:

[0075] 74 parts of natural rubber, 13 parts of isoprene rubber, 9 parts of polyolefin elastomer, 6 parts of nano media, 1.8 parts of graphene, 2.2 parts of carbon nanotubes, 2 parts of zinc oxide, 4 parts of heat stabilizer, 1.8 parts of crosslinking agent , 2.4 parts of expansion agent, 2.4 parts of blowing agent.

[0076] In this embodiment, the graphene is reduced graphene oxide.

[0077] In this embodiment, the carbon nanotubes have a diameter of 90-120 nm and a length of 1.5-3 μm.

[0078] In this embodiment, the nano-medium is nano-calcium carbonate.

[0079] In the present embodiment, the thermal stabilizer is a mixture of zinc stearate and stearic acid; the mass ratio of zinc stearate and stearic acid in the mixture of zinc stearate and stearic acid is 10 :7.

[0080] In this embodiment, the cr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene natural rubber polymer automobile cushion composite foamed material and a preparation method thereof. The graphene natural rubber polymer automobile cushion composite foamed material is prepared from the following raw materials in parts by weight: 66 to 74 parts of natural rubber, 13 to 17 parts of isoprene rubber, 9 to 12 parts of polyolefin elastomer, 4 to 6 parts of a nano medium, 1.5 to 1.8 parts of graphene, 1.8 to 2.2 parts of carbon nano tube, 1.5 to 2 parts of zinc oxide, 3 to 4 parts of a heat stabilizer, 1.5 to 1.8 parts of a cross-linking agent, 2to 2.4 parts of an expanding agent and 2 to 2.4 parts of a foaming agent. The graphene natural rubber polymer automobile cushion composite foamed material is low in density and has ultra-light property; the compression set rate is low, the rebound resilience is good, durability is achieved, and deformation is not likely to happen in the using process; the mechanical properties such as tensile strength and elongation at break are good, the ultralight property and the excellent mechanical property are well considered, and the market application prospect is promising.

Description

technical field [0001] The invention relates to the technical field of rubber products, in particular to a graphene natural rubber polymer composite foaming material for automobile seat cushions and a preparation method thereof. Background technique [0002] Natural rubber (NR) is a natural polymer compound with cis-1,4-polyisoprene as the main component, and 91% to 94% of its components are rubber hydrocarbons (cis-1,4-polyisoprene Diene), and the rest are non-rubber substances such as protein, fatty acid, ash, sugar, etc. It is generally flake solid, relative density 0.94, refractive index 1.522, elastic modulus 2-4MPa, softens at 130-140°C, sticky and soft at 150-160°C, and begins to degrade at 200°C. It has high elasticity at room temperature, slightly plastic, and crystallizes and hardens at low temperature. It has good alkali resistance, but not strong acid resistance. Insoluble in water, lower ketones and alcohols, can swell in non-polar solvents such as chloroform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/00C08K13/02C08K3/04C08K3/26C08K3/22C08J9/10
CPCC08J9/0061C08J9/0066C08J9/0071C08J9/0095C08J9/103C08J2203/04C08J2307/00C08J2409/00
Inventor 丁天宁丁德材丁幼丝
Owner FUJIAN WUCHIHENG TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More