Craft porcelain with raised particle effect on glaze surface and preparation method thereof

A technology of granule and glaze, which is applied in the field of craft porcelain with raised granule effect on the glaze surface and its preparation field. It can solve the problems of glaze shrinkage, dull glaze effect, and difficult to grasp the glaze layer, so as to increase the melting temperature. , full of layers, and increase the effect of aesthetics

Active Publication Date: 2020-04-07
FUJIAN DEHUA JIASHUN CRAFTS
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Coloring the surface of daily-use ceramic dishes is a common method to increase the beauty of the product. Generally, screen printing, hand-painted patterns on the glaze or direct drawing of patterns are used; water-blocking oil-adjustable glaze powder is also used to scrape patterns under the glaze. These methods cannot naturally integrate the rendering effect between the pattern and the glaze layer. The products produced are relatively dull, the glaze effect is flat, the glaze layer is not easy to grasp, it is difficult to control the quality, and it is easy to form defects such as shrinkage glaze and dirty color, which affect the quality of the product. The overall decorative effect of the product, a little further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] A method for preparing craft porcelain with a glazed surface having the effect of raised particles, comprising the steps of:

[0040] Step 1, weighing the raw materials of the green body according to their weight parts, crushing and sieving to obtain powder, and wet ball milling the powder to obtain mud;

[0041] Step 2, degassing, aging and drying the mud material to obtain a green body;

[0042] Step 3, placing the green body in a kiln, firing at 950-980°C for 6-8 hours to obtain a ceramic green body;

[0043] Step 4, weighing the raw materials of the glaze slurry according to their weight, crushing, sieving, and wet ball milling to obtain a glaze, and then mixing the prepared glaze and frit dry particles evenly in a certain proportion to obtain a surface glaze;

[0044] Step 5, applying glaze on the ceramic biscuit;

[0045] Step 6, sending the glazed ceramic biscuit into a kiln for sintering, so as to obtain craft porcelain with the effect of raised particles on t...

Embodiment 1

[0060] A craft porcelain whose glaze surface has the effect of raised particles, including a body and a glaze set on the body,

[0061] The green body includes the following raw materials in parts by weight: 35 parts of quartzite, 18 parts of anorthite, 25 parts of Dehua kaolin, 15 parts of calcite, 5 parts of amphibole, 5 parts of serpentine, 3 parts of magnesium oxide, 0.5 parts of lanthanum oxide parts, 0.1 parts of germanium oxide.

[0062]The surface glaze includes glaze slurry and frit dry particles, and the glaze slurry includes the following raw materials in parts by weight: 25 parts of Dehua quartz, 15 parts of halloysite, 10 parts of Dehua feldspar, 8 parts of montmorillonite, and 6 parts of sepiolite , 12 parts of dickite, 3 parts of pyroxene, 1 part of alumina, and 0.2 parts of lanthanum oxide.

[0063] The dry frit granules include the following raw materials in parts by weight: 25 parts of limestone, 15 parts of dolomite, 10 parts of Dehua pyrophyllite, 10 parts...

Embodiment 2

[0086] A craft porcelain whose glaze surface has the effect of raised particles, including a body and a glaze set on the body,

[0087] The green body includes the following raw materials in parts by weight: 40 parts of quartzite, 15 parts of anorthite, 30 parts of Dehua kaolin, 10 parts of calcite, 8 parts of amphibole, 3 parts of serpentine, 5 parts of magnesium oxide, and 1 part of lanthanum oxide parts, 0.3 parts of germanium oxide.

[0088] The surface glaze includes glaze slurry and frit dry particles, and the glaze slurry includes the following raw materials in parts by weight: 30 parts of Dehua quartz, 10 parts of halloysite, 12 parts of Dehua feldspar, 5 parts of montmorillonite, and 8 parts of sepiolite , 16 parts of dickite, 1 part of pyroxene, 2 parts of alumina, and 0.1 part of lanthanum oxide.

[0089] Dry frit granules include the following raw materials in parts by weight: 22 parts of limestone, 18 parts of dolomite, 12 parts of Dehua pyrophyllite, 6 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a craft porcelain with a raised particle effect on a glaze surface and a preparation method thereof. The craft porcelain with a raised particle effect on a glaze surface comprises a green body and overglaze arranged on the green body, the overglaze comprises a glaze slurry and frit dry particles, the glaze slurry comprises the following raw materials: Dehua quartz, halloysite, Dehua feldspar, montmorillonite, sepiolite, dickite, pyroxene, aluminum oxide and lanthanum oxide, during preparation of the craft porcelain, the overglaze is uniformly applied to the surface of the green body, then the green body is sent into a kiln for firing, the surface of the fired craft porcelain has the decoration effect of naturally fused convex bumped artistic patterns, and bump points are clear, vivid, full and rich in layering sense, thus further improving the aesthetic sense of the craft porcelain.

Description

technical field [0001] The invention belongs to the field of craft porcelain preparation, and in particular relates to craft porcelain with the effect of raised particles on the glaze surface and a preparation method thereof. Background technique [0002] Coloring the surface of daily-use ceramic dishes is a common method to increase the beauty of the product. Generally, screen printing, hand-painted patterns on the glaze or direct drawing of patterns are used; water-blocking oil-adjustable glaze powder is also used to scrape patterns under the glaze. These methods cannot naturally integrate the rendering effect between the pattern and the glaze layer. The products produced are relatively dull, the glaze effect is flat, the glaze layer is not easy to grasp, it is difficult to control the quality, and it is easy to form defects such as shrinkage glaze and dirty color, which affect the quality of the product. The overall decorative effect of the product has been further improv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/34C03C8/02C04B41/86
CPCC04B33/13C03C8/02C04B33/34C04B41/86C04B41/5022C04B2235/3481C04B2235/3208C04B2235/3427C04B2235/3445C04B2235/3206C04B2235/3227C04B2235/3287
Inventor 陈金贵
Owner FUJIAN DEHUA JIASHUN CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com