Cooling liquid for diamond wire cutting

A diamond wire cutting and cooling liquid technology, applied in the petroleum industry, lubricating compositions, etc., can solve problems such as poor biodegradability and fish death, and achieve the effects of enhanced adhesion, less impurities, and thickened cooling liquid

Inactive Publication Date: 2020-04-10
江苏德比新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Alcohols and ethers are one of the main components in the current traditional cooling liquid, which have poor biodegradability and can remain in water and soil for a long time. The COD content of 5300mg / L can cause fish death

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A coolant for diamond wire cutting, the weight percentage of each component in the coolant is: 16% stabilizer, 0.5% water-soluble lubricant, 1% extreme pressure agent, 3% preservative, lubricant Wet agent 1%, defoamer 0.01%, the balance is deionized water.

[0022] Preferably, the stabilizer is at least one of triethanolamine oleate, polyvinylpyrrolidone, and ammonium polymethacrylate; the water-soluble lubricant is polyethylene glycol, triethyl phosphate, oleic acid at least one of; the extreme pressure agent is at least one of borax, sodium silicate; the preservative is at least one of dodecenyl succinic acid diethanolamide, sodium benzoate; the wetting The agent is at least one of fatty alcohol polyoxyethylene ether and sodium dodecylbenzenesulfonate; the defoamer is at least one of polyoxyethylene polyoxypropanolamine ether and simethicone.

Embodiment 2

[0024] A coolant for diamond wire cutting, the weight percentage of each component in the coolant is: 26% stabilizer, 2% water-soluble lubricant, 4% extreme pressure agent, 8% preservative, lubricant Wet agent 4%, defoamer 0.04%, the balance is deionized water.

[0025] Preferably, the stabilizer is at least one of triethanolamine oleate, polyvinylpyrrolidone, and ammonium polymethacrylate; the water-soluble lubricant is polyethylene glycol, triethyl phosphate, oleic acid at least one of; the extreme pressure agent is at least one of borax, sodium silicate; the preservative is at least one of dodecenyl succinic acid diethanolamide, sodium benzoate; the wetting The agent is at least one of fatty alcohol polyoxyethylene ether and sodium dodecylbenzenesulfonate; the defoamer is at least one of polyoxyethylene polyoxypropanolamine ether and simethicone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a cooling liquid for diamond wire cutting. The cooling liquid comprises the following components in percentage by weight: 16-26% of a stabilizer, 0.5-2% of a water-soluble lubricant, 1-4% of an extreme pressure agent, 3-8% of a preservative, 1-4% of a wetting agent, 0.01-0.04% of a defoaming agent and the balance of deionized water. The cooling liquid has the advantages of high efficiency, low toxicity and good water solubility, and can effectively inhibit the damage of microbial growth to the stability of the cooling liquid.

Description

technical field [0001] The invention relates to the field of coolant, in particular to a coolant for diamond wire cutting. Background technique [0002] Diamond wire cutting technology replaces traditional mortar cutting. It uses electroplating technology to bond diamond and steel wire to attach diamond abrasive to the surface of steel wire, and directly acts on the surface of silicon rod or silicon ingot to produce grinding with diamond wire to achieve cutting. Effect. Diamond wire cutting has the characteristics of fast cutting speed, less silicon consumption, and low material loss. Due to the high efficiency of diamond wire cutting and the use of pure water as the main solvent, more heat will be generated on the surface of the wire saw and the silicon rod, which needs to be dissipated and lubricated in time by the cooling liquid; to suppress the reaction of silicon powder and pure water during cutting. Fire accidents; therefore coolant is used in diamond wire cutting te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10N30/06C10N30/12
CPCC10M173/02C10M2201/087C10M2201/102C10M2207/126C10M2207/144C10M2209/08C10M2209/104C10M2209/108C10M2215/04C10M2215/08C10M2217/028C10M2219/044C10M2223/04C10M2229/041
Inventor 吴友洲戚晓峰
Owner 江苏德比新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products