A thin strip and silicon steel technology, which is applied in the field of silicon steel thin strip preparation, can solve the problems of affecting steel quality and large resource consumption

Active Publication Date: 2021-09-14
NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above analysis, the embodiment of the present invention aims to provide a method for preparing a silicon steel strip to solve the technical problems of high resource consumption and residual oxygen and inclusions affecting the quality of steel in the existing silicon steel strip preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of silicon steel thin strip
  • A kind of preparation method of silicon steel thin strip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The application discloses a method for preparing a thin silicon steel strip, such as figure 1 shown, including the following steps:

[0034] Step 1. Using a high-vacuum single-roller rotary quenching arc melting system to prepare silicon-containing silicon-iron-carbon alloy thin strips

[0035] Step 1.1, after weighing high-purity iron powder, graphite powder and silicon powder, mix and stir according to a certain ratio to obtain mixed raw materials;

[0036] Step 1.2, put the mixed raw material prepared in step 1.1 into the first quartz test tube, then put the first quartz test tube into the corundum crucible, and use a horizontal heating furnace to carry out program temperature control heating, the heating time is 25 ~ 35min, the heating temperature It is 1780~1800K, and the block master alloy is obtained;

[0037] Step 1.3, put the bulk master alloy prepared in step 1.2 into a second quartz test tube of moderate length, set the second quartz test tube with an eject...

Embodiment 2

[0058] The preparation method of present embodiment prepares silicon steel comprises the following steps:

[0059] Step 1, using a high-vacuum single-roller rotary quenching arc melting system to prepare silicon-iron-carbon alloy thin strips, including the following steps:

[0060] Step 1.1. Weigh out 9.5g of high-purity iron powder, 0.4g of graphite powder and 0.1g of silicon powder with a JJ623BC electronic balance, mix and stir evenly to obtain mixed raw materials;

[0061] Step 1.2, put the mixed raw materials into the first quartz test tube, heat the mixed raw materials to 1780-1800K in a horizontal heating furnace, and the heating time is 25-35 minutes to obtain a block master alloy;

[0062] Step 1.3. Put the blocky master alloy into the second quartz test tube which has an ejection hole and is fixed under the spray casting gun, so that the block master alloy in the test tube is just placed in the heating area of ​​the induction coil, and the copper mold is cooled Plac...

Embodiment 3

[0070] The preparation method that present embodiment prepares silicon steel comprises the following steps: as figure 2 as shown,

[0071] Step 1: preparing silicon-iron-carbon alloy thin strips;

[0072] In order to reduce the content of sulfur element in silicon steel to 0.006%, a pretreatment process of molten iron is required. The pretreatment adopts the method of single-blowing granular magnesium for desulfurization. After the molten iron is added with slag accumulator and slag is removed once, powder is sprayed for desulfurization. After standing for 3 minutes, slag accumulator is added, and powder is sprayed and slag is removed again. The composition of molten iron after pretreatment is C=0.5%, Si=2.5%, S=0.006%, Als=0.025%, N=0.008%, P<0.005%, O<0.003%.

[0073] The molten iron obtained in step 1 is made into a thin slab through strip continuous casting, that is, the molten iron obtained after the pretreatment of molten iron in step 1 flows into the tundish preheate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a thin silicon steel strip, which belongs to the technical field of metal material smelting and solves the problems of high resource consumption and residual oxygen and inclusions affecting the quality of steel in the existing silicon steel thin strip preparation process. The preparation method of the silicon steel thin strip of the present application comprises the following steps: step 1, preparing the silicon-iron-carbon alloy thin strip; step 2, decarburizing the silicon-iron-carbon alloy thin strip to obtain the silicon steel thin strip; step 3, detecting the thickness of the thin strip Carbon element distribution, microstructure, phase, average carbon content and magnetic properties. The silicon steel strip preparation method of the present application omits the converter smelting and other processes, which is of great significance for saving energy consumption investment, shortening the smelting process, reducing production and environmental protection.

Description

technical field [0001] The invention relates to the technical field of metal material smelting, in particular to a method for preparing a thin silicon steel strip. Background technique [0002] Silicon steel, also known as "electrical steel", is a silicon-iron soft magnetic alloy with extremely low carbon content (about <0.02wt%), and the Si content is generally 1.5wt%-4.5wt%. Silicon steel accounts for more than 90% of the total magnetic materials, and is the most widely used soft magnetic alloy, mainly used in military industry and electronic power industry. Its production technology is complicated and its manufacturing technology is strict, so it is called "handicraft among steel products." [0003] Decarburization has a great influence on the final product performance of silicon steel. The less residual carbon content in the steel, the less possibility of magnetic failure and reduced magnetic performance during its service. The traditional silicon steel smelting pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/06C21D3/04C22C38/02C22C33/06C22C38/06
CPCB22D11/0611C21D3/04C22C33/06C22C38/001C22C38/002C22C38/02C22C38/06
Inventor 洪陆阔艾立群孙彩娇候耀斌周美洁周玉青孟凡峻
Owner NORTH CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap