Preparation method of high-strength flame-retardant waterproof glass wool

A glass wool and high-strength technology, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of poor flame retardancy of glass wool, high brittleness of glass wool, general waterproof performance, etc., to enhance toughness and mechanical strength, reduce Brittleness, effect of improving impact resistance

Inactive Publication Date: 2020-05-08
常州武城服饰有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The technical problem to be solved by the present invention is to provide a high-strength anti-impact performance and poor durability of glass wool due to its high brittleness and general mechanical strength, as well as its poor flame-retardant performance and general waterproof performance. Preparation method of fire-proof and waterproof glass wool

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Preparation of mixed slurry:

[0035] Bagasse and wheat straw were put into an oven at a mass ratio of 5:1, dried for 3 hours at a temperature of 60°C, and then put into a pulverizer after drying to obtain a mixed material. The mixed material and hydrochloric acid with a mass fraction of 6% were pressed Put it into a beaker with a mass ratio of 1:10, stir with a stirrer at a speed of 400r / min for 60min, place the beaker in a microwave oven after stirring, and microwave for 10min at a power of 600W to prepare a mixed slurry;

[0036] Preparation of oxidation reaction solution:

[0037] Place the above beaker in an ice-water bath, add dropwise sodium hydroxide solution with a mass fraction of 10% to the beaker to adjust the pH value to 11, raise the temperature of the water bath to 80°C, and react at a constant temperature for 40 minutes to prepare a reaction mixture. Add the sodium hypochlorite powder of reaction mixture liquid quality 2% in the beaker, stir 30min with ...

Embodiment 2

[0046] Preparation of mixed slurry:

[0047] Put bagasse and wheat straw into an oven at a mass ratio of 5:1, dry for 3.5 hours at a temperature of 65°C, and put them into a pulverizer after drying to obtain a mixed material. Mix the mixed material with 8% hydrochloric acid Put it into a beaker at a mass ratio of 1:10, stir with a stirrer at a speed of 450r / min for 70min, place the beaker in a microwave oven after stirring, and microwave for 11min at a power of 700W to prepare a mixed slurry;

[0048] Preparation of oxidation reaction solution:

[0049] Place the above beaker in an ice-water bath, add dropwise sodium hydroxide solution with a mass fraction of 12.5% ​​to the beaker to adjust the pH value to 12, raise the temperature of the water bath to 90°C, and react at a constant temperature for 45 minutes to prepare a reaction mixture. Add the sodium hypochlorite powder of reaction mixture quality 3% in the beaker, stir 35min with the rotating speed of 550r / min with agitat...

Embodiment 3

[0058] Preparation of mixed slurry:

[0059] Put bagasse and wheat straw into an oven at a mass ratio of 5:1, dry for 4 hours at a temperature of 70°C, and put them into a pulverizer after drying to obtain a mixed material. Mix the mixed material with 10% hydrochloric acid by mass Put it into a beaker with a ratio of 1:10, stir with a stirrer at a speed of 500r / min for 80min, place the beaker in a microwave oven after stirring, and microwave for 12min under the condition of a power of 800W to prepare a mixed slurry;

[0060] Preparation of oxidation reaction solution:

[0061] Place the above-mentioned beaker in an ice-water bath, add dropwise sodium hydroxide solution with a mass fraction of 15% to the beaker to adjust the pH value to 13, raise the temperature of the water bath to 100°C, and react at a constant temperature for 50 minutes to prepare a reaction mixture. Add the sodium hypochlorite powder of reaction mixture quality 4% in the beaker, stir 40min with the rotatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of building material preparation, and particularly relates to a preparation method of high-strength flame-retardant waterproof glass wool. The method comprises the following steps: mixing and crushing bagasse and wheat straw; mixing and grinding a solid product, cullet, calcite and other raw materials; performing high-temperature treatment to obtain molten glass; and putting the molten glass in a glass wool centrifuge for processing and drying to obtain the high-strength flame-retardant waterproof glass wool. According to the preparation method, thebagasse and the wheat straw are subjected to hydrochloric acid soaking and alkali liquor high-temperature treatment, fiber molecules are subjected to oxidation treatment through sodium hypochlorite,the bonding effect among all components in the glass wool is improved, the impact resistance of the glass wool is improved, and the durability is enhanced; aluminum ions are introduced into plant fibers, the mechanical strength of the glass wool is improved, meanwhile, elemental aluminum is dispersed in the glass wool by using the fiber component, the flame retardant performance of the glass woolis enhanced under the condition of high temperature, and the fiber component and carbohydrate compounds are carbonized to improve the waterproof performance and mechanical strength, and wide application prospects are achieved.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to a preparation method of high-strength flame-retardant and waterproof glass wool. Background technique [0002] CN201410853918.0 discloses a glass wool ceiling, which includes a glass wool board layer, a glass fiber felt layer, a gypsum coating layer, and the glass wool board layer is made of centrifugal glass wool fibers with an environmentally friendly resin binder. The mass ratio of the environmentally friendly resin binder and gypsum paint is: 85-93:7-15:2-3; the preparation method is to spray the environmentally friendly resin binder evenly on the surface of the centrifugal glass wool fiber in an atomized state, Then the cotton is collected by the cotton collector, compressed and transported into the curing furnace for curing to obtain a glass wool board, which is then veneered with glass fiber felt, and then sprayed with compressed gypsum pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C13/00C03C14/00C03C1/00C03B37/04C04B30/02C04B111/27C04B111/28
CPCC03B37/04C03C1/002C03C13/00C03C14/00C04B30/02C04B2111/27C04B2111/28C04B14/42
Inventor 刘鹏
Owner 常州武城服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap