Method for preparing ITO (Indium Tin Oxide) granulation powder by mixing method
A technology of granulating powder and mixing method, which is applied in the field of preparation of ITO granulating powder, can solve the problems of dispersant failure, complicated operation, difficult to transfer clean, etc., and achieve the goal of reducing grinding time, avoiding particle agglomeration, and shortening grinding time Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Example 1: Take 90Kg of indium oxide powder and 10Kg of tin oxide powder, the average crystal grain size of indium oxide powder is 120nm, the average crystal grain size of tin oxide powder is 70nm, spare; take 0.5Kg of polycarboxylic acid compound Dispersant and 1.5Kg of polyvinyl alcohol are dissolved in deionized water to form a 40Kg mixed solution, add the weighed powder to this mixed solution, and mix into a pre-dispersed slurry with a solid content of 71.4% under stirring; The slurry was put into an ultrasonic instrument with an ultrasonic frequency of 40 Hz for 30 minutes, and then added to a sand mill for grinding for 1 hour. Correspondingly, when the particle size D50 of the slurry is 0.5 micron and D90 is 1 micron, a few drops of n-butanol are added for processing. After defoaming, a mixed slurry is prepared, and spray drying is performed to prepare ITO granulated powder, wherein the inlet air temperature is 220°C, the outlet air temperature is 100°C, and the ato...
Example Embodiment
[0038] Example 2: Take 90Kg of indium oxide powder and 10Kg of tin oxide powder, the average crystal grain size of indium oxide powder is 100nm, the average crystal grain size of tin oxide powder is 100nm, spare; take 0.7Kg polyvinylpyrrolidone dispersant Dissolve 1.5Kg of carboxymethyl cellulose in deionized water to form a 40Kg mixed solution, add the weighed powder to this mixed solution, and mix to form a pre-dispersed slurry with a solid content of 71.4%; The slurry was put into an ultrasonic instrument with an ultrasonic frequency of 40 Hz for 30 minutes, and then added to a sand mill for grinding for 1 hour. Correspondingly, when the particle size D50 of the slurry is 0.4 micron and D90 is 0.9 micron, a few drops of n-butanol are added. After defoaming, a mixed slurry is prepared, and spray drying is performed to prepare ITO granulated powder, wherein the inlet air temperature is 180°C, the outlet air temperature is 80°C, and the atomizer frequency is 35 Hz.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap