Method for preparing magnetic zsm-5 zeolite with clay and red mud as raw materials and microsolvent

A technology of ZSM-5 and clay, which is applied in the field of zeolite preparation, can solve problems such as difficult to meet actual needs and weak magnetic properties, and achieve the effects of avoiding the use of water and iron salts, strong magnetic properties, and reducing production costs

Active Publication Date: 2021-06-22
HUAIYIN INSTITUTE OF TECHNOLOGY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Red mud is a kind of iron-containing aluminum plant waste, as well as silicon and aluminum components, so when adding fly ash, silica sol, steel slag (Microporous and Mesoporous Materials, 2015, 202, 208~216; FuelProcessing Technology, 2019, 189, 39~48; Microporous and Mesoporous Materials, 2018, 270, 24~29) After adjusting the silicon-aluminum ratio, the conventional hydrothermal method can also be used to prepare magnetic zeolite, but the magnetic properties of this zeolite are due to its The main components of iron oxides are hematite and goethite, resulting in weak magnetic properties and difficult to meet actual needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing magnetic zsm-5 zeolite with clay and red mud as raw materials and microsolvent
  • Method for preparing magnetic zsm-5 zeolite with clay and red mud as raw materials and microsolvent
  • Method for preparing magnetic zsm-5 zeolite with clay and red mud as raw materials and microsolvent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0025] Disperse 20g of attapulgite in 80 ml of 3mol / L HCl solution, soak at 80°C for 48 h, filter, wash and dry to obtain acidified attapulgite; weigh 1.6g of acidified attapulgite, 0.16g of red mud, 0.4 g ammonium chloride, 0.2g tetrapropylammonium bromide were mixed and ground for 30min to obtain a powder, then 0.5g NaOH and 0.6g H were added to the powder 2 O prepared NaOH solution, stirred evenly to form a paste mixture, sealed and left to stand for 24 hours, then transferred to a sealed reaction kettle, crystallized at 180°C for 4 hours to obtain ZSM-5 zeolite crystals, cooled ZSM-5 zeolite crystals, added water to wash, and suction filtered , After drying, calcined at 550°C for 3 hours to obtain ZSM-5 zeolite, whose crystal form and morphology are as follows figure 1 and figure 2 Shown are ZSM-5 zeolite crystals.

Embodiment approach 2

[0027] Disperse 20g of attapulgite in 80 ml of 3mol / L HCl solution, soak at 80°C for 48 h, filter, wash and dry to obtain acidified attapulgite; weigh 1.6g of acidified attapulgite, 0.28g of red mud, 0.4 G sodium chloride, 0.3g tetrapropylammonium bromide were mixed and ground for 30min to obtain a powder, then 0.6g NaOH and 0.8g H were added to the powder 2 O prepared NaOH solution, stirred evenly to form a paste mixture, sealed and allowed to stand for 24 hours, then transferred to a sealed reaction kettle, crystallized at 180°C for 12 hours to obtain ZSM-5 zeolite crystals, cooled ZSM-5 zeolite crystals, washed with water, and suction filtered , After drying, calcined at 550°C for 3 hours to obtain ZSM-5 zeolite.

Embodiment approach 3

[0029] Disperse 20g of attapulgite in 80 ml of 3mol / L HCl solution, soak at 80°C for 48 h, filter, wash and dry to obtain acidified attapulgite; weigh 1.6g of acidified attapulgite, 0.4g of red mud, 0.4 g ammonium chloride, 0.4g tetrapropylammonium bromide were mixed and ground for 30min to obtain a powder, then 0.6g NaOH and 1g H were added to the powder 2 O prepared NaOH solution, stirred evenly to form a paste mixture, sealed and left to stand for 24 hours, then transferred to a sealed reaction kettle, crystallized at 180°C for 24 hours to obtain ZSM-5 zeolite crystals, cooled ZSM-5 zeolite crystals, washed with water, and suction filtered , After drying, calcined at 550°C for 3 hours to obtain ZSM-5 zeolite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of zeolite preparation, and discloses a method for preparing magnetic ZSM‑5 zeolite by using clay and red mud as raw materials and microsolvents, and mixing and grinding acidified clay, red mud, chloride and tetrapropylammonium bromide into powder , and then add NaOH solution to the powder and stir to form a paste mixture; seal the paste mixture and transfer it to a sealed reaction kettle for crystallization to obtain ZSM‑5 zeolite crystals; ZSM‑5 zeolite crystals are washed with water, dried, Calcination to remove the template agent; raise the temperature to 600~700°C, pass nitrogen gas for 1 hour at the same time, then pass hydrogen gas for 1~2 hours, after reducing red mud iron-containing oxides, strong magnetic ZSM-5 zeolite is obtained. The present invention uses natural clay and solid waste red mud as raw materials, chlorides as mineralizers, sodium hydroxide as alkalinity regulator, and utilizes a microsolvent method to prepare strong magnetic ZSM-5 zeolite, avoiding a large amount of solvents and iron salts The use reduces the subsequent treatment process, which is economical and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of zeolite preparation, in particular to a method for preparing magnetic ZSM-5 zeolite by using clay and red mud as raw materials and microsolvents. Background technique [0002] ZSM-5 zeolite is an inorganic crystalline material with regular pores, which has excellent adsorption and catalytic performance, and has a wide range of applications in the field of adsorption and catalysis. ZSM-5 zeolite is usually synthesized from sodium silicate, tetraethyl orthosilicate, sodium aluminate and other materials, and is synthesized under hydrothermal conditions by using a template agent. The ZSM-5 zeolite synthesized by this method has high crystallinity and excellent performance, but the raw material is expensive, and the waste water needs to be treated after the product is separated. [0003] In order to reduce costs and reduce the use of solvents, some minerals containing silicon and aluminum such as illite (Micr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/40C01G49/08
CPCC01B39/40C01G49/08C01P2002/72C01P2004/03C01P2004/80C01P2006/42
Inventor 蒋文彬邹韵琴张永红韦星王佳佳周凯王璐瑶蒋金龙吴妹谷亚昕
Owner HUAIYIN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap