A seaweed and masterbatch technology, applied in the field of fiber manufacturing, can solve the problems of low hydrophilic performance of seaweed polyester masterbatch, immature polyester masterbatch manufacturing process, easy loss of activity of seaweed, etc., so as to achieve strong seaweed activity, promote human health, The effect of strong negative ions and far-infrared effects

Active Publication Date: 2020-05-19
BESTEE MATERIAL (TSINGTAO) CO LTD
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Today, with the advancement of science and technology, seaweed is used in the textile field, but the manufacturing process of seaweed for polyester masterbatch is not yet mature; resulting in many defects in polyester masterbatch containing seaweed, which seriously affects the quality of clothing
[0005] The ex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1 A kind of seaweed polyester masterbatch and preparation method thereof

[0036] 1. Preparation of seaweed modifier

[0037] Mix seaweed extract, negative ion powder, calcium stearate, lauryl dimethyl benzyl ammonium chloride and ethanol-water solution in a mass ratio of 2:2:3:1:20, ethanol-water solution The volume ratio of ethanol in the mixture is 7%, and the mixture is stirred at a speed of 2500rpm for 5.5h to obtain a seaweed modifier.

[0038] Said seaweed extract: fucoidan, the active substance content is 98%, the fineness is 80 mesh, and the content of thioesterified L-trehalose is 80-85%;

[0039] The negative ion powder: the fineness is 8000-8500 mesh, and the negative ion is 20000-30000 / CM 3 Between, while the far infrared emission rate is 90-92%.

[0040] 2. Preparation of loading agent

[0041] Mix coconut shell granular activated carbon, dolomite powder, and silica-modified starch in a mass ratio of 2:1:5, and place the obtained mixture in ...

Embodiment 2

[0053]Embodiment 2 A kind of seaweed polyester masterbatch and preparation method thereof

[0054] 1. Preparation of seaweed modifier

[0055] Mix seaweed extract, negative ion powder, calcium stearate, lauryl dimethyl benzyl ammonium chloride and ethanol-water solution in a mass ratio of 2:2:3:1.5:18, ethanol-water solution The volume ratio of ethanol in the mixture is 7%, and the mixture is stirred at a speed of 2500rpm for 5h to obtain a seaweed modifier.

[0056] Said seaweed extract: fucoidan, the active substance content is 98%, the fineness is 80 mesh, and the content of thioesterified L-trehalose is 80-85%;

[0057] The negative ion powder: the fineness is 8000-8500 mesh, and the negative ion is 20000-30000 / CM 3 Between, while the far infrared emission rate is 90-92%.

[0058] 2. Preparation of loading agent

[0059] Coconut shell granular activated carbon, dolomite powder, and silicon dioxide modified starch are mixed according to the mass ratio of 2:1:5, and the ...

Embodiment 3

[0071] Embodiment 3 A kind of seaweed polyester masterbatch and preparation method thereof

[0072] 1. Preparation of seaweed modifier

[0073] Seaweed extract, negative ion powder, calcium stearate, lauryl dimethyl benzyl ammonium chloride and ethanol-water solution are mixed according to the mass ratio of 3:1.5:3.5:1.5:20, ethanol-water solution The volume ratio of ethanol in the mixture is 7%, and the mixture is stirred at a speed of 2500rpm for 6h to obtain the seaweed modifier.

[0074] Said seaweed extract: fucoidan, the active substance content is 98%, the fineness is 80 mesh, and the content of thioesterified L-trehalose is 80-85%;

[0075] The negative ion powder: the fineness is 8000-8500 mesh, and the negative ion is 20000-30000 / CM 3 Between, while the far infrared emission rate is 90-92%.

[0076] 2. Preparation of loading agent

[0077] Coconut shell granular activated carbon, dolomite powder, and silicon dioxide modified starch are mixed according to the mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of seaweed polyester master batch. According to the seaweed polyester master batch, the content of seaweed extract is 0.1-5%. The preparation method comprises a step of preparing a seaweed modifier. In the step of preparing the seaweed modifier, the seaweed extract, negative ion powder, calcium stearate, dodecyl dimethyl benzyl ammonium chloride and an ethanol-water solution are mixed, and stirred at a speed of 2000-2500rpm for 5-6h to obtain the seaweed modifier, wherein the volume ratio of ethanol in the ethanol-water solution is 6-8%. The preparation method further comprises the steps of preparing a loading agent, preparing master batch modified powder and preparing the seaweed polyester master batch. The dispersion degree and the uniformity degree of seaweed active ingredients in the prepared seaweed polyester master batch are remarkably improved, and no obvious agglomeration phenomenon occurs. A good inhibition effect is achieved. The seaweed polyester master batch has relatively strong negative ion and far-infrared effects.

Description

technical field [0001] The invention belongs to the technical field of fiber manufacturing, and in particular relates to a seaweed polyester masterbatch and a preparation process thereof. Background technique [0002] Polyester is a synthetic fiber obtained by spinning polyester obtained by polycondensation of organic dibasic acid and dibasic alcohol, referred to as PET fiber, which belongs to polymer compounds. Invented in 1941, it is currently the largest variety of synthetic fibers. The biggest advantage of polyester fiber is that it has good wrinkle resistance and shape retention, and has high strength and elastic recovery ability. It is strong and durable, anti-wrinkle and non-ironing, and non-sticky. However, it has poor hydrophilicity and air permeability, and people feel poor when wearing it. [0003] With the continuous improvement of people's living standards, people have higher and higher requirements for clothing fabrics, not only requiring the improvement of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L5/04C08L3/02C08L33/02C08K7/24C08K3/26C08K3/36C08K5/098C08K13/04C08J3/22D01F1/10D01F6/92
CPCC08J3/226C08J2405/04C08J2467/02C08K3/26C08K3/36C08K5/098C08K7/24C08K13/04D01F1/103D01F6/92
Inventor 黄效华刘洁刘宇甄丽黄效谦
Owner BESTEE MATERIAL (TSINGTAO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap