Skin care film and preparation method thereof

A technology for skin care and polylysine, which is applied to skin care preparations, skin diseases, pharmaceutical formulations, etc., can solve the problems of affecting wound healing and comfort, affecting air permeability, poor nursing effect, etc., and achieving low preparation costs. , The effect of short time consumption and good air permeability

Inactive Publication Date: 2020-05-26
李虹
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these active ingredients are all coated on non-woven fabrics or other textile media. Due to poor adhesion, poor strength and poor nursing effect, the coating affects air permeability, wound healing and comfort.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Skin care film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A skin care film, characterized in that it is made of the following parts by weight of raw materials: 10 parts of vinyl-modified hyperbranched polylysine, 0.1 part of strontium acetylacetonate hydrate, 2 parts of isopulegol, glycidyl ether 3 parts of group-terminated allyl alcohol random polyether, 5 parts of ionized imidazole base polycarbonate-based polyester polycondensate, 1 part of hyaluronic acid, 0.02 parts of azobisisobutyronitrile.

[0029] The preparation method of the ionized imidazole salt-based polycarbonate-based polyester polycondensate includes the following steps:

[0030] Step S1: Add polycarbonate diol, imidazole-4,5-dicarboxylic acid, tetrabutyl titanate, and dimethyl sulfoxide into the autoclave, replace the air in the autoclave with nitrogen, and then set it at a temperature of 240°C, The esterification reaction is carried out under the condition of an absolute pressure of 50KPaa. When the amount of water output reaches the theoretical amount, the ester...

Embodiment 2

[0035] A skin care film, characterized in that it is made of the following parts by weight of raw materials: 13 parts of vinyl-modified hyperbranched polylysine, 0.15 parts of strontium acetylacetonate hydrate, 2.5 parts of isopulegol, and glycidyl ether 3.5 parts of group-terminated allyl alcohol random polyether, 6 parts of ionized imidazole base polycarbonate-based polyester polycondensate, 1.5 parts of hyaluronic acid, and 0.03 parts of azobisisoheptonitrile.

[0036] The preparation method of the ionized imidazole salt-based polycarbonate-based polyester polycondensate includes the following steps:

[0037] Step S1: Add polycarbonate diol, imidazole-4,5-dicarboxylic acid, titanium dioxide, and N,N-dimethylformamide into the autoclave, replace the air in the autoclave with helium, and then set it at a temperature of 250 The esterification reaction is carried out under the conditions of ℃ and 65KPa absolute pressure. When the water output reaches the theoretical amount, the este...

Embodiment 3

[0042] A skin care film, characterized in that it is made of the following parts by weight of raw materials: 15 parts of vinyl-modified hyperbranched polylysine, 0.2 parts of strontium acetylacetonate hydrate, 3 parts of isopulegol, and glycidyl ether 4 parts of group-terminated allyl alcohol random polyether, 7.5 parts of ionized imidazole base polycarbonate-based polyester polycondensate, 2 parts of hyaluronic acid, and 0.035 parts of benzoyl peroxide.

[0043] The preparation method of the ionized imidazole salt-based polycarbonate-based polyester polycondensate includes the following steps:

[0044] Step S1: Add polycarbonate diol, imidazole-4,5-dicarboxylic acid, titanium chloride, and N,N-dimethylacetamide into the autoclave, replace the air in the autoclave with neon gas, and then The esterification reaction is carried out at a temperature of 255°C and an absolute pressure of 80KPa. When the amount of water output reaches the theoretical amount, the esterification is termina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a skin care film. The film is prepared from the following raw materials in parts by weight: 10 to 20 parts of vinyl modified hyperbranched polylysine, 0.1 to 0.3 part of strontium acetylacetonate hydrate, 2 to 4 parts of isopulegol, 3 to 5 parts of glycidyl ether-terminated allyl alcohol random polyether, 5 to 10 parts of ionized imidazolium salt-based polycarbonate-based polyester polycondensate, 1 to 3 parts of hyaluronic acid and 0.02 to 0.05 part of an initiator. The invention further discloses a preparation method of the skin care film. The skin care film disclosedby the invention is good in biocompatibility, sufficient in strength, good in air permeability and remarkable in skin care effect, can effectively prevent wound infection, accelerate wound healing, promote skin growth and reduce scars, and further has multiple functions of whitening, resisting skin aging and the like.

Description

Technical field [0001] The invention relates to the technical field of preparation of care materials, in particular to a skin care film and a preparation method thereof. Background technique [0002] In recent years, with increasing pressure from life and work, aging and increasing environmental problems, more and more people, especially modern women who love beauty, have been trapped by skin aging, wrinkles and sagging The appearance, loss of elasticity and gloss. In order to change this situation, they pin their hopes on beauty skin care products, hoping that beauty skin care products can restore their youth and health, and make their skin more shiny, elastic and free of stains. As one of the many types of beauty and skin care products, skin care membranes have attracted widespread attention due to their hydrating, calming, whitening and wound healing effects. [0003] In daily life, in addition to normal aging of the skin, it is often accompanied by skin damage, such as burns ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/88A61K8/85A61K8/73A61K8/58A61K8/39A61K8/34A61Q19/00A61Q19/02A61Q19/08A61P17/02A61P31/00
CPCA61K8/34A61K8/39A61K8/58A61K8/735A61K8/85A61K8/88A61P17/02A61P31/00A61Q19/00A61Q19/02A61Q19/08
Inventor 李虹曹玲
Owner 李虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com