Organic/inorganic composite gel plugging agent with rigid interior and flexible exterior, and preparation method thereof
A technology of inorganic compounding and leak-stopping agent, applied in dyeing organosilicon compound treatment, chemical instruments and methods, drilling composition, etc., can solve the problems of poor dispersibility and compatibility, insufficient temperature resistance, etc. The effect of strong resistance, high temperature resistance, and reduction of unnecessary losses
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0046] The preparation of organic / inorganic composite rigid material includes steps:
[0047] (1) Dissolve 4g of γ-methacryloxypropyltrimethoxysilane (KH570) in 100 mL of ethanol-water mixed solvent to obtain solution A; the volume ratio of ethanol to water in the mixed solvent is 4:1, The pH of the mixed solvent was adjusted to 4 with acetic acid; 20 g of nano calcium carbonate was dispersed in 100 mL of ethanol to obtain dispersion B, and the average particle size of the nano calcium carbonate was 50 nm.
[0048] (2) Add dispersion B to solution A dropwise, pour it into a three-necked flask, pour nitrogen into it, heat to 70°C, stir and react for 5h at a stirring speed of 300r / min; then filter the reaction system with suction and remove the resulting product. Washed with water and ethanol for 3 times, then dried at 50° C. for 24 h, and the dried product was ground for 3 min at 30,000 r / min to obtain modified nano calcium carbonate.
[0049] (3) Disperse 6g styrene, 6g butyl methac...
Embodiment 2
[0051] An organic / inorganic composite internal rigid and external flexible gel plugging agent is prepared by including the following mass parts of raw materials: 30 parts of copolymerization monomer, 0.3 part of crosslinking agent, 4 parts of surfactant, and 0.2 part of initiator.
[0052] The copolymerization monomer is the organic / inorganic composite rigid material prepared in Example 1, acrylamide, 2-acrylamido-2-methylpropanesulfonic acid, acrylic acid, and the mass ratio is 2:6:2:3; The initiator is potassium persulfate; the crosslinking agent is N,N-methylenebisacrylamide (BIS); the surfactant is sodium lauryl sulfate.
[0053] The preparation method of the above organic / inorganic composite internal rigid external flexible gel plugging agent includes the steps:
[0054] Disperse the comonomer, crosslinking agent, and surfactant in deionized water in sequence, and the mass ratio of comonomer and deionized water is 3:7; adjust the system with a sodium hydroxide aqueous solution w...
Embodiment 3
[0056] An organic / inorganic composite internal rigid external flexible gel plugging agent is prepared by including the following mass parts of raw materials: 30 parts of copolymerization monomer; 0.3 parts of crosslinking agent; 4 parts of surfactants; and 0.2 parts of initiators.
[0057] The copolymerization monomer is the organic / inorganic composite rigid material prepared in Example 1, acrylamide, 2-acrylamido-2-methylpropanesulfonic acid, acrylic acid, and the mass ratio is 3:6:2:3; The initiator is potassium persulfate; the crosslinking agent is N,N-methylenebisacrylamide (BIS); the surfactant is sodium lauryl sulfate.
[0058] The preparation method of the above organic / inorganic composite internal rigid external flexible gel plugging agent includes the steps:
[0059] Disperse the comonomer, crosslinking agent, and surfactant in deionized water in sequence, and the mass ratio of comonomer and deionized water is 3:7; adjust the system with a sodium hydroxide aqueous solution w...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap