A preparation method and application of oral microspheres loaded with mscs-derived exosomes

A technology of exosomes and sources, applied in the direction of medical preparations with non-active ingredients, medical preparations containing active ingredients, microcapsules, etc., can solve the problem of unstable therapeutic effect, large infusion dose, and the efficiency of autoimmune diseases. Low-level problems, to achieve the effect of ensuring long-term survival, convenient operation, and stable release

Active Publication Date: 2021-08-13
NANJING DRUM TOWER HOSPITAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the shortcomings of MSCs exosomes in the treatment of autoimmune diseases, such as low efficiency, large infusion dose, and unstable therapeutic effect, the present invention provides a preparation of oral microspheres loaded with MSCs-derived exosomes and its application in the treatment of RA. Applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of oral microspheres loaded with mscs-derived exosomes
  • A preparation method and application of oral microspheres loaded with mscs-derived exosomes
  • A preparation method and application of oral microspheres loaded with mscs-derived exosomes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] An oral microsphere loaded with MSCs-derived exosomes, the preparation method of which comprises the following steps:

[0038] (1) Preparation of ALG / CST outer core solution:

[0039] Weigh sodium alginate ALG and chitosan CST respectively, add each into double-distilled water to disperse, prepare sodium alginate solution and chitosan solution, and fully dissolve them respectively; after cooling to room temperature, mix the two according to a certain ratio, and stir thoroughly Until uniform; the concentration of ALG / CST outer core solution is 1% ALG / 1% CST.

[0040] (2) Preparation of ALG / CNC core solution:

[0041] Weigh sodium alginate ALG and sodium hydroxymethylcellulose CNC-Na respectively, add each into double-distilled water to disperse, and dissolve fully respectively to prepare sodium alginate solution and sodium hydroxymethylcellulose solution; after cooling to room temperature, the two or mixed according to a certain ratio, fully stirred until uniform; the co...

Embodiment 2

[0048] An oral microsphere loaded with exosomes derived from MSCs, the preparation method of which comprises the following steps:

[0049] (1) Preparation of ALG / CST outer core solution:

[0050] Weigh sodium alginate ALG and chitosan CST respectively, add each into double-distilled water to disperse, prepare sodium alginate solution and chitosan solution, and fully dissolve them respectively; after cooling to room temperature, mix the two according to a certain ratio, and stir thoroughly until uniform; the concentration of the ALG / CST outer core solution is 1% ALG / 1% CST.

[0051] (2) Preparation of ALG / CNC core solution:

[0052] Weigh sodium alginate ALG and sodium hydroxymethylcellulose CNC-Na respectively, add each into double-distilled water to disperse, and dissolve fully respectively to prepare sodium alginate solution and sodium hydroxymethylcellulose solution; after cooling to room temperature, the two or mixed according to a certain ratio, fully stirred until unif...

Embodiment 3

[0059] An oral microsphere loaded with exosomes derived from MSCs, the preparation method of which comprises the following steps:

[0060] (1) Preparation of ALG / CST outer core solution:

[0061] Weigh sodium alginate ALG and chitosan CST respectively, add each into double-distilled water to disperse, prepare sodium alginate solution and chitosan solution, and fully dissolve them respectively; after cooling to room temperature, mix the two according to a certain ratio, and stir thoroughly until uniform; the concentration of the ALG / CST outer core solution is 1% ALG / 1% CST.

[0062] (2) Preparation of ALG / CNC core solution:

[0063] Weigh sodium alginate ALG and sodium hydroxymethylcellulose CNC-Na respectively, add each into double-distilled water to disperse, and dissolve fully respectively to prepare sodium alginate solution and sodium hydroxymethylcellulose solution; after cooling to room temperature, the two or mixed according to a certain ratio, fully stirred until unif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and application of oral microspheres loaded with MSCs-derived exosomes. The preparation method includes the following steps: (1) preparation of ALG / CST outer core solution, (2) preparation of ALG / CNC inner core solution, (3) separation of mesenchymal stem cell-derived exosomes, (4) preparation of loaded MSCs Exosome microspheres. The present invention combines the hydrophobic ALG / CST with the hydrophilic ALG / CNC, wraps the exosome core with ALG / CST, overcomes the shortcomings of ALG easy acid hydrolysis, low CNC drug loading, etc., and effectively protects the exosome immune system. Destroyed by gastric acid and digestive juice, and has pH-sensitive small intestine slow-release targeting, MSCs can be safely transported to the small intestine by oral means, and can be used for damage repair, immune regulation and anti-inflammatory through the absorption function of the small intestine. Inflammation, to achieve the treatment of RA and other related autoimmune diseases.

Description

technical field [0001] The invention relates to the field of biological materials, in particular to a preparation method and application of oral microspheres loaded with exosomes derived from MSCs. Background technique [0002] More and more studies have confirmed that exosomes derived from mesenchymal stem cells can promote angiogenesis, reduce inflammation, and repair damaged tissues by transmitting signaling molecules between cells. Compared with MSCs, exosomes have the advantages of better stability, high survival rate after transplantation therapy, and no obvious adverse reactions. In addition, exosomes contain a large number and variety of protein cytokines and bioactive molecules, which are the main way for MSCs to exert anti-inflammatory, anti-fibrosis and immune regulation functions. Therefore, MSCs exosomes have certain clinical application prospects in the prevention and treatment of immune system diseases such as systemic lupus erythematosus and its complication...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K35/28A61K9/50A61K47/36A61K47/38A61P19/02A61P37/02
CPCA61K9/0053A61K9/5036A61K9/5078A61K35/28A61P19/02A61P37/02
Inventor 孙凌云甘璟璟赵远锦
Owner NANJING DRUM TOWER HOSPITAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com