Unlock instant, AI-driven research and patent intelligence for your innovation.

A kind of preparation method of low-voltage positively charged nanofiltration membrane and its products and applications

A positively charged, nanofiltration membrane technology, applied in the field of low-pressure positively charged nanofiltration membrane preparation, can solve the problems of insignificant positive charging effect, inability to retain divalent salts, etc., to improve hydrophilicity and increase stability , high-throughput effect

Active Publication Date: 2022-04-12
GUIZHOU MATERIAL IND TECH INSTITUE
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, from the reported separation results, the nanofiltration membrane prepared by introducing amine groups can only intercept colored soluble organic matter but not divalent salts, that is, it can only be used to intercept colored soluble organic matter and is called loose nanofiltration membrane. And its effect of positive charge is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1: A kind of preparation method of low pressure positively charged nanofiltration membrane:

[0041] S1: In terms of parts by mass, take 17 parts of chlorinated polyvinyl chloride, 3.4 parts of polystyrene / N-phenylmaleimide / epoxy functional group copolymer, and 7 parts of polyethylene glycol (800g / mol) and 72.6 parts of dimethyl sulfoxide, stirred and dissolved in a dissolution tank at 70°C, mixed, and defoamed to obtain a polymer solution; The surface of the ester nonwoven fabric is scraped at a speed of 0.2m / s to form a flat film. The thickness of the flat film is 300μm. After air cooling, it is solidified in room temperature water and then soaked in an ethanol / water mixture with a mass ratio of 1:1 at room temperature. Wash twice, 1 hour each time, fully wash to remove the solvent and porogen, take it out and dry it to obtain a blended polymer ultrafiltration membrane with a thickness of 200 μm and a pore size of 6 nm;

[0042] S2, the polyvinylamine (mol...

Embodiment 2

[0046] Embodiment 2: A kind of preparation method of low pressure positively charged nanofiltration membrane:

[0047] S1: In terms of parts by mass, take 17 parts of chlorinated polyvinyl chloride, 3.4 parts of polystyrene / N-phenylmaleimide / epoxy functional group copolymer, and 7 parts of polyethylene glycol (800g / mol) and 72.6 parts of dimethyl sulfoxide, stirred and dissolved in a dissolution tank at 70°C, mixed, and defoamed to obtain a polymer solution; The surface of the ester nonwoven fabric is scraped at a speed of 0.2m / s to form a flat film. The thickness of the flat film is 300μm. After air cooling, it is solidified in room temperature water and then soaked in an ethanol / water mixture with a mass ratio of 1:1 at room temperature. Wash twice, 1 hour each time, fully wash to remove the solvent and porogen, take it out and dry it to obtain a blended polymer ultrafiltration membrane with a thickness of 200 μm and a pore size of 6 nm;

[0048] S2, the polyvinylamine (mol...

Embodiment 3

[0052] Embodiment 3: A kind of preparation method of low pressure positively charged nanofiltration membrane:

[0053] S1: In terms of parts by mass, take 17 parts of chlorinated polyvinyl chloride, 3.4 parts of polystyrene / N-phenylmaleimide / epoxy functional group copolymer, and 7 parts of polyethylene glycol (800g / mol) and 72.6 parts of dimethyl sulfoxide, stirred and dissolved in a dissolution tank at 70°C, mixed, and defoamed to obtain a polymer solution; The surface of the ester nonwoven fabric is scraped at a speed of 0.2m / s to form a flat film. The thickness of the flat film is 300μm. After air cooling, it is solidified in room temperature water and then soaked in an ethanol / water mixture with a mass ratio of 1:1 at room temperature. Wash twice, 1 hour each time, fully wash to remove the solvent and porogen, take it out and dry it to obtain a blended polymer ultrafiltration membrane with a thickness of 200 μm and a pore size of 6 nm;

[0054] S2, the polyvinylamine (mol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a low-pressure positively charged nanofiltration membrane, comprising steps: S1, mixing a polymer, a copolymer and a porogen with a solvent to form a solution, coating it on the surface of a nonwoven fabric, washing to remove the solvent and Porogenic agent to obtain a blended polymer ultrafiltration membrane; S2, the surface of the obtained blended polymer ultrafiltration membrane is coated with a polyamine solution for chemical crosslinking reaction to form a loose nanofiltration separation layer; S3, the surface of the obtained loose nanofiltration separation layer Coating the small molecule organic matter solution for chemical cross-linking reaction to form a nanofiltration separation layer; S4, coating the surface of the obtained nanofiltration separation layer with a metal ion solution for chelation reaction, and heat treatment after controlled drying to obtain that product; also discloses its product and application. The low-voltage positively charged nanofiltration membrane of the present invention is resistant to oxidation, thin in thickness, does not fall off during use, and can realize efficient separation of heavy metal ions. The membrane has good hydrophilicity, pollution resistance and permeation flux; the preparation method is simple in process and easy to use. Large-scale production has good industrial application prospects.

Description

technical field [0001] The invention relates to the technical field of nanofiltration membrane separation, in particular to a method for preparing a low-pressure positively charged nanofiltration membrane, its products and applications. Background technique [0002] Nanofiltration membrane is a pressure-driven membrane between reverse osmosis membrane and ultrafiltration membrane. The pore size is usually about 1nm. Because of the synergy of steric hindrance and Donnan effect, this type of membrane has a unique separation Performance, this type of membrane can efficiently intercept divalent and multivalent salts and organic compounds with a molecular weight of 200-1000 g / mol under lower pressure conditions (compared to reverse osmosis membranes), while the rejection rate of monovalent ions is very low . It has been widely used in the separation and purification of medicine and biological products, separation of dyes, food industry, removal of multivalent ions (such as remov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D67/00B01D69/02B01D69/10B01D61/00
CPCB01D67/0079B01D67/0093B01D69/02B01D69/10B01D61/027B01D2325/36B01D2325/16
Inventor 杨园园秦舒浩陈贵靖崔振宇杨敬葵
Owner GUIZHOU MATERIAL IND TECH INSTITUE