Blended yarn of graphene fiber enhanced hemp-cotton multifunctional fibers
A graphene fiber and blended yarn technology, applied in the direction of fiber type, fiber treatment, plant fiber, etc., can solve the problem of wear resistance, corrosion resistance, corrosion resistance, UV resistance and antibacterial properties, and can not meet the resistance of blended yarns. It can achieve the effect of excellent antibacterial performance, improved UV resistance, and good anti-mite performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] see figure 1 The present invention provides the following technical solutions: a graphene fiber reinforced hemp-cotton multi-functional fiber blended yarn, including a blended yarn, the blended yarn is made by blending hemp-cotton multi-functional fiber and graphene fiber.
[0030] Specifically, the spinning yarn includes the following preparation steps:
[0031] S1, place the hemp fiber in the pectinase solution to soak at room temperature, then continue to immerse the treated hemp fiber in the chitosan aqueous solution for soaking, dehydration, and drying;
[0032] S2, soak the hemp fiber and polyester, graphene nylon fiber, bamboo pulp fiber and cotton fiber obtained in step S1 in acetone, carry out ultrasonic vibration treatment at the same time, dehydrate and dry after washing, and obtain hemp-cotton multifunctional fiber ;
[0033] S3, performing solution treatment on the hemp-cotton multi-functional fiber prepared in step S2 by adding a flame retardant to obtai...
Embodiment 2
[0045] see figure 1 The present invention provides the following technical solutions: a graphene fiber reinforced hemp-cotton multi-functional fiber blended yarn, including a blended yarn, the blended yarn is made by blending hemp-cotton multi-functional fiber and graphene fiber.
[0046] Specifically, the spinning yarn includes the following preparation steps:
[0047] S1, place the hemp fiber in the pectinase solution to soak at room temperature, then continue to immerse the treated hemp fiber in the chitosan aqueous solution for soaking, dehydration, and drying;
[0048] S2, soak the hemp fiber and polyester, graphene nylon fiber, bamboo pulp fiber and cotton fiber obtained in step S1 in acetone, carry out ultrasonic vibration treatment at the same time, dehydrate and dry after washing, and obtain hemp-cotton multifunctional fiber ;
[0049] S3, performing solution treatment on the hemp-cotton multi-functional fiber prepared in step S2 by adding a flame retardant to obtai...
Embodiment 3
[0061] see figure 1 The present invention provides the following technical solutions: a graphene fiber reinforced hemp-cotton multi-functional fiber blended yarn, including a blended yarn, the blended yarn is made by blending hemp-cotton multi-functional fiber and graphene fiber.
[0062] Specifically, the spinning yarn includes the following preparation steps:
[0063] S1, place the hemp fiber in the pectinase solution to soak at room temperature, then continue to immerse the treated hemp fiber in the chitosan aqueous solution for soaking, dehydration, and drying;
[0064] S2, soak the hemp fiber and polyester, graphene nylon fiber, bamboo pulp fiber and cotton fiber obtained in step S1 in acetone, carry out ultrasonic vibration treatment at the same time, dehydrate and dry after washing, and obtain hemp-cotton multifunctional fiber ;
[0065] S3, performing solution treatment on the hemp-cotton multi-functional fiber prepared in step S2 by adding a flame retardant to obtai...