Environment-friendly treatment method and treatment agent for industrial wastewater
A technology for industrial wastewater and environmental protection treatment, applied in water/sewage treatment, adsorbed water/sewage treatment, water/sludge/sewage treatment, etc. To achieve the effect of selective adsorption, reducing the production of secondary pollutants, and reducing the cost of recovery
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0050] An environmental protection treatment agent for industrial wastewater is a pyridone amphoteric cross-linked polystyrene microsphere containing amino and carboxyl groups, prepared through the following steps:
[0051] S1. styrene and p-chloromethylstyrene with a molar ratio of 2.5:1 are used as polymerized monomers to prepare chloromethylated polystyrene, as follows:
[0052] Dissolve 2.70g of polyvinylpyrrolidone in 160g of ethanol, mix them well to form solution A, dissolve 0.30g of azobisisobutyronitrile in 30g of styrene, mix them well to form solution B; add solution A to a 500mL three-necked flask , under mechanical stirring, add solution B into the three-necked flask and mix evenly, blow nitrogen into the system for 15 minutes to discharge the oxygen in the system, and keep stirring and polymerizing the three-necked flask in an oil bath at 70°C;
[0053] After reacting for one hour, disperse 0.30g of azobisisobutyronitrile in 15mL of ethanol, and ultrasonically sh...
Embodiment 2-3
[0059] The environmental protection treatment agent of the industrial waste water prepared by embodiment 2-3, compared with embodiment 1, difference is that, in step S1, the mol ratio of styrene and p-chloromethyl styrene is respectively 1:1 and 4 : 1, the others are basically the same as in Embodiment 1, and will not be repeated here.
Embodiment 4-6
[0061] Embodiment 4-6 respectively provides a kind of environmental protection treatment method of industrial waste water, respectively adopts the environmental protection treatment agent of the industrial waste water prepared in embodiment 1-3, and treatment method is as follows:
[0062] (1) prepare the cationic dye and the anionic dye aqueous solution that concentration is 200mg / L respectively;
[0063] (2) 15 mg of pyridone amphoteric cross-linked polystyrene microspheres prepared in Examples 1 to 3 were added to 50 ml of the above-mentioned cationic dye and anionic dye aqueous solution, stirred at room temperature, and adsorption equilibrium was reached after 3-4 hours of adsorption, Filtration and separation to obtain pyridone amphoteric cross-linked polystyrene microspheres that adsorb dyes;
[0064] (3) Place the pyridone amphoteric cross-linked polystyrene microspheres that absorb the dye in a hydrochloric acid solution with a concentration of 0.2 mol / L, stir at room ...
PUM
Property | Measurement | Unit |
---|---|---|
adsorption capacity | aaaaa | aaaaa |
adsorption capacity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap