Alkali shrinkage technology of all-cotton jersey

A technology of cotton jersey and craftsmanship, which is applied in the direction of improved hand-feeling fibers, dry-cleaning fiber products, textiles and papermaking, etc., which can solve the problems of poor color fastness and uneven coloring of cotton jersey, so as to prevent pilling and wrinkling , Improve color fastness, improve the effect of stability

Inactive Publication Date: 2020-08-11
浙江健安达纺织科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art, the purpose of the present invention is to provide an alkali shrinkage process for cotton jersey, which avoids the problems of uneven coloring and poor color fastness of cotton jersey

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali shrinkage technology of all-cotton jersey
  • Alkali shrinkage technology of all-cotton jersey
  • Alkali shrinkage technology of all-cotton jersey

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The invention discloses an alkali shrinkage process of a cotton jersey, which comprises the following steps:

[0045] S1. Pre-treatment: pre-treat the cotton jersey through an open-width washing machine;

[0046] S2. Alkali rolling is carried out on the cotton jersey; the pretreated cotton jersey is subjected to alkali rolling by a rolling car, the concentration of sodium hydroxide lye is 120g / L, and the change of lye concentration is monitored in real time by the lye concentration tester ;Cotton jersey with sodium hydroxide lye is piled up for 20 hours at room temperature of 20°C, and dyed directly after washing and neutralizing in the dye vat; and triethanol stearate is also added to the sodium hydroxide lye base amine and diethyl carbonate; alkali shrinkage treated cotton jersey such as figure 1 shown;

[0047] S3. After-finishing of cotton jersey; after-treatment of the cotton jersey after alkali rolling is carried out with finishing aids; the finishing agent cons...

Embodiment 2

[0051] The invention discloses an alkali shrinkage process of a cotton jersey, which comprises the following steps:

[0052] S1. Pre-treatment: pre-treat the cotton jersey through an open-width washing machine;

[0053] S2. Alkali rolling is carried out on the cotton jersey; the pretreated cotton jersey is subjected to alkali rolling through a rolling machine, the concentration of sodium hydroxide lye is 160g / L, and the change of lye concentration is monitored in real time by the lye concentration tester ;Cotton jersey with sodium hydroxide lye is piled up for 30h at room temperature of 25°C, and dyed directly after washing and neutralizing in the dye vat; and triethanol stearate is also added to the sodium hydroxide lye amines and diethyl carbonate;

[0054] S3. After-finishing of cotton jersey; after-treatment of the cotton jersey after alkali rolling is carried out with finishing aids; the finishing agent consists of citric acid, tert-butyl acetate, hydroxypropyl acrylate,...

Embodiment 3

[0058] The invention discloses an alkali shrinkage process of a cotton jersey, which comprises the following steps:

[0059] S1. Pre-treatment: pre-treat the cotton jersey through an open-width washing machine;

[0060] S2. Alkali rolling is carried out on the cotton jersey; the pretreated cotton jersey is subjected to alkali rolling through a rolling machine, the concentration of sodium hydroxide lye is 150g / L, and the change of lye concentration is monitored in real time by the lye concentration tester ;Cotton jersey with sodium hydroxide lye is piled up for 24 hours at room temperature of 24°C, and dyed directly after washing and neutralizing in the dye vat; and triethanol stearate is also added to the sodium hydroxide lye amines and diethyl carbonate;

[0061] S3. After-finishing of cotton jersey; after-treatment of the cotton jersey after alkali rolling is carried out with finishing aids; the finishing agent consists of citric acid, tert-butyl acetate, hydroxypropyl acry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of alkali shrinkage technology of cloth, and discloses an alkali shrinkage technology of all-cotton jersey. The technology comprises the following steps ofS1, pre-treatment, wherein the pre-treatment of the all-cotton jersey is carried out through an open-width washing machine; S2, alkali padding of the all-cotton jersey; S3, afterfinish processing ofthe all-cotton jersey; and S4, drying and sizing of the all-cotton jersey, wherein the sizing of the all-cotton jersey is completed through a setting machine; and the pre-shrinking process is carriedout. The technology has the following advantages and effects that the pre-treatment is carried out through the open-width washing machine to ensure the uniformity of subsequent alkali shrinkage of theall-cotton jersey, the internal structure of cotton fiber of uniformly alkali-shrunk all-cotton jersey is changed, the ability of dyeing cotton fiber on the dye is improved, the coloring is easier, all fastness indicators reach national standards, the dimensional stability is good, the draping feeling is good, the fabric is stiff and smooth and shiny, and is not easy to pill and wrinkle, and theoverall grade is greatly improved.

Description

technical field [0001] The invention relates to the technical field of the alkali shrinkage process of cloth, in particular to an alkali shrinkage process of cotton jersey. Background technique [0002] Cotton jersey is very common in the market, and consumers are willing to buy it. Pure cotton jersey is a single-sided fabric with 100% cotton. Many T-shirts are made of pure cotton jersey, which has better sweat absorption. Cotton jersey is easy to wrinkle, absorbs water well but sticks to the skin easily, causing a "stuffy" feeling. At the same time, after washing the cotton jersey many times, the glossiness is poor, the color is not bright enough, and the cotton jersey is loose and has no crisp feeling; in order to solve this problem, the cotton jersey is usually treated with an alkali shrinkage process. The process of treating cotton knitted fabrics with concentrated caustic soda solution in a relaxed state. The alkali shrinkage of cotton knitted fabrics has two process...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/38D06M15/643D06M15/00D06M13/328D06M13/207D06M13/224D06M13/432D06L1/12D06M101/06
CPCD06M11/38D06M15/643D06M15/00D06M13/328D06M13/207D06M13/224D06M13/2246D06M13/432D06L1/12D06M2101/06D06M2200/50D06M2200/20
Inventor 高安根高清清高菡璐
Owner 浙江健安达纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com