A kind of preparation method of cuprous oxide electrode

A cuprous oxide and electrode technology, applied in the field of electrochemistry, can solve the problems of high cost, poor structure uniformity, complex preparation process, etc., and achieve the effect of high capacitance value and good conductivity

Active Publication Date: 2022-02-18
HEBEI UNIV OF TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, commonly used metal current collectors with large specific surface areas include foamed metals and porous metals prepared by dealloying methods. These metal current collectors also have problems such as complex preparation process, high cost, and poor structural uniformity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of cuprous oxide electrode
  • A kind of preparation method of cuprous oxide electrode
  • A kind of preparation method of cuprous oxide electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) The copper sheet was ultrasonically cleaned with a mixed solution of ethanol and deionized water, and then immersed in a sulfuric acid solution with a mass concentration of 10% for 5 hours to remove possible oxides on the surface of the copper sheet.

[0029] (2) Add 3.2g copper sulfate (0.02 mol), 1.0g ferric sulfate, 0.2g phenyltrimethylammonium chloride, 0.2g benzylamine in 100g deionized water, stir and dissolve, and use 10% Sulfuric acid adjusted the pH of the solution to 5.1.

[0030] (3) take the processed copper sheet as the negative electrode and the platinum sheet as the anode, and the prepared solution of the step (2) is the electrodeposition solution, at room temperature, the current density is 70mA / cm 2 Under the condition of DC electrodeposition for 5 minutes; after the reaction, the sample was washed with deionized water and dried at 150°C for 2 hours to obtain a cuprous oxide electrode.

[0031] The morphology and structure of the prepared cuprous o...

Embodiment 2

[0034] (1) Change sulfuric acid into hydrochloric acid, carry out pretreatment to copper sheet with embodiment 1 (1) process step.

[0035] (2) Add 2.7g cupric chloride, 0.5g ferric chloride, 0.3g phenyltrimethylammonium chloride, 0.1g phenethylamine in 100g deionized water, stir and dissolve, and adjust with 10% sulfuric acid with mass concentration The pH of the solution was 5.6.

[0036] (3) At 120mA / cm 2 Under the condition of direct current electrodeposition for 3 minutes, the other process steps are the same as in Example 1 (3), and a cuprous oxide electrode can be prepared.

Embodiment 3

[0038] (1) Copper sheet is carried out pretreatment with embodiment 1 (1) technological step.

[0039] (2) add 3.6g copper acetate, 1.5g ferric sulfate, 0.1g benzyltrimethylammonium chloride, 0.3g cyclohexylamine in 100g deionized water, stir and dissolve, be the sulfuric acid adjustment solution of 10% with mass concentration The pH is 4.3.

[0040] (3) At 40mA / cm 2 Under the conditions of direct current electrodeposition for 8 minutes, other process steps are the same as in Example 1 (3), and a cuprous oxide electrode can be prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
current densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a cuprous oxide electrode. The method comprises the following steps: cleaning the copper sheet ultrasonically, and then immersing it in sulfuric acid or hydrochloric acid solution to obtain a treated copper sheet; using the treated copper sheet as a cathode and a platinum sheet as an anode, inserting it into an electrodeposition solution, at room temperature , The current density is 40~120mA / cm 2 Under the condition of direct current electrodeposition for 3-8 minutes, then dry the sample at 130-170°C to obtain the cuprous oxide electrode. The electrodeposition solution is composed of adding 0.02mol divalent copper salt, 0.5-1.5g ferric salt, 0.1-0.3g quaternary ammonium salt and 0.1-0.3g organic amine compound for every 80-120g deionized water. The invention has simple process, low cost, good controllability and excellent product performance.

Description

Technical field: [0001] The invention belongs to the field of electrochemistry, in particular to a method for preparing a cuprous oxide electrode. Background technique: [0002] Supercapacitors are electrical energy storage devices that are widely used in electric vehicles, urban rail transit, portable electronic equipment, aerospace, new energy systems, smart grids, and military equipment. [0003] The performance of supercapacitors is mainly determined by the electrodes, which are composed of current collectors and active substances. Pseudocapacitive active substances have higher storage capacity, which mainly include metal oxides and conductive polymers. Copper oxide has the advantages of good performance, easy preparation, low cost, and environmental protection. There have been reports on copper oxide electrodes. For example, "Chem. Phys. Lett." (2018, 691, P366-372) reported a preparation method of copper oxide electrodes, first preparing nanoporous bamboo leaf-like Cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D9/08H01G11/46H01G11/86H01G11/26
CPCC25D9/08H01G11/46H01G11/86H01G11/26
Inventor 王西新印泽坤赵建玲李子庆
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap