Copper nanoparticle solution as well as preparation method and application thereof
A copper nanoparticle and solution technology, applied in the fields of nanotechnology, nano-optics, nanotechnology, etc., can solve the problems of transition metal ion interference, cumbersome synthesis procedures, long response time, etc., to achieve strong selectivity, broad application prospects, reaction short time effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0051] Example 1:
[0052] Preparation of copper nanoparticle solution
[0053] Using polyvinylpyrrolidone as the protective agent, 2-mercaptobenzothiazole as the stabilizer, and hydrazine hydrate as the reducing agent, a new method for preparing orange-red fluorescent copper nanoparticles, the reaction diagram is as follows figure 1 Shown:
[0054] (1) Accurately weigh copper chloride and dissolve it in ultrapure water to obtain a concentration of 1.0 mM CuCl 2 Aqueous solution; accurately weigh 2-mercaptobenzothiazole and dissolve it with 1.0M NaOH solution to prepare a 10.0mM 2-mercaptobenzothiazole solution; accurately weigh polyvinylpyrrolidone and dissolve it in ultrapure water to obtain a concentration of 0.07mM Of polyvinylpyrrolidone, pipette 1.0 mL of copper chloride solution, 10.0 mL of polyvinylpyrrolidone solution, and 5.0 mL of 2-mercaptobenzothiazole solution in a clean and dry 25.0 mL colorimetric tube.
[0055] (2) Add 0.4 mL of hydrazine hydrate stock solution to the...
Example Embodiment
[0066] Example 2
[0067] The technical scheme of this embodiment is the same as that of embodiment 1, except that 2.0 mL of polyvinylpyrrolidone solution is added in step (2), and the concentration of polyvinylpyrrolidone in the solution system is adjusted to 5.6 μM.
Example Embodiment
[0068] Example 3
[0069] The technical scheme of this embodiment is the same as that of embodiment 1, except that 6.0 mL of polyvinylpyrrolidone solution is added in step (2), and the concentration of polyvinylpyrrolidone in the solution system is adjusted to 16.8 μM.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap