Preparation method of intelligent anti-skid solid wood composite floor
A solid wood composite flooring and anti-skid technology, which is applied in the jointing of wooden veneers, manufacturing tools, wood treatment, etc., can solve the problems of poor anti-mildew effect, high formaldehyde content, poor flame retardancy, etc., and achieve good low temperature resistance, Low formaldehyde emission and good wear resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0035] A preparation method for an intelligent non-slip solid wood composite floor, the steps are:
[0036] Step 1: Heat and dry a group of veneers at 60°C to a moisture content of 10%, place the dried veneers in a sodium selenite solution with a mass concentration of 8 mg / L at 40°C, soak for 2 hours, and then Sonicate at 31KHz for 30min, then freeze-dry at -40°C to a moisture content of 8%;
[0037] The second step: 100 parts of soybean protein adhesive, 2 parts of chitin, 0.5 parts of nano-silicon chip, 4 parts of OP-10 emulsifier, 3 parts of resorcinol, 2 parts of amine, 2 parts of kaolin, 0.5 part of urea, 1 part of diphenyl-isooctyl phosphate, 5 parts of butyl methacrylate, 0.1 part of benzoyl peroxide, 10 parts of diethylene glycol methacrylate , 0.03 parts of dimethyl benzyl dodecyl ammonium bromide, 6 parts of diethylenetriamine, 3 parts of dimethyl phthalic acid, 0.6 parts of triclosimide, and 6 parts of styrene, mix well and put into grinding Machine grinding for 2...
Embodiment 2
[0049] A preparation method for an intelligent non-slip solid wood composite floor, the steps are:
[0050] Step 1: Heat and dry a group of veneers at 70°C to a moisture content of 14%, place the dried veneers in a sodium selenite solution at 50°C with a mass concentration of 10 mg / L, soak for 3 hours, and then Sonicate at 33KHz for 40min, then freeze-dry at -40°C to a moisture content of 10%;
[0051] The second step: 100 parts of soybean protein adhesive, 4 parts of chitin, 1.5 parts of nano-silicon chip, 6 parts of OP-10 emulsifier, 5 parts of resorcinol, 6 parts of amine, 4 parts of kaolin, 2.5 parts of urea, 3 parts of diphenyl-isooctyl phosphate, 15 parts of butyl methacrylate, 0.3 parts of benzoyl peroxide, 20 parts of diethylene glycol methacrylate , 0.05 parts of dimethyl benzyl dodecyl ammonium bromide, 10 parts of diethylenetriamine, 7 parts of dimethyl phthalic acid, 1 part of triclosulphate, and 8 parts of styrene, mix them evenly and put them into grinding Mach...
Embodiment 3
[0063] A preparation method for an intelligent non-slip solid wood composite floor, the steps are:
[0064] Step 1: Heat and dry a group of veneers at 65°C to a moisture content of 12%, place the dried veneers in a sodium selenite solution with a mass concentration of 9 mg / L at 45°C, soak for 3 hours, and then Sonicate at 32KHz for 35min, then freeze-dry at -40°C to a moisture content of 9%;
[0065] The second step: mix 100 parts of soybean protein adhesive, 3 parts of chitin, 1 part of nano-silicon chip, 5 parts of OP-10 emulsifier, 4 parts of resorcinol, and 4 parts of amine, 3 parts of kaolin, 1.5 parts of urea, 2 parts of diphenyl-isooctyl phosphate, 10 parts of butyl methacrylate, 0.2 parts of benzoyl peroxide, 15 parts of diethylene glycol methacrylate , 0.04 parts of dimethyl benzyl dodecyl ammonium bromide, 8 parts of diethylenetriamine, 5 parts of dimethyl phthalic acid, 0.8 parts of triclosimide, 7 parts of styrene, mix well and put into grinding Machine grinding ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| hardness | aaaaa | aaaaa |
| hardness | aaaaa | aaaaa |