VN-AgMoS2 composite material with wide temperature range self-lubricating performance and preparation method of VN-AgMoS2 composite material

A composite material and self-lubricating technology, which is applied in the wide temperature range self-lubricating VN-AgMoS2 composite material and its preparation field, to achieve the effect of tight combination, less equipment investment and uniform structure

Active Publication Date: 2020-11-20
NINGBO KANGQIANG MICRO ELECTRONICS TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main purpose of the present invention is to provide a VN-Ag/MoS with excellent wide temperature range self-lubricating properties 2 Composite m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • VN-AgMoS2 composite material with wide temperature range self-lubricating performance and preparation method of VN-AgMoS2 composite material
  • VN-AgMoS2 composite material with wide temperature range self-lubricating performance and preparation method of VN-AgMoS2 composite material
  • VN-AgMoS2 composite material with wide temperature range self-lubricating performance and preparation method of VN-AgMoS2 composite material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] A preparation method of a wide temperature range nickel-based self-lubricating composite material, comprising the steps of:

[0030] 1) Weigh 70-90% of VN powder, 5-15% of silver powder and 5-15% of molybdenum disulfide powder by mass ratio to obtain original ingredients;

[0031] 2) Use a planetary ball mill for mechanical mixing of the original ingredients to obtain a uniform mixed powder;

[0032] 3) Put the mixed powder into the graphite grinding tool for cold pressing;

[0033] 4) Under vacuum protection, the graphite abrasive tool with mixed powder is sintered at high temperature by hot pressing to obtain VN-Ag / MoS 2 composite material.

[0034] Described VN powder, Ag powder and MoS 2 All are purchased from the market, and the average particle size is <15 μm, <1 μm and <10 μm, respectively.

[0035] As a further improvement of the above preparation method, the ball-to-material ratio in the ball milling process in step 2) is 5:1-10:1, the ball-milling speed is...

Example Embodiment

[0039] Example 1 A VN-Ag / MoS with excellent wide temperature range self-lubricating properties 2 The composite material and its preparation method are carried out according to the following steps:

[0040] (1) According to the mass fraction of VN powder is 70%, Ag / MoS 2 The mass fractions were 15% of the proportion of ingredients, weighing 70 grams of vanadium nitride powder and Ag / MoS 2 15 grams of each powder to obtain the original batch, wherein the average particle size of the VN powder is 2 The average particle size of the powder is <10 μm.

[0041] (2) Put the original ingredients in a planetary ball mill, and mix them for 5 hours at a ball-to-material ratio of 10:1 and a rotational speed of 200 r / min to obtain uniformly mixed sintered ingredients;

[0042](3) Put the sintered ingredients into the graphite grinding tool, firstly perform cold pressing at a pressure of 10 MPa, and then perform hot pressing sintering in a vacuum environment, where the sintering temperatur...

Example Embodiment

[0044] Example 2 A VN-Ag / MoS with excellent wide temperature range self-lubricating properties 2 The composite material and its preparation method are carried out according to the following steps:

[0045] (1) According to the mass fraction of VN powder is 80%, Ag / MoS 2 The mass fractions were 10% of the proportion of ingredients, weighing 80 grams of vanadium nitride powder and Ag / MoS 2 10 grams of each powder to obtain the original ingredients, wherein the average particle size of VN powder 2 The average particle size of the powder is <10 μm.

[0046] (2) Put the original ingredients in a planetary ball mill, and mix them for 5 hours at a ball-to-material ratio of 10:1 and a rotational speed of 200 r / min to obtain uniformly mixed sintered ingredients;

[0047] (3) Put the sintered ingredients into the graphite grinding tool, firstly perform cold pressing at a pressure of 10 MPa, and then perform hot pressing sintering in a vacuum environment, where the sintering temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Hardnessaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a VN-AgMoS2 composite material with wide temperature range self-lubricating performance, and relates to the field of self-lubricating composite materials. The VN-AgMoS2 composite material consists of the following components, by mass percent, 70-90% of VN powder, 5-15% of silver powder and 5-15% of molybdenum disulfide powder. A vanadium nitride is selected as a matrix of the composite material, silver / molybdenum disulfide is selected as a composite lubricating agent, vanadium nitride ceramics provide excellent wide temperature range abrasion resistance, while room temperature lubrication action comes from the molybdenum disulfide lubricating agent of a layer structure, and medium-high temperature lubrication action comes from an oxide lubricating agent produced in the process of high temperature friction, such as molybdenum oxide, silver molybdate acid and silver vanadate. The VN-AgMoS2 composite material is applicable to a large number of machine parts in extreme working conditions such as high temperature, high load and high vacuum in aerospace, energy, automobile and machine manufacturing industries, and has broad application prospects.

Description

technical field [0001] The invention relates to the field of self-lubricating composite materials, more specifically, to a wide temperature range self-lubricating VN-AgMoS 2 Composite materials and methods for their preparation. Background technique [0002] In aerospace, energy, automobile, machinery manufacturing and other industries, there are a large number of machine parts working under extreme working conditions such as high temperature, high load and high vacuum, which will affect the wear resistance, corrosion resistance, fatigue resistance and high temperature performance of materials. More and more stringent requirements have been put forward. Lubricating oil and grease Conventional lubricating materials are prone to failure and volatilization in high temperature environments, and it is difficult to exert effective lubrication under the conditions of dust and high impact strength, resulting in the equipment being in a state of lean oil or dry friction, causing dam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C29/16C22C1/05C22C1/10
CPCC22C1/051C22C29/005C22C29/16
Inventor 郑芳
Owner NINGBO KANGQIANG MICRO ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products