MXene/nitrogen-doped carbon foam composite material with 3D porous neuron-like structure and its preparation method
A technology of nitrogen-doped carbon and composite materials, which is applied in the preparation/purification of carbon, the manufacture of hybrid/electric double layer capacitors, titanium carbide, etc., and can solve the problems of unstable porous MXene structure, complex synthesis process, and ecological pollution. Achieve the effects of improving electrical properties, promoting penetration, and reducing capacitance loss
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] A kind of MXene / N doped carbon foam composite material of 3D porous neuron structure, its preparation method is as follows:
[0031] 1) Slowly dissolve 1.6g of lithium fluoride in 20mL of 9M hydrochloric acid solution, stir for 5min, and slowly add 1g of Ti 3 AlC 2 (10min), stirred at 45°C for 24h, then washed and centrifuged with deionized water at 3500rpm, centrifuged for 5min each time, centrifuged 6-8 times until the pH value of the supernatant was greater than 6, collected the precipitate, and added the precipitate to 100mL Ultrasonic dispersion in water for 3h under the protection of argon, centrifuge the resulting dispersion at 3500rpm for 1h, collect the supernatant to obtain MXene colloidal solution, the concentration is about 5mg mL -1 , add deionized water to the MXene colloidal dispersion, and ultrasonically disperse evenly to obtain a concentration of 2.5mgmL -1 MXene colloidal dispersion;
[0032] 2) Fully immerse melamine formaldehyde resin foam with a...
PUM
Property | Measurement | Unit |
---|---|---|
pore volume | aaaaa | aaaaa |
pore volume | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com