Healthy ecological cotton including soybean fibers and preparation method of healthy ecological cotton

A soybean fiber and ecological cotton technology, which is applied in the directions of fiber chemical characteristics, melt spinning, stretch spinning, etc., can solve the problems of bamboo charcoal fiber and hollow fiber accounting for a large proportion, the overall tendency to harden, and the inconspicuous soybean fiber, etc. Achieve the effects of high preparation efficiency, not easy to form holes, and low preparation cost

Inactive Publication Date: 2020-12-08
CHENGDU ZHIA TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large proportion of bamboo charcoal fiber and hollow fiber in this ecological cotton, the advantages of soybean fiber are not obvious, and it is easy to harden and form holes on the whole

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]A healthy ecological cotton containing soybean fiber is characterized in that it is made of the following raw materials in parts by weight: 50 parts of soybean fiber, 15 parts of acetonitrile fiber, 30 parts of functional synthetic fiber, and 3 parts of recycled polyester powder; Functional synthetic fibers are made by melt spinning the following components in parts by weight: Cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyl triethyl 60 parts of oxysilane copolymer, 5 parts of graphene hollow nanofibers.

[0035] The preparation method of described cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyltriethoxysilane copolymer comprises the following steps: cucurbitadienol, Acrylonitrile, 3-(2-propenylselenyl)-L-alanine, vinyltriethoxysilane, and initiator were added to the high boiling point solvent, and stirred and reacted at 70°C for 4 hours in a nitrogen atmosphere, and then Precipitate in water, wash the precipitated polymer with e...

Embodiment 2

[0046] A healthy ecological cotton containing soybean fiber is characterized in that it is made of the following raw materials in parts by weight: 53 parts of soybean fiber, 17 parts of acetonitrile fiber, 33 parts of functional synthetic fiber, and 4 parts of recycled polyester powder; Functional synthetic fibers are made by melt spinning the following components in parts by weight: Cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyl triethyl 65 parts of oxysilane copolymer, 7 parts of graphene hollow nanofibers.

[0047] The preparation method of described cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyltriethoxysilane copolymer comprises the following steps: cucurbitadienol, Acrylonitrile, 3-(2-propenylselenyl)-L-alanine, vinyltriethoxysilane, and initiator were added to the high boiling point solvent, and stirred and reacted at 73°C for 4.5 hours in an inert gas atmosphere, Then it was precipitated in water, and the precipitated polyme...

Embodiment 3

[0058] A healthy ecological cotton containing soybean fiber is characterized in that it is made of the following raw materials in parts by weight: 55 parts of soybean fiber, 20 parts of acetonitrile fiber, 35 parts of functional synthetic fiber, and 4.5 parts of recycled polyester powder; Functional synthetic fibers are made by melt spinning the following components in parts by weight: Cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyl triethyl 70 parts of oxysilane copolymer, 8 parts of graphene hollow nanofibers.

[0059] The preparation method of described cucurbitadienol / acrylonitrile / 3-(2-propenylselenoyl)-L-alanine / vinyltriethoxysilane copolymer comprises the following steps: cucurbitadienol, Acrylonitrile, 3-(2-propenylselenyl)-L-alanine, vinyltriethoxysilane, and initiator were added to the high boiling point solvent, and stirred and reacted at 75°C for 5 hours in an inert gas atmosphere, Then it was precipitated in water, and the precipitated polyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses healthy ecological cotton including soybean fibers. The healthy ecological cotton is characterized by being prepared from the following raw material in parts by weight: 50-60 parts of soybean fibers, 15-25 parts of acetonitrile fibers, 30-40 parts of functional synthetic fibers and 3-6 parts of regenerated polyester powder, wherein the functional synthetic fibers are prepared from the following components in parts by weight through melt spinning: 60-80 parts of cucurbitadienol / acrylonitrile / 3-(2-Propenylseleno)-L-alanine / vinyltriethoxysilane copolymer and 5-10 parts ofgraphene hollow nanofibers. The invention further discloses a preparation method of the healthy ecological cotton including the soybean fibers. The healthy ecological cotton including the soybean fibers is excellent in comprehensive performance, good in heat retention property and skin-friendly property, good in washing fastness, high-temperature resistance and weather resistance, good in air permeability, not prone to hardening, not prone to forming broken holes, and ecological, environmentally friendly and healthy to use.

Description

technical field [0001] The invention relates to the technical field of ecological cotton, in particular to a healthy ecological cotton containing soybean fiber and a preparation method thereof. Background technique [0002] With the advancement of science and technology, people not only pay attention to the quality and specifications of textiles in the traditional sense, but also pay more attention to a series of ecological safety such as the safety, health and environmental impact of textiles. The fusion and unity of quality and fashion, nature and ecology have been reflected in modern clothing design. As a common textile, cotton has three characteristics: good hygroscopicity, strong warmth retention, and non-irritating to the human body. It is especially suitable for children, pregnant women and people who are prone to allergies who have high requirements for the sleeping environment. Due to the insufficient opening of the cotton fiber in the traditional cotton quilt, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/587D04H1/60D01D5/08D01D5/12D01D10/02D01F8/18D01F8/10
CPCD01D5/08D01D5/12D01D10/02D01F8/10D01F8/18D04H1/4382D04H1/587D04H1/60
Inventor 向红荣
Owner CHENGDU ZHIA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More