Bulletproof flashboard with edge covering structure and manufacturing method thereof

A technology of bulletproof inserts and wrapping, applied in the structure of armor plates, chemical instruments and methods, protective clothing, etc., can solve the problems of poor binding force on the side of ceramics, diffusion of ceramic cracks to the edge, and insufficient ability to resist multiple bullets. Achieve the effect of improving bullet resistance and multiple bullet resistance, improving mechanical strength, and enhancing mechanical strength

Pending Publication Date: 2021-01-22
际华集团股份有限公司系统工程中心 +1
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, high-performance fibers such as aramid fibers are used for bulletproof inserts on the ceramic surface for lateral restraint, which plays the role of crack arrest and anti-sputtering. However, this structure has the problem of poor restraint on the side of the ceramic, which easily causes ceramic cracks to spread to the edge, making it difficult to Guarantee the integrity of bulletproof ceramics, resulting in insufficient resistance to multiple bullets
[0003] The patent with the publication number CN110230952A proposes to constrain the entire circumference of the ceramic bulletproof panel by means of integral fiber winding, but since the ceramic plate is multi-curved, the winding effect of this method on the concave surface is not ideal
The patent of Publication No. CN110953933 A proposes to use seamless tubular fabric orthogonally nested to cover the ceramic plate in a seamless tubular shape, but it is convenient to cover the ceramic plate because the nest is larger than the ceramic plate, so this method covers The overlaid ceramic surface is prone to wrinkling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bulletproof flashboard with edge covering structure and manufacturing method thereof
  • Bulletproof flashboard with edge covering structure and manufacturing method thereof
  • Bulletproof flashboard with edge covering structure and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] Manufacture of bullet-proof insert with hemming structure

[0079] Phenolic resin 50g, polyvinyl butyral 5g, and defoamer n-butanol 0.2g and solvent ethanol 50g, mix in ball mill tank, ball mill 2 hours, obtain cast slurry; Ball mill speed is set to 300rpm, and ball mill ball is An alumina ball with a mass of 400g and a diameter of 4mm;

[0080] The casting slurry is cast into a film on a casting machine, the casting speed is 1m / min, and the height of the scraper is 1mm;

[0081] The temperature in the drying zone is set at 60°C, and after the casting film is dried, a phenolic resin-based ordinary film is obtained;

[0082] Lay ultra-high molecular weight polyethylene board, phenolic resin-based common film, second aramid woven cloth, phenolic resin-based common film, boron carbide ceramic plate, phenolic resin-based common film, and first aramid woven cloth in sequence Ok, get the composite material, put it into a vacuum bag and seal it; among them, the thickness of ...

Embodiment 2

[0086] Manufacture of Bulletproof Plate with Heat-absorbing Adhesive Film and Hemming Structure

[0087] Phenolic resin 50g, polyvinyl butyral 5g, graphene 10g, particle size are 10000 meshes of magnesium hydroxide 10g, with antifoaming agent n-butanol 0.2g and solvent ethanol 50g, mix in ball mill tank, ball mill 2 hours, obtain fluid Extend the slurry; the ball milling speed is set to 300rpm, and the ball milling ball is an alumina ball with a quality of 400g and a diameter of 4mm;

[0088] The casting slurry is cast into a film on a casting machine, the casting speed is 1m / min, and the height of the scraper is 1mm;

[0089] The temperature in the drying zone is set at 60°C, and after the cast film is dried, a phenolic resin-based heat-absorbing adhesive film is obtained;

[0090] The ultra-high molecular weight polyethylene plate, phenolic resin-based heat-absorbing adhesive film, the second aramid woven cloth, phenolic resin-based ordinary adhesive film, boron carbide cer...

Embodiment 3

[0108] Manufacture of bullet-proof insert with hemming structure

[0109] 50g of bisphenol A epoxy resin with a molecular weight of 4500-6500, 10g of liquid nitrile rubber toughening agent, and 50g of solvent acetone are mixed in a ball milling tank, and 0.5g of maleic anhydride is added after ball milling for 2 hours, and then continue Ball milled for 10 minutes to obtain the coating slurry; the ball milling speed was set at 300rpm, and the milling ball was an alumina ball with a mass of 400g and a diameter of 4mm; then the slurry was coated on the base film with a coating machine, and the curing temperature was 110°C , the curing time is 6h, and the epoxy resin-based ordinary adhesive film is obtained;

[0110] Lay ultra-high molecular weight polyethylene board, ordinary epoxy resin film, second aramid woven cloth, ordinary epoxy resin film, boron carbide ceramic plate, ordinary epoxy resin film, and first aramid woven cloth in sequence OK, get the material to be composited...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bulletproof flashboard with an edge covering structure and a manufacturing method thereof. The bulletproof flashboard comprises first woven cloth, a ceramic plate, second woven cloth and an ultra-high molecular weight polyethylene plate which are arranged in sequence, wherein the edge end face of the ceramic plate is covered with the edge part of the first woven cloth. According to the bulletproof flashboard with the edge covering structure, the edge end part of the ceramic plate is coated with the woven cloth, so that the surface and the end surface of the ceramic plate are coated with the continuous woven cloth, constraint force on the ceramic plate in the three-dimensional direction is formed, the mechanical strength of the ceramic plate is enhanced, the back bulge value of the bulletproof flashboard is effectively reduced, and the bullet resistance and the multi-bullet resistance of the bulletproof flashboard are improved.

Description

technical field [0001] The application belongs to the technical field of personal protective equipment, and in particular relates to bulletproof materials, in particular to a bulletproof insert with a hemming structure and a manufacturing method thereof. Background technique [0002] At present, high-performance fibers such as aramid fibers are used for bulletproof inserts on the ceramic surface for lateral restraint, which plays the role of crack arrest and anti-sputter. Guarantee the integrity of bulletproof ceramics, resulting in insufficient ability to resist multiple bullets. [0003] The patent with the publication number CN110230952A proposes to constrain the entire circumference of the ceramic bulletproof panel by means of overall winding of fibers, but since the ceramic plate is multi-curved, the winding effect of this method on the concave surface is not ideal. The patent of Publication No. CN110953933 A proposes to use seamless tubular fabric orthogonally nested ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F41H5/04B32B3/08B32B3/26B32B5/02B32B7/022B32B7/12B32B9/00B32B9/04B32B27/08B32B27/12B32B27/20B32B27/32B32B27/40B32B27/42B32B37/06B32B37/10B32B37/12B32B38/00B32B38/18
CPCF41H5/0428B32B5/02B32B9/005B32B9/047B32B27/12B32B27/32B32B3/08B32B7/12B32B9/00B32B9/007B32B3/26B32B7/022B32B37/06B32B37/1018B32B38/0012B32B38/1808B32B37/1284B32B27/20B32B27/08B32B27/40B32B27/42B32B2038/0016B32B2264/108B32B2270/00B32B2307/56B32B2571/00
Inventor 田琨力小安嵇从民段银海陈晓林葛爱雄王庆春王丽芳赵艳娇徐芳薛霜黄嘉俊
Owner 际华集团股份有限公司系统工程中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap