A Method of Refining Carbide in Large Size gh4738 Ingot

A carbide, large-scale technology, applied in the direction of improving process efficiency, improving energy efficiency, etc., to achieve the effect of refining grains, refining carbides, and promoting homogeneous nucleation of TiN

Active Publication Date: 2021-03-30
UNIV OF SCI & TECH BEIJING +1
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The large ingot type GH4738 superalloy often adopts a double or triple process with vacuum self-consumption melting as the final smelting link, but there is no report on the smelting process for large-scale carbide refinement in GH4738 ingots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method of Refining Carbide in Large Size gh4738 Ingot
  • A Method of Refining Carbide in Large Size gh4738 Ingot
  • A Method of Refining Carbide in Large Size gh4738 Ingot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The vacuum induction melting ingot specification of GH4738 superalloy is φ508mm, and the vacuum self-consumption melting ingot specification is φ560mm (that is, the diameter of the final GH4738 ingot is φ560mm). The specific process includes the following steps:

[0057] ① Using pure nickel plate, pure chromium block, pure cobalt plate, pure tungsten bar, electrode carbon, pure molybdenum block, pure aluminum block, sponge titanium, iron-boron alloy, and sponge zirconium as raw materials, the crucible is nickel-washed before smelting. GB / T 14992-2005 Classification and Designation of High-temperature Alloys and Intermetallic High-Temperature Materials" as the standard, add pure nickel plate, pure chromium block, pure cobalt plate, pure tungsten bar, electrode carbon, pure molybdenum block in sequence according to the proportion, and vacuumize To <0.05Pa, power transmission smelting, after melting, power frequency stirring for 20min, sequentially add sponge titanium, pure...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for refining carbides in large-size GH4738 ingots. The method includes: preparing raw materials; performing vacuum induction melting on the raw materials to obtain induction melting ingots; using the induction melting ingots as consumable electrodes to perform vacuum consumable melting in sequence according to the arc starting stage, stable melting stage and heat capping stage; After consumable smelting, the furnace is cooled and stripped to obtain GH4738 ingots with refined carbides; by strictly controlling the nitrogen content in the vacuum induction smelting ingots, the reasonable smelting rate during the vacuum consumable smelting process, with He gas Cooling system to reduce the carbon segregation in the GH4738 ingot, refine the grains, and promote the homogeneous nucleation of TiN, so as to achieve the effect of refining the carbide size in the GH4738 ingot. The method of the invention can effectively reduce the nitrogen content in the alloy, refine the size of the carbide in the GH4738 ingot, and improve the mechanical properties of the GH4738 ingot.

Description

technical field [0001] The invention belongs to the technical field of superalloy preparation, and in particular relates to a method for refining carbides in large-size GH4738 ingots. Background technique [0002] GH4738 superalloy has good yield strength and fatigue resistance at 760~870°C, and is widely used in hot end parts such as aeroengine turbine blades. Carbide is an important part of the structure of superalloys and has an important impact on the properties of superalloys. Carbide has a dual role in the alloy. On the one hand, it can strengthen the grain boundary and play a pinning role in the process of stress deformation. On the other hand, large-size carbides destroy the continuity of the alloy and reduce the initiation point of cracks. The mechanical properties of the alloy. The formation mechanism of large-size carbides is divided into two types, one is formed by precipitation from the grain boundary during alloy smelting and solidification, and the other is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22B9/20C22B9/05C22C1/02
CPCC22B9/05C22B9/20C22C1/023Y02P10/25
Inventor 杨树峰杨曙磊赵朋曲敬龙王宁杜金辉荣义刘威谷雨周扬徐志强
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap