Fluid loss agent suitable for aluminate cement paste and preparation method offluid loss agent

A fluid loss reducing agent and cement slurry technology, applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of low solid content, rheological parameters, large water ash, etc., to increase the bearing effect, reduce the Particle fineness, the effect of increasing hydrophilicity

Active Publication Date: 2021-03-19
CNPC DRILLING RES INST +2
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of thermal recovery of heavy oil, the thermal stability of oil well cement after adding sand will still be reduced, so that the cementing quality and cement sheath integrity of heavy oil thermal recovery wells have not been resolved, thus affecting thick oil wells. Production safety and production life of oil thermal recovery wells
At present, the water-cement ratio of aluminate cement slurry is relatively large, the solid content is small, and the free water is relatively large, which leads to a large amount of water loss in aluminate cement slurry, causing rheological parameters and thickening time to deviate far from the preset values, seriously reducing Displacement efficiency affects construction quality and even leads to failure of cementing operation
The oil well cement fluid loss reducer used for Portland cement is often not suitable for aluminate cement slurry, and there is an urgent need to develop a fluid loss reducer suitable for aluminate cement slurry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluid loss agent suitable for aluminate cement paste and preparation method offluid loss agent
  • Fluid loss agent suitable for aluminate cement paste and preparation method offluid loss agent
  • Fluid loss agent suitable for aluminate cement paste and preparation method offluid loss agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Preparation process of fluid loss reducer:

[0033] Formula 1: 21.2 grams of N-(3-dimethylaminopropyl) methacrylamide, 16.7 grams of methacryloyloxyethyltrimethylammonium chloride, 12.3 grams of 2-acrylamido-2-methylpropane Sulfonic acid, 0.7 grams of acrylic acid, 0.4 grams of ammonium persulfate, 124 grams of water.

[0034] 1. Preparation method of Agent A: Weigh each component for later use, add some water to the reaction kettle, and then add 21.2 grams of N-(3-dimethylaminopropyl) methacrylamide and 12.3 grams of 2-propylene Amino-2-methylpropanesulfonic acid, stir until the material is completely dissolved, add an inorganic base to adjust the pH to 8, then add 16.7 grams of methacryloyloxyethyltrimethylammonium chloride component and 0.7 gram of acrylic acid, stirred at a speed of 75 rpm until the material was completely dissolved, slowly added an initiator to the remaining water, made into an initiator solution, added an intermediate reaction solution, stirred a...

Embodiment 2

[0043] Preparation process of fluid loss reducer:

[0044] Formula 2: 26.1 grams of N-(3-dimethylaminopropyl) methacrylamide, 20.3 grams of methacryloyloxyethyltrimethylammonium chloride, 14.8 grams of 2-acrylamido-2-methylpropane Sulfonic acid, 0.8 grams of acrylic acid, 0.5 grams of ammonium persulfate, 146 grams of water.

[0045] 1. Preparation method of Agent A: Weigh the quality of each component for later use, add some water to the reaction kettle, and then add 26.1 grams of N-(3-dimethylaminopropyl) methacrylamide and 14.8 grams of 2-propylene Amino-2-methylpropanesulfonic acid, stir until the material is completely dissolved, add an inorganic base to adjust the pH to 8, then add 20.3 grams of methacryloyloxyethyltrimethylammonium chloride component and 0.8 gram of acrylic acid, stirred at a speed of 75 rpm until the material was completely dissolved, slowly added an initiator to the remaining water, made into an initiator solution, added an intermediate reaction solu...

Embodiment 3

[0054] Preparation process of fluid loss reducer:

[0055] Formula 3: 28.6 grams of N-(3-dimethylaminopropyl) methacrylamide, 23.4 grams of methacryloyloxyethyltrimethylammonium chloride, 17.4 grams of 2-acrylamido-2-methylpropane Sulfonic acid, 0.9 grams of acrylic acid, 0.6 grams of ammonium persulfate, 155 grams of water.

[0056] 1. Preparation method of Agent A: Weigh each component for later use, add some water to the reaction kettle, and then add 28.6 grams of N-(3-dimethylaminopropyl) methacrylamide and 17.4 grams of 2-propylene Amino-2-methylpropanesulfonic acid, stir until the material is completely dissolved, add an inorganic base to adjust the pH to 8, then add 23.4 grams of methacryloyloxyethyltrimethylammonium chloride component and 0.9 gram of acrylic acid, stirred at a speed of 75 rpm until the material was completely dissolved, slowly added an initiator to the remaining water, made into an initiator solution, added an intermediate reaction solution, stirred a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fluid loss agent suitable for aluminate cement paste and a preparation method of the fluid loss agent. The fluid loss agent comprises an agent A and an agent B. The agent Ais a quadripolymer formed by polymerizing N-(3-dimethylaminopropyl) methacrylamide, methacryloyloxyethyl trimethyl ammonium chloride, 2-acrylamido-2-methyl propanesulfonic acid and acrylic acid through a free radical aqueous solution; and the agent B is titanium dioxide. The preparation method comprises the following steps of: mixing the agent A and the agent B according to a mass ratio of 5-10: 1; carrying out crushing and surface modification; carrying out microwave surface treatment, filtering, and drying to obtain the fluid loss agent. The preparation method is reliable in principle and easy and convenient to operate; the prepared fluid loss agent can effectively control the water loss of aluminate cement paste, and the fluid loss agent is suitable for heavy oil thermal recovery well cementation engineering and has a bright market application prospect.

Description

technical field [0001] The invention relates to a fluid loss reducer for cement slurry in the well cementing process in the field of petroleum exploration and development and a preparation method thereof, in particular to a fluid loss reducer suitable for aluminate cement slurry and a preparation method thereof. Background technique [0002] In the field of traditional oil and gas well cementing, the cementing process is to put the casing into the borehole, and then seal the annular space between the casing and the borehole with cement slurry, the purpose of which is to keep the casing in place, support and protect Casing prevents formation fluid from flowing between layers. Well cementing operation is an important part of drilling engineering, not only during drilling, but also during all remaining production periods is a critical and challenging operation. Heavy oil resources are widely distributed in my country, and thermal oil recovery methods (steam huff and puff, stea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/26C08F220/60C08F220/34C08F220/58C08F220/06C09K8/487