Tripolyindanone derivative modified water-based acrylic resin and preparation method thereof

A technology based on water-based acrylic and tridanone, which is applied in biocide-containing paints, anti-fouling/underwater coatings, coatings, etc., to achieve good fluorescence performance, good antibacterial properties, and good stability

Inactive Publication Date: 2021-04-13
UNION FOSHAN CHEM +1
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, there is no researcher in China who has applied triindone to acrylic resin, but combining the characteristics of water-based acrylic resin and triindone, it is of great significance to connect triindone to the structure of water-based acrylic resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tripolyindanone derivative modified water-based acrylic resin and preparation method thereof
  • Tripolyindanone derivative modified water-based acrylic resin and preparation method thereof
  • Tripolyindanone derivative modified water-based acrylic resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A water-based acrylic resin modified by melindone derivatives, the components of which are: 2.5 parts of melindone derivatives, 6.5 parts of isophorone diisocyanate, 0.6 parts of hydroxyethyl acrylate, over 0.4 parts of benzoyl oxide, 3.5 parts of acrylic acid, 50.0 parts of methyl methacrylate, 65.0 parts of butyl methacrylate, 5.0 parts of allyl glycidyl ether, 12.0 parts of propylene glycol butyl ether, 12.0 parts of propylene glycol methyl ether acetate, 7.0 parts of N-methylpyrrolidone, 3.2 parts of triethylamine, and 150.0 parts of deionized water.

[0031] A kind of preparation method of terindanone derivative modified waterborne acrylic resin in the present embodiment, comprises the following steps:

[0032] a. In the reactor, add N-methylpyrrolidone, triindone derivatives, and isophorone diisocyanate in sequence according to the weight of the formula, and heat up to react;

[0033] b. Then add hydroxyethyl acrylate, keep warm and react at 80-86°C, measure the ...

Embodiment 2

[0040] A water-based acrylic resin modified by melindone derivatives, the components of which are: 2.0 parts of melindone derivatives, 6.0 parts of isophorone diisocyanate, 0.8 parts of hydroxyethyl acrylate, over 0.5 parts of benzoyl oxide, 3.8 parts of acrylic acid, 48.0 parts of isobornyl acrylate, 55.0 parts of lauryl methacrylate, 7.0 parts of allyl glycidyl ether, 18.0 parts of alcohol ester dodecane, 7.0 parts of N-methylpyrrolidone , ammonia water 2.5 parts, deionized water 145.0 parts.

[0041] The invention provides a kind of preparation method of terindanone derivative modified water-based acrylic resin, comprising the following steps:

[0042] a. In the reactor, add N-methylpyrrolidone, triindone derivatives, and isophorone diisocyanate in sequence according to the weight of the formula, and heat up to react;

[0043] b. Then add hydroxyethyl acrylate, keep warm and react at 80-86°C, measure the NCO value, and when it is consistent with the design value, the prepo...

Embodiment 3

[0050] A water-based acrylic resin modified by melindone derivatives, the components of which are: 1.8 parts of melindone derivatives, 5.6 parts of isophorone diisocyanate, 0.7 parts of hydroxyethyl acrylate, over 0.5 parts of benzoyl oxide, 3.8 parts of acrylic acid, 30.0 parts of cyclohexyl methacrylate, 30.0 parts of methyl methacrylate, 30.0 parts of butyl methacrylate, 35.0 parts of isooctyl methacrylate, allyl glycidyl 8.0 parts of ether, 20.0 parts of diethylene glycol butyl ether, 6.0 parts of N-methylpyrrolidone, 3.5 parts of triethylamine, and 180.0 parts of deionized water.

[0051] The invention provides a kind of preparation method of terindanone derivative modified water-based acrylic resin, comprising the following steps:

[0052] a. In the reactor, add N-methylpyrrolidone, triindone derivatives, and isophorone diisocyanate in sequence according to the weight of the formula, and heat up to react;

[0053] b. Then add hydroxyethyl acrylate, keep warm and react a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a tripolyindanone derivative modified water-based acrylic resin and a preparation method thereof. The resin is prepared from the following components in parts by weight: 1.5 to 4.5 parts of indanone derivative, 3.0 to 11.0 parts of isophorone diisocyanate, 0.5 to 1.2 parts of hydroxyethyl acrylate, 0.1 to 0.6 part of benzoyl peroxide, 2.0 to 5.0 parts of acrylic acid, 30.0 to 70.0 parts of acrylate hard monomer, 40.0 to 85.0 parts of acrylate soft monomer, 3.0 to 8.0 parts of allyl glycidyl ether, 12.0 to 35.0 parts of cosolvent, 5.0 to 10.0 parts of N-methylpyrrolidone, 1.8 to 7.5 parts of a neutralizer and 100.0 to 200.0 parts of deionized water. The prepared indanone derivative modified water-based acrylic resin has a series of functions of good artificial aging resistance, salt fog resistance, good fluorescence property and the like, and when the resin is prepared into water-based paint, an antibacterial agent does not need to be added, and the water-based paint has good antibacterial and bactericidal functions.

Description

technical field [0001] The invention relates to a modified water-based acrylic resin, in particular to a terindone derivative modified water-based acrylic resin and a preparation method thereof, belonging to the technical field of synthesizing water-based functional resins. Background technique [0002] Water-based acrylic resin has the advantages of good color retention, gloss retention, weather resistance, and alkali resistance. Moreover, there are a wide variety of raw materials, large options, and relatively cheap prices. Therefore, water-based coatings prepared from acrylates are widely used in many fields such as construction, leather, paper, metal anticorrosion, wood, and plastics. Compared with acrylic resin, some properties of water-based acrylic resin are not perfect, and these shortcomings of water-based acrylic resin seriously restrict its application and development. [0003] In addition to reducing the volatilization of organic compounds, as the needs of moder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/00C08F220/14C08F220/18C08F220/06C08F216/14C08G18/67C08G18/32C09D151/08C09D5/08C09D5/22C09D5/14
CPCC08F283/008C08G18/3819C08G18/672C09D5/08C09D5/14C09D5/22C09D151/08C08F220/14C08F220/1804C08F220/06C08F216/1416C08F220/1811C08F220/1812C08F220/1806C08F220/1808
Inventor 张武康伦国姚东生
Owner UNION FOSHAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap