Composite polymer functional fiber, preparation method thereof and pressure spraying equipment for preparing composite polymer functional fiber

A nanocomposite fiber and polymer technology, applied in the field of fiber materials, can solve the problems of high energy consumption, expensive equipment and accessories, and uneven filament thickness

Pending Publication Date: 2021-05-11
北京中科艾加科技有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the equipment and accessories required by the meltblown method are expensive and consume a lot of energy.
You can also use the manual pres...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite polymer functional fiber, preparation method thereof and pressure spraying equipment for preparing composite polymer functional fiber
  • Composite polymer functional fiber, preparation method thereof and pressure spraying equipment for preparing composite polymer functional fiber
  • Composite polymer functional fiber, preparation method thereof and pressure spraying equipment for preparing composite polymer functional fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Embodiment 1 Composite polymer functionalized fiber web processing equipment

[0055] Such as figure 1 with figure 2 As shown, the composite polymer functionalized fiber web processing equipment provided in this embodiment includes sequentially arranged: gauze roller 1, manual adjustment device 2, pressure spraying device 4, sample chamber 5, drying mechanism 6, Ultrasonic point pressing mechanism 7 and take-up roller 8, and conveyor belt 3. The pressure spraying device is an automatic pressure spraying device known in the art.

[0056] The support layer is placed on the gauze roller 1, and the manual adjustment device 2 is used to adjust the transmission position and stability of the gauze. Conveying movement and winding after processing. First, it is sent to the position of the pressure spraying device 4, and the polymer nanocomposite solution contained in the sample chamber 5 is extruded and sprayed in a mist form by the pressure spraying device 4 through the se...

Embodiment 2

[0057] Polyvinylidene fluoride nanocomposite solution, supporting layer and protective layer used in embodiment 2

[0058] 1. Preparation of Polyvinylidene Fluoride Nanocomposite Solution

[0059] Dissolve the carboxyl-modified graphene oxide sheet (GO) and polyvinylidene fluoride with a molecular weight of 500,000-550,000 g / mol in N,N'-dimethylformamide, ultrasonically disperse for 4 hours, and centrifuge to collect the Serum.

[0060] Wherein, the surface carboxyl-modified graphene oxide sheet accounts for 2.0 wt% of the total mass of the polyvinylidene fluoride nanocomposite material.

[0061] 2. Selection of support layer

[0062] The supporting grid skeleton made of nylon is selected, the thickness of the supporting grid skeleton is 0.6mm, and the supporting grid cloth is 20-100 mesh nylon and glass fiber mesh cloth. In this embodiment, 20 mesh mesh cloth is selected.

[0063] Optical and scanning electron micrographs of the support layer as Figure 4 as shown in a. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite polymer functional fiber, a preparation method thereof and pressure spraying equipment for preparing the composite polymer functional fiber. The composite polymer functional fiber comprises a protective layer, a spinning layer and a supporting layer which are arranged in sequence; the spinning layer comprises a composite polymer fiber, and the composite polymer fiber comprises a polymer and a nano material doped in the polymer; the protective layer is selected from shaping yarns and/or patterned plain cloth; and the supporting layer is selected from fibers with a net structure. The fiber has a support layer-spinning-protective layer sandwich structure, is stable in structure, uniform in fiber and controllable in size, and can be used for a filter screen or a sewage filter membrane of atmospheric haze particulate matters and the like.

Description

technical field [0001] The invention belongs to the field of fiber materials, and in particular relates to a composite polymer functionalized fiber, a preparation method thereof and pressure spraying equipment used for the preparation thereof. Background technique [0002] Electrospinning technology has become one of the main ways to effectively prepare nanofiber materials due to its simple manufacturing equipment, low spinning cost, various types of spinnable materials, and controllable process. Fiber membranes with different structures and sizes can be obtained by adjusting the nozzle structure of the spinning equipment and controlling the experimental conditions. At present, electrospinning technology can be used to prepare a wide variety of functional fibers with controllable size, including organic, organic / inorganic composites and inorganic nanofibers. However, there are still some limitations in the preparation of functionalized fibers by electrospinning technology. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/02B32B27/12B32B37/06B32B37/10B32B37/12D06M17/00B32B3/24B32B17/02B32B17/12B32B27/36B32B27/30B32B27/32B32B27/28B32B33/00
CPCB32B5/08B32B5/26B32B5/028B32B3/266B32B33/00D06M17/00B32B37/10B32B37/06B32B37/1284B32B2250/03B32B2250/20B32B2262/14B32B2262/0238B32B2262/0253B32B2262/0223B32B2262/0284B32B2262/0261B32B2262/101
Inventor 牛琳李秀双
Owner 北京中科艾加科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap