Tyvek water-based flexographic printing material and preparation method thereof

A flexographic printing and water-based technology, which is applied in the field of Tyvek water-based flexographic printing materials and its preparation, can solve the problems of slow drying speed, easy decolorization, poor resolubility and easy paste

Inactive Publication Date: 2021-05-14
山东德创精化科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating-free double PE water-based flexographic ink disclosed in this document has the characteristics of high gloss, waterproof, abrasion resistance, and freezing resistance. However, this ink is only suitable for double PE cup printing, and the drying speed is slow when printing Tyvek. Poor resolvability and easy paste problem
Chinese patent, application number: 200610062147.9 invention patent document, discloses a water-based flexographic printing ink and its preparation method, which includes film-forming resin emulsion 8.7-47.2%, water-based acrylic color paste 40-50%, defoaming 0.1-0.3% of solvent, 0.2-2.0% of water-based wax slurry, 2-8% of isopropanol, 10-30% of ethylene glycol, 0.5-1% of ethanolamine, and the balance is water; the water-based flexographic printing ink disclosed in this document It has the advantages of clear imprint and low production cost; this ink has good adaptability to coated paper printing, but it has poor adhesion and easy decolorization when it is used on materials with low surface tension and low penetration like Tyvek
[0005] In summary, there are obviously inconveniences and defects in the actual use of the existing technology, so it is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A Tyvek water-based flexographic printing material: it is composed of the following raw materials in weight percentage: 55% of diluting agent and 45% of water-based color paste; wherein, the diluting agent is composed of the following raw materials in weight percentage: ETERANE89216 60%, JONCRYL7256 26.5% , Pripol 1006F 3%, 3620 4%, wetting agent 1%, isopropanolamine 5%, defoamer 0.5%

[0032] Its preparation method is: (1) preparation of diluent: take polyurethane resin, acrylic resin, adhesion promoter, wear-resisting agent, wetting agent, stabilizer, defoamer and deionized water in the reaction Mix well in the kettle and set aside;

[0033] (2) Mix the water-based color paste and the diluent in step (1) evenly, and then use a sand mill to grind to a fineness of ≤5 μm.

[0034] Then the printed material was prepared on a flexographic proofing machine to test the adhesion, resolvability and abrasion resistance of the sample, and the test results are listed in Table 1. ...

Embodiment 2

[0036] A Tyvek water-based flexographic printing material: it is composed of the following raw materials by weight percentage: diluent 60% and water-based color paste 40%; wherein, the diluent is composed of the following raw materials by weight percentage: ETERANE89235 70%, JONCRYL74-A 16.5%, Priplast 1901 3%, S-232 4%, wetting agent 1%, isopropanolamine 5%, defoamer 0.5%

[0037] Its preparation method is: (1) preparation of diluent: take polyurethane resin, acrylic resin, adhesion promoter, wear-resisting agent, wetting agent, stabilizer, defoamer and deionized water in the reaction Mix well in the kettle and set aside;

[0038] (2) Mix the water-based color paste and the diluent in step (1) evenly, and then use a sand mill to grind to a fineness of ≤5 μm.

[0039] Then the printed material was prepared on a flexographic proofing machine to test the adhesion, resolvability and abrasion resistance of the sample, and the test results are listed in Table 1.

Embodiment 3

[0041] A Tyvek water-based flexographic printing material: it is composed of the following raw materials by weight percentage: diluent 65% and water-based color paste 35%; wherein, the diluent is composed of the following raw materials by weight percentage: ETERANE89216 80%, JONCRYL7256 5% , Pripol 1006F 5%, 3620 4%, wetting agent 1%, triisopropanolamine 4.5%, defoamer 0.5%

[0042] Its preparation method is: (1) preparation of diluent: take polyurethane resin, acrylic resin, adhesion promoter, wear-resisting agent, wetting agent, stabilizer, defoamer and deionized water in the reaction Mix well in the kettle and set aside;

[0043] (2) Mix the water-based color paste and the diluent in step (1) evenly, and then use a sand mill to grind to a fineness of ≤5 μm.

[0044] Then the printed material was prepared on a flexographic proofing machine to test the adhesion, resolvability and abrasion resistance of the sample, and the test results are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention is suitable for the technical field of printing material preparation, and provides a Tyvek water-based flexographic printing material. The Tyvek water-based flexographic printing material comprises the following raw material components in percentage by weight of 55-65% of a diluent which comprises the following raw material components in percentage by weight of 60-80% of polyurethane resin, 0-35% of acrylic resin, 1-5% of an adhesion promoter, 1-4% of a wear-resistant agent, 0-1% of a wetting agent, 0-8% of a stabilizing agent, 0.1-0.5% of a defoaming agent, 30-40% of deionized water, and 35-45% of water-based color paste. Therefore, when a flexographic printing machine is used for printing a Tyvek material, the printing material has the characteristics of clear printed patterns, good adhesive force, high drying speed, low odor and capability of meeting the latest environmental protection requirement, and can completely replace the existing high-VOC solvent type printing ink.

Description

technical field [0001] The invention relates to the technical field of printing material preparation, in particular to a Tyvek water-based flexographic printing material and a preparation method thereof. Background technique [0002] Tyvek is a unique non-woven product introduced in recent years. It is a spun-bonded olefin made of countless fine polyethylene fibers. This unique spray-spinning technology can produce light-weight, reflective High rate yet very tough material. This material has the characteristics of not easily deformed, soft and smooth, light and tough, excellent opacity, moisture resistance, and water stain resistance, and is widely used in the medical packaging and food packaging industries. However, because it is made of polyethylene material, there is a problem that the surface of the material is inert and it is not suitable for easy printing. At present, the printing industry mostly uses high-VOC solvent-based ink printing to solve the problem of easy de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52D06P3/79
CPCD06P1/5285D06P1/5257D06P1/5221D06P3/79
Inventor 王学春李建华
Owner 山东德创精化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap