A preparation and solvent technology, which is applied in the field of synthetic preparations and its preparation, can solve the problems of complex operation process, low efficiency, and low utilization rate of finished products, and achieve the effects of increasing the contact area, improving maintenance, and extending the storage period

Pending Publication Date: 2021-06-04
王子聪
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, for the safe use and related application of radium stones, there are problems such as complicated operation process, low utilization rate of finished products produced by using radium stones, and low efficiency after being mixed into skin care products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation method for a synthetic preparation, comprising the steps of:

[0044] A, one-time calcination: select 1000 grams of radium stone and 1000 grams of purple sand according to the corresponding ratio and mix them, kiln at 700 degrees Celsius for 2 hours, cool down, and obtain standby material A;

[0045] B. Secondary calcination: after pulverizing the standby material A obtained above, pass it through an 800-mesh sieve, mix corresponding proportions of purple sand, kiln at 900 degrees Celsius for 2 hours, and cool to obtain the standby material B;

[0046] C, three times of calcination: after pulverizing the standby material B obtained above, pass it through an 800-mesh sieve, mix the corresponding proportion of purple sand, kiln at 900 degrees Celsius for 2 hours, and cool to obtain the standby material C;

[0047]D. Obtain the finished product: select yam skin according to the corresponding proportion, mix it with the above-mentioned reserve C and negative p...

Embodiment 2

[0052] A preparation method for a synthetic preparation, comprising the steps of:

[0053] A, one-time calcination: select 1000 grams of radium stone and 1000 grams of purple sand according to the corresponding ratio, mix them in a kiln at 750 degrees Celsius for 3 hours, cool down, and obtain standby material A;

[0054] B. Secondary calcination: after pulverizing the standby material A obtained above, pass through a 1000-mesh sieve, mix corresponding proportions of purple sand, kiln at 1000 degrees Celsius for 3 hours, and cool to obtain standby material B;

[0055] C. Calcining three times: crush the standby material B obtained above and pass through a 1000-mesh sieve, mix the corresponding proportion of purple sand, kiln at 1000 degrees Celsius for 3 hours, and cool to obtain the standby material C;

[0056] D. Obtaining the finished product: select yam skin according to the corresponding proportion, mix it with the above-mentioned reserve C and negative potential water, f...

Embodiment 3

[0058] A preparation method for a synthetic preparation, comprising the steps of:

[0059] A, one-time calcination: select 1000 grams of radium stone and 1000 grams of purple sand according to the corresponding ratio and mix them, kiln at 700 degrees Celsius for 2 hours, cool down, and obtain standby material A;

[0060] B. Secondary calcination: after pulverizing the standby material A obtained above, pass it through an 800-mesh sieve, mix corresponding proportions of purple sand, kiln at 900 degrees Celsius for 2 hours, and cool to obtain the standby material B;

[0061] C, three times of calcination: after pulverizing the standby material B obtained above, pass it through an 800-mesh sieve, mix the corresponding proportion of purple sand, kiln at 900 degrees Celsius for 2 hours, and cool to obtain the standby material C;

[0062] D. Obtaining the finished product: select the yam skin according to the corresponding proportion, mix it with the above-mentioned reserve material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of preparation synthesis and application, and discloses a synthetic preparation and a preparation method and application thereof. According to the preparation method, the radium stone and the purple sand are subjected to kiln firing according to the optimal proportion, and the Chinese yam peel is combined for fermentation to obtain a finished product. After the finished product is mixed into a skin care product, the penetrability of skin and the adsorbability of nutritional ingredients can be improved, meanwhile, far infrared rays and negative oxygen ions are released to achieve the anti-oxidation effect, and the function and effect of improving maintenance are achieved. During preparation, the radium stone is crushed, kilned and cooled for many times, other impurities contained in the radium stone are removed, the radioactivity of the radium stone is reduced through high-temperature kilning, the safety is improved, and high efficiency is achieved. When the finished product is obtained, the Chinese yam peel, a solvent and the like are selected for fermentation, the Chinese yam peel, the solvent and the like can be more fully reacted and mixed with the radium stone standby substance, the contact area of the radium stone standby substance is increased, meanwhile, Chinese yam polysaccharides and dioscin active ingredients rich in the Chinese yam peel are fully fused, and the storage life is prolonged.

Description

technical field [0001] The invention belongs to the technical field of preparation synthesis and application, and in particular relates to a synthetic preparation and its preparation method and application. Background technique [0002] Generally, in purple sand, the content of iron oxide can reach up to about 8%, and the content of trace elements such as silicon and manganese is also relatively high. Others include calcium, magnesium, sodium, potassium, etc., which are also important elements needed by the human body. The inner pot of purple sand cookware, like medical stone, is a mineralized environment that helps the body absorb important elements. The general purple sand liner is hygienic, non-toxic and easy to clean, avoiding the intake of harmful metal ions, and the stewed food has the original flavor without losing nutrition. [0003] The amount of negative ions generated by radium stone is as high as 1150-1650ions, which belongs to the currently known high natural m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/19A61K8/25A61K8/9794A61Q19/00A61Q19/08
CPCA61K8/19A61K8/25A61K8/9794A61Q19/00A61Q19/08A61K2800/85A61K2800/805A61K2800/412
Inventor 王子聪
Owner 王子聪