Anti-sagging modified asphalt waterproof coating and preparation method thereof

A technology of modified asphalt and waterproof coatings, which is applied in the direction of asphalt coatings, fireproof coatings, coatings, etc. It can solve the problems of poor sag resistance and low temperature temperature difference of asphalt waterproof coatings, and achieve excellent sag resistance, Excellent low temperature temperature and good anti-sag performance

Inactive Publication Date: 2021-06-25
四川环图材料科技有限公司
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide an anti-sagging modified asphalt waterproof coating, which is used to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-sagging modified asphalt waterproof coating, including the following raw materials in parts by weight: 100 parts of silicon acrylic emulsion, 250 parts of cationic emulsified asphalt, 70 parts of water, 300 parts of talcum powder, polydimethyl 2 parts of siloxane, 5 parts of sodium tripolyphosphate as a dispersant, 3 parts of hydroxyethyl cellulose as a thickener, and 20 parts of polyglycerol-3 diisostearate as an anti-sag additive.

[0024] Cationic emulsified asphalt is composed of the following raw materials: 55 parts of liquid asphalt 70# asphalt, 2.7 parts of hydrochloric acid, 45 parts of water, and 0.5 part of cationic surfactant cetyl ammonium bromide.

[0025] The preparation method of cationic emulsified asphalt comprises the following steps:

[0026] (1) Add the hydrochloric acid of ingredients into water, adjust the pH value of water to 5-6;

[0027] (2) Add the cationic surfactant of the ingredients into water, heat to 60-80° C., and stir at a high...

Embodiment 2

[0037] An anti-sagging modified asphalt waterproof coating, comprising the following raw materials in parts by weight: 125 parts of silicon acrylic emulsion, 300 parts of cationic emulsified asphalt, 65 parts of water, 260 parts of talcum powder, and 2.2 parts of defoaming agent polypropylene glycol , 5.5 parts of sodium lauryl sulfate as a dispersant, 3.4 parts of hydroxypropyl methylcellulose as a thickener, and 18 parts of polyglycerol-3 diisostearate as an anti-sag additive.

[0038] Cationic emulsified asphalt is composed of the following raw materials: 45 parts of liquid asphalt 70# asphalt, 0.5 parts of hydrochloric acid, 50 parts of water, and 1 part of cationic surfactant polydimethyldiallylammonium chloride.

[0039] The preparation steps of cationic emulsified asphalt are the same as in Example 1.

[0040] A preparation method of anti-sagging modified asphalt waterproof coating is the same as in Example 1.

[0041] The solid content, heat resistance, water impermea...

Embodiment 3

[0045] An anti-sagging modified asphalt waterproof coating, comprising the following raw materials in parts by weight: 75 parts of silicon acrylic emulsion, 200 parts of cationic emulsified asphalt, 75 parts of water, 350 parts of talcum powder, antifoaming agent polyoxypropylene oxide 1.8 parts of vinyl glyceryl ether, 4.5 parts of sodium polyacrylate as a dispersant, 2.6 parts of ethyl hydroxyethyl fiber as a thickener, and 22 parts of polyglycerol-3 diisostearate as an anti-sag additive.

[0046] Cationic emulsified asphalt is composed of the following raw materials: 45 parts of liquid asphalt 70# asphalt, 5 parts of hydrochloric acid, 40 parts of water, and 0.1 part of cationic surfactant dodecyl dimethyl benzyl ammonium bromide.

[0047] The preparation steps of cationic emulsified asphalt are the same as in Example 1.

[0048] A preparation method of anti-sagging modified asphalt waterproof coating is the same as in Example 1.

[0049] The solid content, heat resistance...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface dry timeaaaaaaaaaa
Low temperatureaaaaaaaaaa
Surface dry timeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-sagging modified asphalt waterproof coating. The waterproof coating is prepared from, by weight, 75 to 125 parts of a silicone acrylic emulsion, 200 to 300 parts of cationic emulsified asphalt, 65 to 75 parts of water, 260 to 350 parts of talcum powder, 1.8 to 2.2 parts of a defoaming agent, 4.5 to 5.5 parts of a dispersing agent, 2.6 to 3.4 parts of a thickening agent and 18 to 22 parts of anti-sagging auxiliary agent polyglycerol-3 diisostearate. The invention also discloses a preparation method of the anti-sagging modified asphalt waterproof coating. The modified asphalt waterproof coating prepared by the invention has the characteristics of high solid content, good stability, high drying speed, good anti-sagging performance, good high temperature resistance and good low temperature resistance.

Description

technical field [0001] The invention relates to the field of building waterproof materials, in particular to an anti-sag modified asphalt waterproof coating and a preparation method thereof. Background technique [0002] Traditional waterproof materials mainly include flexible waterproof materials such as waterproof membranes, waterproof coatings, and sealing ointments, as well as rigid waterproof materials that are based on cement substrates and add liquid medicine and other additives. Waterproof coating refers to a coating formed by coatings that can prevent rainwater or groundwater from seeping. Waterproof coatings can be divided into emulsion type, solvent type, reactive type and modified asphalt according to the state and form of the coating. [0003] In recent years, with the rapid development of my country's infrastructure construction, people's demand for waterproof coatings is increasing, and the performance requirements for waterproof coatings are also getting high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D195/00C09D5/00C09D133/04C09D7/63
CPCC09D195/00C09D5/18C09D7/63C08L2201/08C08L43/04C08K5/103
Inventor 刘中富周光强
Owner 四川环图材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap