Preparation method of defect foam graphene loaded transition metal monatomic catalyst

A technology of foamed graphene and transition metals, applied in electrolysis process, electrodes, electrolysis components, etc., can solve the problems of large fossil fuel consumption, greenhouse gas emission, etc., achieve the effect of increasing quantity, improving catalytic activity, and broadening the field of preparation

Active Publication Date: 2021-08-06
CHINA THREE GORGES UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this process involves high temperature and pressure, consumes a lot of fossil fuels, and emits a lot of greenhouse gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of defect foam graphene loaded transition metal monatomic catalyst
  • Preparation method of defect foam graphene loaded transition metal monatomic catalyst
  • Preparation method of defect foam graphene loaded transition metal monatomic catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Take 1 gram of the dried graphene oxide sample, soak it in nitric acid solution for 4 hours, and centrifuge and wash it to neutral with deionized water. It can be seen from the figure that the defective graphene oxide is relatively thin, and there are obvious defects in the morphology.

[0033] Take 100 mg of dried defective graphene oxide and dissolve it in 100 mL of thiourea aqueous solution for ultrasonic dispersion, stir for 6 h, re-disperse in aqueous solution after centrifugation, add 1 ml of 19 mmol / L ferrous sulfate solution for ultrasonic dispersion. The filtered sample was redispersed in the solution and treated with 700W microwave for 1min, the sample turned from yellow to grayish black. The microwaved sample was acid-washed in 3 mol / L HCL solution for 8 hours to remove the particles and impurities inside, and then washed to neutrality. The neutralized sample was prepared into a 40 mL solution, placed in a reaction kettle at 180°C for 6 hours, and freeze-dri...

Embodiment 2

[0039] Take 1 gram of the dried graphene oxide sample, soak it in nitric acid solution for 2 hours, and wash it by centrifugation with deionized water until it becomes neutral.

[0040] Take 100 mg of dried defective graphene oxide and dissolve it in 100 mL of urea aqueous solution for ultrasonic dispersion, stir for 6 h, re-disperse in aqueous solution after centrifugation, and add 3 ml of 15 mmol / L molybdenum chloride solution for ultrasonic dispersion. The filtered sample was redispersed in the solution and treated with 500W microwave for 3min, the sample turned from yellow to grayish black. The sample after microwave was acid-washed in 3 mol / L HCL solution for one day to remove the particles and impurities inside, and then washed to neutrality. The neutralized sample was prepared into a 40 mL solution, placed in a reaction kettle at 180°C for 12 hours, and freeze-dried for 24 hours.

[0041] The freeze-dried samples were placed in a tube furnace with argon at 800°C for tw...

Embodiment 3

[0044] The preparation method is the same as in Example 2, only the transition metal salt is molybdenum chloride, and the performance diagram is shown in the attached Figure 7 , it can be seen from the figure that the synthesis efficiency is the highest at -0.3V (VS.RHE), and its synthetic ammonia yield is 30μgh -1 mgcat -1 , with a Faraday efficiency of 15%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a defect foam graphene loaded transition metal monatomic catalyst and application of the defective foam graphene loaded transition metal monatomic catalyst in nitrogen reduction synthesis of ammonia. The preparation method comprises the following steps: loading transition metal monatomic on defective graphene oxide by using a microwave method, treating the obtained product by using a hydrochloric acid solution, washing to be neutral, and dispersing in an aqueous solution. The surface of a sample treated by microwaves is provided with oxygen-containing functional groups, and a product is obtained after hydro-thermal treatment and freeze drying. The product is reduced at high temperature and the transition metal atoms are rearranged by using a heat treatment method to ensure the formation of the transition metal monatomic so as to prepare the defect foam graphene loaded transition metal monatomic catalyst. The preparation method has the advantages that 1, active sites are increased by utilizing defects, and the number of transition metal single atoms is increased; and 2 the surface area of the catalyst is increased by using the three-dimensional network, and the catalytic activity is improved. The catalyst obtained by the method has high catalytic activity, durability and stability.

Description

technical field [0001] The invention relates to the field of electrocatalytic synthesis of ammonia at room temperature, specifically relates to anchoring transition metal atoms by preparing defective graphene oxide, and assembling the sample into a three-dimensional foam network structure through hydrothermal reaction, further reducing the defective foam graphene through high temperature annealing, improving the Thermal stability of transition metal single atoms. Background technique [0002] Ammonia is an important raw material for the production of nitric acid, fertilizers and explosives. Before the invention of artificial nitrogen fixation technology, NH 3 It is difficult to meet the demand of rapid population growth. The birth of the Haber-Bosch method has significantly increased the world's population and industrialization. However, this process involves high temperature and pressure, consumes a lot of fossil fuels, and emits a lot of greenhouse gases. Therefore, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25B1/27C25B11/075C25B11/065C25B11/054
CPCC25B1/00
Inventor 陈少娜卜梦珂代忠旭
Owner CHINA THREE GORGES UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com