Anti-radiation heat-insulation fabric and preparation method thereof

A radiation protection and fabric technology, applied in textiles and papermaking, fiber treatment, plant fibers, etc., can solve the problems of accelerating the aging speed of polymers, plant growth, developmental hazards, and prone to skin diseases, etc., to improve mechanical strength And radiation protection performance, reduce environmental pollution, good water absorption effect

Inactive Publication Date: 2021-10-19
东台市东驰服装有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Ultraviolet radiation is more harmful to the human body. The human body is exposed to ultraviolet radiation for a long time, which is prone to skin diseases and eventually induces skin cancer. Ultraviolet radiation can also accelerate the decomposition and aging of organic and inorganic materials, and can accelerate the aging speed of polymers. Discoloration of dyes, etc., and then changes in the properties of materials, ultraviolet radiation can also cause damage to the growth and development of plants, so it is particularly important to invent a radiation-proof and heat-insulating fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-radiation heat-insulation fabric and preparation method thereof
  • Anti-radiation heat-insulation fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A radiation-proof and heat-insulating fabric, the radiation-proof and heat-insulating fabric is made of a fabric and a modified polyurethane coating coated on the surface of the fabric;

[0038] The fabric is flax fiber;

[0039] The modified polyurethane coating is made from the following raw materials in parts by weight, 15 parts of isophorone diisocyanate, 30 parts of polycaprolactone diol, 3 parts of dimethylol propionic acid, 0.5 parts of catalyst, Made from 2 parts trimethylolpropane.

[0040] The modified polyurethane coating also includes a flame retardant and an ultraviolet absorber.

[0041] The ultraviolet absorber is made of resorcinol, trichlorotoluene and solvent;

[0042] The flame retardant consists of phenol, phosphorus oxychloride, catalyst and anhydrous aluminum trichloride.

[0043] Described solvent is toluene.

[0044] A preparation method of a radiation-proof and heat-insulating fabric, the specific steps are as follows,

[0045] S1, the prep...

Embodiment 2

[0055] A radiation-proof and heat-insulating fabric, the radiation-proof and heat-insulating fabric is made of a fabric and a modified polyurethane coating coated on the surface of the fabric;

[0056] The fabric is woven from flax fiber;

[0057] The modified polyurethane coating is made from the following raw materials in parts by weight, 17 parts of isophorone diisocyanate, 35 parts of polycaprolactone diol, 3.5 parts of dimethylol propionic acid, 0.7 parts of catalyst, Made from 2.5 parts of trimethylolpropane.

[0058] The modified polyurethane coating also includes a flame retardant and an ultraviolet absorber.

[0059] The ultraviolet absorber is made of resorcinol, trichlorotoluene and solvent;

[0060] The flame retardant consists of phenol, phosphorus oxychloride, catalyst and anhydrous aluminum trichloride.

[0061] Described solvent is toluene.

[0062] A preparation method of a radiation-proof and heat-insulating fabric, the specific steps are as follows,

[...

Embodiment 3

[0073] A radiation-proof and heat-insulating fabric, the radiation-proof and heat-insulating fabric is made of a fabric and a modified polyurethane coating coated on the surface of the fabric;

[0074] The fabric is woven from flax fiber;

[0075] The modified polyurethane coating is made from the following raw materials in parts by weight, 16 parts of isophorone diisocyanate, 37 parts of polycaprolactone diol, 3.4 parts of dimethylol propionic acid, 0.8 parts of catalyst, Made from 2.6 parts of trimethylolpropane.

[0076] The modified polyurethane coating also includes a flame retardant and an ultraviolet absorber.

[0077] The ultraviolet absorber is made of resorcinol, trichlorotoluene and solvent;

[0078] The flame retardant consists of phenol, phosphorus oxychloride, catalyst and anhydrous aluminum trichloride.

[0079] Described solvent is toluene.

[0080] A preparation method of a radiation-proof and heat-insulating fabric, the specific steps are as follows,

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-radiation heat-insulation fabric and a preparation method thereof. The anti-radiation heat-insulation fabric is prepared from a fabric and a modified polyurethane coating coated on the surface of the fabric; the fabric is formed by weaving linen fibers; the modified polyurethane coating is prepared from the following raw materials in parts by weight: 15-20 parts of isophorone diisocyanate, 30-40 parts of polycaprolactone diol, 3-4 parts of dimethylolpropionic acid, 0.5-1 part of a catalyst and 2-3 parts of trimethylolpropane; the modified polyurethane coating further comprises a flame retardant and an ultraviolet light absorber; the ultraviolet light absorber is prepared from resorcinol, trichlorotoluene and a solvent; the flame retardant is prepared from phenol, phosphorus oxychloride, a catalyst and anhydrous aluminum trichloride; and the solvent is toluene. On the basis of an original linen fiber fabric, the modified polyurethane coating is added on the linen fiber fabric through a padding process, and the added modified polyurethane coating can improve the mechanical strength and the anti-radiation performance of the product fabric.

Description

technical field [0001] The invention relates to the technical field of fabric preparation, in particular to a radiation-proof and heat-insulating fabric and a preparation method thereof. Background technique [0002] The wavelength range of ultraviolet radiation is 40-400nm. Generally, ultraviolet wavelengths are divided into A band: 320-400nm, B band 280-320nm, C band: 200-280nm, vacuum ultraviolet band 10-200nm, and ultraviolet rays with a wavelength less than 200nm will It is absorbed by the atmosphere and cannot be transmitted, and the ozone layer can absorb solar radiation substances with a wavelength of less than 300nm. Therefore, in the current ultraviolet protection, the main anti-ultraviolet radiation has a wavelength between 290-400nm. [0003] Ultraviolet radiation is more harmful to the human body. The human body is exposed to ultraviolet radiation for a long time, which is prone to skin diseases and eventually induces skin cancer. Ultraviolet radiation can also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/572D06M13/127D06M101/06
CPCD06M15/572D06M13/127D06M2101/06D06M2200/25
Inventor 朱敏李进东周克华康灵李楚涵朱灵铃
Owner 东台市东驰服装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com