Chlorine-permeation-resistant and mildew-proof film and preparation method and application thereof

A technology of resin and raw materials, which is applied in the field of anti-mold film and its preparation, and resistance to chlorine penetration. It can solve the problems of easy growth of mold on the surface of the membrane material, affect the normal use of swimming pools, and poor stability of the membrane material, and achieve good chlorine penetration resistance. , good adhesion and chlorine resistance, good stability

Active Publication Date: 2021-11-02
GUANGDONG GUANSHENG PLASTICS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, PVC film is widely used. However, these films are usually exposed to the sun as pool decoration materials, resulting in poor film stability.
The water in the swimming pool contains hypochlorite, which is also easy to corrode and penetrate the membrane material, which further leads to the aging, discoloration, and even pulverization of the membrane material, which makes the pool decoration materials need to be replaced frequently
In addition, various molds are easy to grow in the open-air swimming pool, which makes the surface of the membrane easy to grow mold and affects the normal use of the swimming pool.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorine-permeation-resistant and mildew-proof film and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Embodiment 1: the preparation of chlorine permeation-resistant, mildew-proof film

[0054] A chlorine penetration-resistant, mildew-resistant film, the raw material components for preparing the film, in parts by weight, include 100 parts of polyvinyl chloride resin, 0.5 part of graphene oxide, 0.5 part of carbon nanotubes, 2 parts of nano-zinc oxide Parts, 30 parts of KH550 silane coupling agent, 50 parts of diisononyl phthalate, 3 parts of barium zinc stabilizer, 0.5 parts of 2-hydroxy-4-n-octyloxybenzophenone, 5 parts of light calcium carbonate share.

[0055] The preparation method of the above-mentioned chlorine-resistant permeation, mildew-proof film comprises the following steps:

[0056] (1) Banbury mixing: heat up each raw material component (heating temperature is 155° C.) and stir and mix. The stirring and mixing of each raw material component is through low-speed stirring and high-speed stirring. The stirring speed of low-speed stirring is 60 rpm. The time ...

Embodiment 2

[0059] Embodiment 2: the preparation of chlorine permeation-resistant, mildew-proof film

[0060] A chlorine penetration-resistant, mildew-resistant film, the raw material components for preparing the film, in parts by weight, including 90 parts of polyvinyl chloride resin, 1.5 parts of graphene oxide, 1.0 parts of carbon nanotubes, 4 parts of nano-zinc oxide 45 parts of gamma-glycidyl etheroxypropyl trimethoxysilane, 60 parts of diisononyl phthalate, 3 parts of barium zinc stabilizer, 0.6 parts of phenyl o-hydroxybenzoate, 5 parts of light calcium carbonate .

[0061] The preparation method of the above-mentioned chlorine-resistant permeation, mildew-proof film comprises the following steps:

[0062] (1) Banbury mixing: heat up each raw material component (heating temperature is 160°C) and stir and mix. The stirring and mixing of each raw material component is through low-speed stirring and high-speed stirring. The stirring speed of low-speed stirring is 70 rpm. The time is...

Embodiment 3

[0065] Embodiment 3: the preparation of chlorine penetration, mildew proof film

[0066] Compared with Example 1, there is an ink layer on the surface of the film in Example 3, and the thickness of the ink layer is 10 μm.

[0067] The ink components forming the ink layer include 15 parts of polyurethane modified epoxy resin, 15 parts of polyester resin, 1 part of silicone defoamer, 0.3 parts of carbon nanotubes, 1.5 parts of glyceryl tristearate, butyl acetate 64 parts, 0.5 parts of nano zinc oxide.

[0068] The preparation method of the ink is as follows: first mix the polyurethane modified epoxy resin, the polyester resin and butyl acetate respectively to obtain the polyurethane modified epoxy resin mixture and the polyester resin mixture, and then mix the polyurethane modified epoxy resin mixture and Add the remaining components to the polyester resin mixture, stir and mix, the stirring speed is 400 rpm, and the stirring time is 1 hour, and the ink is prepared.

[0069] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of materials, and discloses a chlorine-permeation-resistant and mildew-proof film and a preparation method and application thereof. The film is prepared from the following raw material components: resin, graphene oxide, carbon nanotubes, nano zinc oxide and a coupling agent. Due to the coupling agent, the graphene oxide, the carbon nanotubes and the nano-zinc oxide can be uniformly dispersed in the resin, so that the effects of the graphene oxide, the carbon nanotubes and the nano-zinc oxide are exerted, and the chlorine permeation resistance of the prepared membrane can be remarkably improved due to the coexistence of the graphene oxide, the carbon nanotubes and the nano-zinc oxide; nano-zinc oxide not only has anti-ultraviolet, anti-infrared, sterilizing and mildew-proof effects, but also interacts with the one-dimensional carbon nanotubes and the two-dimensional graphene oxide, so that the chlorine penetration resistance of the film is improved, and the mechanical property of the film can be improved. The film has good chlorine penetration resistance, is good in stability in illumination and water containing pypocholoride, and is not liable to discolor and age.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a chlorine permeation-resistant and mildew-proof film and its preparation method and application. Background technique [0002] Traditional pools are decorated with ceramic tiles, which have certain safety hazards. For example, the tiles are too hard and easy to be bruised; there may be a small amount of radioactive substances in the tiles, which also have certain potential harm to the human body. Therefore, in the prior art, some film materials have been adopted as the decorative materials of the pool, such as PVC (polyvinyl chloride) film, PE (polyethylene) film, and EVA (ethylene-vinyl acetate) film. Among them, PVC film is widely used. However, these films are usually exposed to the sun as pool decoration materials, resulting in poor stability of the film material. The water in the swimming pool contains hypochlorite, which is also easy to corrode and penetrate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K3/04C08K3/22C08J5/18C09D11/104C09D11/102C09D11/03
CPCC08J5/18C09D11/104C09D11/102C09D11/03C08J2327/06C08K3/042C08K3/041C08K2003/2296C08K2201/011
Inventor 刘锦柱吴乃迪刘斌谢水郑黄斌朱文强
Owner GUANGDONG GUANSHENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com